Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema

Detalhes bibliográficos
Autor(a) principal: Fonseca, Mariana Alves
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/87971
Resumo: Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia
id RCAP_0bf71c811398b0748ea48f8504689143
oai_identifier_str oai:estudogeral.uc.pt:10316/87971
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extremaSynthesis of silica aerogels with poliamide fibers for thermal insulation at extreme temperatureaerogéis de sílicaisolamento térmicoKevlar®resistência térmicasilica aerogelsthermal insulationKevlar®thermal resistanceDissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e TecnologiaOs aerogéis de sílica são materiais sintetizados através da tecnologia sol-gel que consistem em redes tridimensionais de partículas de sílica, exibindo propriedades excecionais como elevada porosidade, baixa massa volúmica, elevada área de superfície e baixa condutividade térmica. No entanto, estes materiais apresentam geralmente baixa resistência mecânica. Esta desvantagem pode ser ultrapassada incorporando outros materiais, o que permite a obtenção de compósitos com melhores características estruturais e, consequentemente, maior resistência mecânica.Uma das técnicas utilizadas para melhoramento do reforço da rede dos aerogéis é a incorporação de fibras, nomeadamente fibras de poliamida, como o Kevlar®. Estas fibras apresentam características mecânicas excecionais que irão tornar mais suportada a estrutura da rede do gel, permitindo que este sofra menor encolhimento durante a secagem. Além disso, as fibras de Kevlar® apresentam ainda elevada resistência térmica. Assim, o aerogel compósito resultante da incorporação destas fibras exibirá uma massa volúmica e condutividade térmica mais baixas do que o aerogel não reforçado, bem como uma boa resistência térmica.Este trabalho surge no âmbito do projeto AeroXTreme, que tem como principais objetivos obter aerogéis com condutividades térmicas baixas (< 0,030 W/(m.K)) e com resistência a temperaturas elevadas (500-550 ºC), de modo a que estes possam ser utilizados para isolamento térmico em condições mais extremas, nomeadamente em veículos espaciais e dispositivos de lançamento para o espaço.A síntese dos aerogéis foi realizada, utilizando como precursores de sílica o tetraetilortossilicato (TEOS) e o viniltrimetoxissilano (VTMS). Para reforço da rede utilizou-se polpa de Kevlar®, que permitiu obter aerogéis monolíticos. Implementaram-se ainda trocas de solvente com hexano ou heptano e modificação de superfície dos géis com trimetilclorossilano (TMCS) ou hexametildissilazano (HMDZ). Os aerogéis foram posteriormente caracterizados quanto à morfologia, estrutura, composição química e resistência térmica.Os valores mais baixos de condutividade térmica (0,0266±2,1x10-4 W/(m.K) e 0,0293±4,0x10-5 W/(m.K)), foram alcançados com os sistemas com razão molar solvente/precursor mais baixos (S=6 e S=10), com modificação de superfície e com sistemas de precursor com 70 % TEOS/30 % VTMS, cumprindo o objetivo do projeto AeroXTreme relativamente a esta propriedade. Para além disso, os aerogéis sintetizados, quando submetidos a uma rampa de temperatura de 10 ºC/min até 800 ºC, apenas tiveram perda de massa significativa a partir dos 500 ºC, cumprindo um outro objetivo do projeto.Silica aerogels are materials synthesized through sol-gel technology, consisting of three-dimensional network of silica particles that exhibit exceptional properties, such as high porosity, low density, high surface area and low thermal conductivity. However, these materials generally present low mechanical strength. This disadvantage can be overcome by incorporating other materials, in order to obtain composites with better structural characteristics and, consequently, higher mechanical strength.One of the techniques used to reinforce the aerogel network is the incorporation of fibers, namely polyamide fibers, such as Kevlar®. These fibers have exceptional mechanical characteristics that will give more support to the structure of the silica network, allowing it to have less shrinkage during drying. Furthermore, the Kevlar® fibers also present high thermal resistance. Therefore, the aerogel composites, resulting from the incorporation of these fibers, will exhibit lower density and thermal conductivity than the non-reinforced aerogel, as well as good thermal resistance.This work was developed under the scope of in the AeroXTreme project, which has as main objectives the development of aerogels with low thermal conductivities (< 0,030 W/(m.K)) and with resistance to high temperatures (500 – 550ºC), so that they can be used for thermal isolation in more extreme conditions, particularly in space vehicles and space launchers.The aerogels’ synthesis was performed using tetraethyl orthosilicate (TEOS) and vinyltrimethoxysilane (VTMS) as silica precursors. For the reinforcement of the network, Kevlar® pulp was used, allowing to obtain monolithic aerogels. Solvent exchange with hexane or heptane, and surface modification of the gels with trichloromethylsilane (TMCS) or hexamethyldisilazane (HMDZ) were also implemented. The aerogels were posteriorly characterized in terms of their morphology, structure, chemical composition and thermal resistance.The lowest thermal conductivity values (0,0266±2,1x10-4 W/(m.K) e 0,0293±4,0x10-5 W/(m.K)) were achieved for the systems with lower solvent/precursor ratios (S=6 and S=10), with surface modification and with precursor proportions of 70 % TEOS/30 % VTMS, fulfilling the objective of the AeroXTreme project regarding this property. Furthermore, the synthesized aerogels, when subjected to a temperature gradient of 10 ºC/min until 800 ºC, only exhibited significant mass loss above 500 ºC, fulfilling the other objective of the project.Outro - Este trabalho foi desenvolvido no âmbito do projeto AeroXTreme – “Nanocompósitos de aerogel de sílica de alto desempenho para isolamento em ambientes de temperatura extrema no Espaço”, que tem como promotor a Universidade de Coimbra e é co-financiado pelo Fundo Europeu para o Desenvolvimento Regional (FEDER), através do Programa Operacional Regional do Centro de Portugal (Centro2020), e por fundos nacionais, através da Fundação para a Ciência e Tecnologia - Refª. CENTRO-01-0145-FEDER-0295332019-09-122025-09-10T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/87971http://hdl.handle.net/10316/87971TID:202308510porFonseca, Mariana Alvesinfo:eu-repo/semantics/embargoedAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-10-27T10:54:40Zoai:estudogeral.uc.pt:10316/87971Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:08:46.747619Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
Synthesis of silica aerogels with poliamide fibers for thermal insulation at extreme temperature
title Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
spellingShingle Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
Fonseca, Mariana Alves
aerogéis de sílica
isolamento térmico
Kevlar®
resistência térmica
silica aerogels
thermal insulation
Kevlar®
thermal resistance
title_short Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
title_full Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
title_fullStr Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
title_full_unstemmed Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
title_sort Síntese de aerogéis de sílica com fibras de poliamida para isolamento térmico a temperatura extrema
author Fonseca, Mariana Alves
author_facet Fonseca, Mariana Alves
author_role author
dc.contributor.author.fl_str_mv Fonseca, Mariana Alves
dc.subject.por.fl_str_mv aerogéis de sílica
isolamento térmico
Kevlar®
resistência térmica
silica aerogels
thermal insulation
Kevlar®
thermal resistance
topic aerogéis de sílica
isolamento térmico
Kevlar®
resistência térmica
silica aerogels
thermal insulation
Kevlar®
thermal resistance
description Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia
publishDate 2019
dc.date.none.fl_str_mv 2019-09-12
2025-09-10T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/87971
http://hdl.handle.net/10316/87971
TID:202308510
url http://hdl.handle.net/10316/87971
identifier_str_mv TID:202308510
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/embargoedAccess
eu_rights_str_mv embargoedAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799133980931391488

Registros relacionados