Influence of thermal parameters on the dendritic arm spacing and the microhardness of Al-5.5wt.%Sn alloy directionally solidified

• Autor(a) principal: Vasconcelos,Angela de Jesus
• Data de Publicação: 2014
• Outros Autores: Silva,Cibele Vieira Arão da, Moreira,Antonio Luciano Seabra, Silva,Maria Adrina Paixão de Sousa da, Rocha,Otávio Fernandes Lima da
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: REM. Revista Escola de Minas (Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0370-44672014000200007
• topic: Horizontal directional solidification; unsteady-state heat flow; primary dendrite arm spacing; microhardness; Al-Sn Alloys

Al-Sn alloys are widely used in tribological applications. In this study, thermal, microstructural and microhardness (HV) analysis were carried out with an Al-5.5wt.%Sn alloy ingot produced by horizontal directional transient solidification. The main parameters analyzed include the growth rate (V L) and cooling rate (T R).These thermal parameters play a key role in the microstructural formation. The dendritic microstructure has been characterized by primary dendritic arm spacing (λ1) which was experimentally determined and correlated with V L, and T R. The behavior presented by the Al-5.5wt.%Sn alloy during solidification was similar to that of other aluminum alloys, i.e., the dendritic network became coarser with decreasing cooling rates, indicating that the immiscibility between aluminum and tin does not have a significant effect on the relationship between primary dendritic arm spacing and the cooling rate. The dependence of the microhardness on V L, T R and λ1 was also analyzed. It was found that for increasing values of T R, the values of HV decrease. On the other hand, the values of HV increase with increasing values of λ1.