Cerâmica varistora à base de SnO2 dopada com Pr6O11

Detalhes bibliográficos
Autor(a) principal: Irion, Herve Stangler
Data de Publicação: 2006
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da UEPG
Texto Completo: http://tede2.uepg.br/jspui/handle/prefix/1391
Resumo: In this work it was investigated the influence the in influence of the doping Pr6O11 in the electrical conductivity and in the microstructural properties in the basic ternary system (98,95 – x)%Sn02 1,0% Co0 0,05%Ta205. The used concentration of the doping Pr6011 had varied in 0,05%, 0.5% in mol, remaining constant the concentrations for the Co0 and Ta205. The processing applied was the conventional method of mixture of oxides in ambient atmosphere. The samples had been conformed in 50 MPa and sintered in 1350°C for 2 hours. After the sintering the densification of ceramics was verified with a value of 93,63% for the system with 0,1% in mol of Pr6011. The study of the electrical properties for the varistor system Sn02.Co0.Ta205 Pr6011 was carried out in continuous current in the ambient temperature and in function of the temperature. It was observed that the variation in the concentration of Pr6011 modifies the electrical behavior of the ceramics. The electrical parameters found are of [alfa]= 8,0, Er= 319 volts/cm and Vb= 0,66 volts/barrier for basic ternary system and [alfa]= 17,0 Er= 853 volts/cm and Vb= 1,15 volts/barrier with the addition of 0,10% in mol of Pr6011. The system with 0,05% mol 0.1% in mol Pr6011 presents the same value of the non linearity coefficient of the system with 0,1% in mol, however, with lower values of rupture tension and barrier tension (Er= 708 volts/cm and Vb= 0,98 volts/barrier). To concentration above of 0,1% in mol of Pr6011, the increase of the concentration of this doping, starts to be deleterious to the varistor characteristics. This effects is due to the increase in the concentration of the stannate of praseodymium phase (Pr2Sn207). This crystalline phase with the cassiterita phase (Sn02)was characterized by DRX and EDS and quantified by the refinement of Rietveld.
id UEPG_aaa76d84981105a98cf09a9ad24f0927
oai_identifier_str oai:tede2.uepg.br:prefix/1391
network_acronym_str UEPG
network_name_str Biblioteca Digital de Teses e Dissertações da UEPG
repository_id_str
spelling Antunes, Augusto CelsoCPF:54883598934http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4791532E5Pianaro, Sidnei AntonioCPF:63221721900http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4782149Z6Cerri, José AlbertoCPF:07783653871http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4784774Z0Borges, Christiane Philippini FerreiraCPF:50093720459http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780700Y0CPF:40683800078Irion, Herve Stangler2017-07-21T20:42:31Z2006-12-212017-07-21T20:42:31Z2006-03-30IRION, Herve Stangler. Cerâmica varistora à base de SnO2 dopada com Pr6O11. 2006. 115 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2006.http://tede2.uepg.br/jspui/handle/prefix/1391In this work it was investigated the influence the in influence of the doping Pr6O11 in the electrical conductivity and in the microstructural properties in the basic ternary system (98,95 – x)%Sn02 1,0% Co0 0,05%Ta205. The used concentration of the doping Pr6011 had varied in 0,05%, 0.5% in mol, remaining constant the concentrations for the Co0 and Ta205. The processing applied was the conventional method of mixture of oxides in ambient atmosphere. The samples had been conformed in 50 MPa and sintered in 1350°C for 2 hours. After the sintering the densification of ceramics was verified with a value of 93,63% for the system with 0,1% in mol of Pr6011. The study of the electrical properties for the varistor system Sn02.Co0.Ta205 Pr6011 was carried out in continuous current in the ambient temperature and in function of the temperature. It was observed that the variation in the concentration of Pr6011 modifies the electrical behavior of the ceramics. The electrical parameters found are of [alfa]= 8,0, Er= 319 volts/cm and Vb= 0,66 volts/barrier for basic ternary system and [alfa]= 17,0 Er= 853 volts/cm and Vb= 1,15 volts/barrier with the addition of 0,10% in mol of Pr6011. The system with 0,05% mol 0.1% in mol Pr6011 presents the same value of the non linearity coefficient of the system with 0,1% in mol, however, with lower values of rupture tension and barrier tension (Er= 708 volts/cm and Vb= 0,98 volts/barrier). To concentration above of 0,1% in mol of Pr6011, the increase of the concentration of this doping, starts to be deleterious to the varistor characteristics. This