Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial
Autor(a) principal: | |
---|---|
Data de Publicação: | 2015 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/6233 |
Resumo: | The present study aims to evaluate the wear resistance of two different materials (SAE 1045 steels and SAE 52100) in different microstructure conditions without lubrification and using biodiesel (B100), biodiesel-diesel blend (B50) and commercial diesel fuel (B7). Two samples of each material were subjected to hardening heat treatment of quenching (temperature: 850 °C and cooled in water in SAE 1045 samples and temperature: 830°C cooled in oil in SAE 52100 steel samples) followed by tempering (300°C in samples of SAE 1045 steel and 100°C and 200°C in SAE 52100 steel samples to 100 ° C). It was obtained samples with four different hardness and different microstructure conditions (tempered martensite in steel SAE 1045 and tempered martensite with Chromium Carbide in steel SAE 52100). The experiments will be conducted in a pin-on-disk tribometer, with rotation of 300 RPM, 1,5kg load and 4400 m distance covered, according to the recommendations of ASTM G99-04, followed by the wear track surface hardness measurement and evolution of the samples wear surface with a Scanning Electron Microscope. At the end of the trials, there was a variation of wear resistance between different materials, different microstructures and different lubricants applied in the test. The results showed a tendency to decrease in wear tests with B100 biodiesel lubrication. |
id |
P_RS_b3dcd363fd3ac7858d93952ab0e16657 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/6233 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Santos, Carlos Alexandre dos172.870.678-54011.686.360-94http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4299522P7Castro, Victor Velho de2015-07-22T14:09:55Z2015-03-31http://tede2.pucrs.br/tede2/handle/tede/6233The present study aims to evaluate the wear resistance of two different materials (SAE 1045 steels and SAE 52100) in different microstructure conditions without lubrification and using biodiesel (B100), biodiesel-diesel blend (B50) and commercial diesel fuel (B7). Two samples of each material were subjected to hardening heat treatment of quenching (temperature: 850 °C and cooled in water in SAE 1045 samples and temperature: 830°C cooled in oil in SAE 52100 steel samples) followed by tempering (300°C in samples of SAE 1045 steel and 100°C and 200°C in SAE 52100 steel samples to 100 ° C). It was obtained samples with four different hardness and different microstructure conditions (tempered martensite in steel SAE 1045 and tempered martensite with Chromium Carbide in steel SAE 52100). The experiments will be conducted in a pin-on-disk tribometer, with rotation of 300 RPM, 1,5kg load and 4400 m distance covered, according to the recommendations of ASTM G99-04, followed by the wear track surface hardness measurement and evolution of the samples wear surface with a Scanning Electron Microscope. At the end of the trials, there was a variation of wear resistance between different materials, different microstructures and different lubricants applied in the test. The results showed a tendency to decrease in wear tests with B100 biodiesel lubrication.O presente trabalho tem por objetivo avaliar a resistência ao desgaste de dois diferentes materiais (três amostras de SAE 1045 e três amostras de aço SAE 52100) em diferentes condições microestruturais, sem lubrificação e com lubrificação (utilizando biodiesel B100, óleo diesel B50 e óleo diesel comercial B7). Duas amostras de cada material foram submetidas a tratamento térmico de têmpera (850°C resfriado em água nas amostras de SAE 1045 e 830°C resfriado em óleo nas amostras de aço SAE 52100) seguida de revenimento (100°C e 300°C nas amostras de SAE 1045 e 100°C e 200°C nas amostras de aço SAE 52100). Assim, foram obtidas amostras com quatro durezas diferentes e diferentes condições microestruturais (martensita revenida no aço SAE 1045 e martensita revenida com uma terceira fase prioritariamente de carbeto de cromo no aço SAE 52100). Os ensaios foram realizados em um tribômetro do tipo pino-sobre-disco, com rotação de 300 RPM, 1,5kg de carga e 4400m de distância percorrida, seguindo as recomendações da norma ASTM G99–04, medição da microdureza superficial da pista de desgaste e avaliação da superfície desgastada das amostras com um Microscópio Eletrônico de Varredura (MEV). Ao final dos ensaios, observou-se a variação da resistência ao desgaste entre os diferentes materiais, diferentes microestruturas e diferentes lubrificantes aplicados no ensaio. Os resultados indicaram uma tendência de diminuição de desgaste nos ensaios realizados com lubrificação de biodiesel B100.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2015-07-22T14:09:55Z No. of bitstreams: 1 472531 - Texto Completo.pdf: 4997837 bytes, checksum: 1590f79ac735e6692cd0c7dd643ff084 (MD5)Made available in DSpace on 2015-07-22T14:09:55Z (GMT). No. of bitstreams: 1 472531 - Texto Completo.pdf: 4997837 bytes, checksum: 1590f79ac735e6692cd0c7dd643ff084 (MD5) Previous issue date: 2015-03-31Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/163150/472531%20-%20Texto%20Completo.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilFaculdade de EngenhariaENGENHARIA DE MATERIAISRESISTÊNCIA DOS MATERIAISBIODIESELDIESELTRIBOLOGIAÓLEOS LUBRIFICANTESENGENHARIASAvaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercialinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-7432719344215120122600600600600-65577057276143978545189710564848268252075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAIL472531 - Texto Completo.pdf.jpg472531 - Texto Completo.pdf.jpgimage/jpeg4338http://tede2.pucrs.br/tede2/bitstream/tede/6233/4/472531+-+Texto+Completo.pdf.jpg232b01318a505116b3ebf5e7c748b426MD54TEXT472531 - Texto Completo.pdf.txt472531 - Texto Completo.pdf.txttext/plain162341http://tede2.pucrs.br/tede2/bitstream/tede/6233/3/472531+-+Texto+Completo.pdf.txtfc61d4c10c25e7ddf084710cbef71aa4MD53ORIGINAL472531 - Texto Completo.pdf472531 - Texto Completo.pdfapplication/pdf4997837http://tede2.pucrs.br/tede2/bitstream/tede/6233/2/472531+-+Texto+Completo.pdf1590f79ac735e6692cd0c7dd643ff084MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6233/1/license.txt5a9d6006225b368ef605ba16b4f6d1beMD51tede/62332015-09-29 08:29:15.137oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2015-09-29T11:29:15Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
title |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
spellingShingle |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial Castro, Victor Velho de ENGENHARIA DE MATERIAIS RESISTÊNCIA DOS MATERIAIS BIODIESEL DIESEL TRIBOLOGIA ÓLEOS LUBRIFICANTES ENGENHARIAS |
title_short |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
title_full |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
title_fullStr |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
title_full_unstemmed |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
title_sort |
Avaliação da resistência ao desgaste dos aços SAE 52100 e SAE 1045 lubrificados com biodiesel e óleo diesel comercial |
author |
Castro, Victor Velho de |
author_facet |
Castro, Victor Velho de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Santos, Carlos Alexandre dos |
dc.contributor.advisor1ID.fl_str_mv |
172.870.678-54 |
dc.contributor.authorID.fl_str_mv |
011.686.360-94 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4299522P7 |
dc.contributor.author.fl_str_mv |
Castro, Victor Velho de |
contributor_str_mv |
Santos, Carlos Alexandre dos |
dc.subject.por.fl_str_mv |
ENGENHARIA DE MATERIAIS RESISTÊNCIA DOS MATERIAIS BIODIESEL DIESEL TRIBOLOGIA ÓLEOS LUBRIFICANTES |
topic |
ENGENHARIA DE MATERIAIS RESISTÊNCIA DOS MATERIAIS BIODIESEL DIESEL TRIBOLOGIA ÓLEOS LUBRIFICANTES ENGENHARIAS |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS |
description |
The present study aims to evaluate the wear resistance of two different materials (SAE 1045 steels and SAE 52100) in different microstructure conditions without lubrification and using biodiesel (B100), biodiesel-diesel blend (B50) and commercial diesel fuel (B7). Two samples of each material were subjected to hardening heat treatment of quenching (temperature: 850 °C and cooled in water in SAE 1045 samples and temperature: 830°C cooled in oil in SAE 52100 steel samples) followed by tempering (300°C in samples of SAE 1045 steel and 100°C and 200°C in SAE 52100 steel samples to 100 ° C). It was obtained samples with four different hardness and different microstructure conditions (tempered martensite in steel SAE 1045 and tempered martensite with Chromium Carbide in steel SAE 52100). The experiments will be conducted in a pin-on-disk tribometer, with rotation of 300 RPM, 1,5kg load and 4400 m distance covered, according to the recommendations of ASTM G99-04, followed by the wear track surface hardness measurement and evolution of the samples wear surface with a Scanning Electron Microscope. At the end of the trials, there was a variation of wear resistance between different materials, different microstructures and different lubricants applied in the test. The results showed a tendency to decrease in wear tests with B100 biodiesel lubrication. |
publishDate |
2015 |
dc.date.accessioned.fl_str_mv |
2015-07-22T14:09:55Z |
dc.date.issued.fl_str_mv |
2015-03-31 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/6233 |
url |
http://tede2.pucrs.br/tede2/handle/tede/6233 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-7432719344215120122 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
-655770572761439785 |
dc.relation.cnpq.fl_str_mv |
4518971056484826825 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Engenharia |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/6233/4/472531+-+Texto+Completo.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/6233/3/472531+-+Texto+Completo.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/6233/2/472531+-+Texto+Completo.pdf http://tede2.pucrs.br/tede2/bitstream/tede/6233/1/license.txt |
bitstream.checksum.fl_str_mv |
232b01318a505116b3ebf5e7c748b426 fc61d4c10c25e7ddf084710cbef71aa4 1590f79ac735e6692cd0c7dd643ff084 5a9d6006225b368ef605ba16b4f6d1be |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765314305523712 |