effects is due to the increase in the concentration of the stannate of praseodymium phase (Pr2Sn207). This crystalline phase with the cassiterita phase (Sn02)was characterized by DRX and EDS and quantified by the refinement of Rietveld.Neste trabalho investigou-se a influência do dopante Pr6O11 na condutividade elétrica e nas propriedades microestruturais no sistema ternário básico (98,95-x)%SnO2.1,0%CoO.0,05%Ta2O5. As concentrações utilizadas do dopante Pr6O11 variaram em 0,05%, 0,1%, 0,3% e 0,5% em mol, mantendo-se constante as concentrações para o CoO e Ta2O5 . O processamento empregado foi o método convencional de mistura dos óxidos. As amostras foram conformadas a 50 MPa e, sinterizadas a 1350ºC por 2 horas em atmosfera ambiente. Após a sinterização verificou-se densificação das cerâmicas, com valor de 93,63% para o sistema com 0,1% em mol de Pr6O11. O estudo das propriedades elétricas para o sistema varistor SnO2.CoO.Ta2O5 Pr6O11 foi realizado em corrente contínua a temperatura ambiente e, em função da temperatura. Observou-se que a variação na concentração de Pr6O11 altera o comportamento elétrico das cerâmicas. Os parâmetros elétricos encontrados são de [alfa] = 8,0, Er= 319 volts/cm e Vb= 0,66 volts/barreira para o sistema ternário básico e, [alfa] = 17,0, Er= 853 volts/cm e Vb = 1,15 volts/barreira com a adição de 0,10% em mol de Pr6O11. O sistema com 0,05% em mol de Pr6O11 apresenta o mesmo valor do coeficiente de não linearidade do sistema com 0,1 % em mol, entretanto, com valores menores de tensão de ruptura e tensão de barreira (Er= 708 volts/cm e Vb= 0,98 volts/barreira). Para concentrações acima de 0,1% em mol de Pr6O11, o aumento da concentração desse dopante, passa a ser deletério para as características varistoras. Esse efeito é devido ao aumento na concentração da fase cristalina estanato de praseodímio (Pr2Sn2O7). Essa fase cristalina, juntamente com a fase cassiterita (SnO2), foi caracterizada por DRX e por EDS e, quantificadas pelo refinamento de Rietveld.Made available in DSpace on 2017-07-21T20:42:31Z (GMT). No. of bitstreams: 1 Herve Stangler Irion.pdf: 4493069 bytes, checksum: 2fe9398c9c2006313a4b148ad265c9dd (MD5) Previous issue date: 2006-03-30application/pdfporUNIVERSIDADE ESTADUAL DE PONTA GROSSAPrograma de Pós-Graduação em Engenharia e Ciências de MateriaisUEPGBRDesenvolvimento e Caracterização de Materiaisóxido de estanhopropriedades não linearesVaristorestanato de praseodímiotin oxidemethod of Rietveldnon linear propertiesvaristorpraseodymium stannateCNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICACerâmica varistora à base de SnO2 dopada com Pr6O11info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UEPGinstname:Universidade Estadual de Ponta Grossa (UEPG)instacron:UEPGORIGINALHerve Stangler Irion.pdfapplication/pdf4493069http://tede2.uepg.br/jspui/bitstream/prefix/1391/1/Herve%20Stangler%20Irion.pdf2fe9398c9c2006313a4b148ad265c9ddMD51prefix/13912017-07-21 17:42:31.433oai:tede2.uepg.br:prefix/1391Biblioteca Digital de Teses e Dissertaçõeshttps://tede2.uepg.br/jspui/PUBhttp://tede2.uepg.br/oai/requestbicen@uepg.br||mv_fidelis@yahoo.com.bropendoar:2017-07-21T20:42:31Biblioteca Digital de Teses e Dissertações da UEPG - Universidade Estadual de Ponta Grossa (UEPG)false
dc.title.por.fl_str_mv Cerâmica varistora à base de SnO2 dopada com Pr6O11
title Cerâmica varistora à base de SnO2 dopada com Pr6O11
spellingShingle Cerâmica varistora à base de SnO2 dopada com Pr6O11
Irion, Herve Stangler
óxido de estanho
propriedades não lineares
Varistor
estanato de praseodímio
tin oxide
method of Rietveld
non linear properties
varistor
praseodymium stannate
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
title_short Cerâmica varistora à base de SnO2 dopada com Pr6O11
title_full Cerâmica varistora à base de SnO2 dopada com Pr6O11
title_fullStr Cerâmica varistora à base de SnO2 dopada com Pr6O11
title_full_unstemmed Cerâmica varistora à base de SnO2 dopada com Pr6O11
title_sort Cerâmica varistora à base de SnO2 dopada com Pr6O11
author Irion, Herve Stangler
author_facet Irion, Herve Stangler
author_role author
dc.contributor.advisor1.fl_str_mv Antunes, Augusto Celso
dc.contributor.advisor1ID.fl_str_mv CPF:54883598934
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4791532E5
dc.contributor.advisor-co1.fl_str_mv Pianaro, Sidnei Antonio
dc.contributor.advisor-co1ID.fl_str_mv CPF:63221721900
dc.contributor.advisor-co1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4782149Z6
dc.contributor.referee1.fl_str_mv Cerri, José Alberto
dc.contributor.referee1ID.fl_str_mv CPF:07783653871
dc.contributor.referee1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4784774Z0
dc.contributor.referee2.fl_str_mv Borges, Christiane Philippini Ferreira
dc.contributor.referee2ID.fl_str_mv CPF:50093720459
dc.contributor.referee2Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780700Y0
dc.contributor.authorID.fl_str_mv CPF:40683800078
dc.contributor.author.fl_str_mv Irion, Herve Stangler
contributor_str_mv Antunes, Augusto Celso
Pianaro, Sidnei Antonio
Cerri, José Alberto
Borges, Christiane Philippini Ferreira
dc.subject.por.fl_str_mv óxido de estanho
propriedades não lineares
Varistor
estanato de praseodímio
topic óxido de estanho
propriedades não lineares
Varistor
estanato de praseodímio
tin oxide
method of Rietveld
non linear properties
varistor
praseodymium stannate
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
dc.subject.eng.fl_str_mv tin oxide
method of Rietveld
non linear properties
varistor
praseodymium stannate
dc.subject.cnpq.fl_str_mv CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
description In this work it was investigated the influence the in influence of the doping Pr6O11 in the electrical conductivity and in the microstructural properties in the basic ternary system (98,95 – x)%Sn02 1,0% Co0 0,05%Ta205. The used concentration of the doping Pr6011 had varied in 0,05%, 0.5% in mol, remaining constant the concentrations for the Co0 and Ta205. The processing applied was the conventional method of mixture of oxides in ambient atmosphere. The samples had been conformed in 50 MPa and sintered in 1350°C for 2 hours. After the sintering the densification of ceramics was verified with a value of 93,63% for the system with 0,1% in mol of Pr6011. The study of the electrical properties for the varistor system Sn02.Co0.Ta205 Pr6011 was carried out in continuous current in the ambient temperature and in function of the temperature. It was observed that the variation in the concentration of Pr6011 modifies the electrical behavior of the ceramics. The electrical parameters found are of [alfa]= 8,0, Er= 319 volts/cm and Vb= 0,66 volts/barrier for basic ternary system and [alfa]= 17,0 Er= 853 volts/cm and Vb= 1,15 volts/barrier with the addition of 0,10% in mol of Pr6011. The system with 0,05% mol 0.1% in mol Pr6011 presents the same value of the non linearity coefficient of the system with 0,1% in mol, however, with lower values of rupture tension and barrier tension (Er= 708 volts/cm and Vb= 0,98 volts/barrier). To concentration above of 0,1% in mol of Pr6011, the increase of the concentration of this doping, starts to be deleterious to the varistor characteristics. This effects is due to the increase in the concentration of the stannate of praseodymium phase (Pr2Sn207). This crystalline phase with the cassiterita phase (Sn02)was characterized by DRX and EDS and quantified by the refinement of Rietveld.
publishDate 2006
dc.date.available.fl_str_mv 2006-12-21
2017-07-21T20:42:31Z
dc.date.issued.fl_str_mv 2006-03-30
dc.date.accessioned.fl_str_mv 2017-07-21T20:42:31Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv IRION, Herve Stangler. Cerâmica varistora à base de SnO2 dopada com Pr6O11. 2006. 115 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2006.
dc.identifier.uri.fl_str_mv http://tede2.uepg.br/jspui/handle/prefix/1391
identifier_str_mv IRION, Herve Stangler. Cerâmica varistora à base de SnO2 dopada com Pr6O11. 2006. 115 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2006.
url http://tede2.uepg.br/jspui/handle/prefix/1391
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv UNIVERSIDADE ESTADUAL DE PONTA GROSSA
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Engenharia e Ciências de Materiais
dc.publisher.initials.fl_str_mv UEPG
dc.publisher.country.fl_str_mv BR
dc.publisher.department.fl_str_mv Desenvolvimento e Caracterização de Materiais
publisher.none.fl_str_mv UNIVERSIDADE ESTADUAL DE PONTA GROSSA
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da UEPG
instname:Universidade Estadual de Ponta Grossa (UEPG)
instacron:UEPG
instname_str Universidade Estadual de Ponta Grossa (UEPG)
instacron_str UEPG
institution UEPG
reponame_str Biblioteca Digital de Teses e Dissertações da UEPG
collection Biblioteca Digital de Teses e Dissertações da UEPG
bitstream.url.fl_str_mv http://tede2.uepg.br/jspui/bitstream/prefix/1391/1/Herve%20Stangler%20Irion.pdf
bitstream.checksum.fl_str_mv 2fe9398c9c2006313a4b148ad265c9dd
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da UEPG - Universidade Estadual de Ponta Grossa (UEPG)
repository.mail.fl_str_mv bicen@uepg.br||mv_fidelis@yahoo.com.br
_version_ 1791081226152443904