Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica

Detalhes bibliográficos
Autor(a) principal: Lopes, Carla Filipa Neves
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/98903
Resumo: Dissertação de Mestrado em Engenharia Civil, Mecânica Estrutural, apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
id RCAP_f12654639508a856d6b700c549a1ad5d
oai_identifier_str oai:estudogeral.uc.pt:10316/98903
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação TérmicaVidro laminadoSentryGlas®TemperaturaVigasSistema de pré-esforçoEnsaios experimentaisFlexão em quatro pontosAção termomecânicaLaminated glassSentryGlas®TemperatureBeamsPre-stress systemExperimental testsFour point bendingThermomechanical actionDissertação de Mestrado em Engenharia Civil, Mecânica Estrutural, apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.Nos últimos anos tem-se verificado um aumento significativo da utilização do vidro na arquitetura. Este aumento deve-se não só às suas extraordinárias vantagens estéticas e arquitetónicas, ao seu potencial em termos de eficiência energética, como também aos diversos avanços tecnológicos, que têm permitido a utilização deste material, com um aproveitamento cada vez mais eficaz, das suas propriedades resistentes. De entre os referidos avanços tecnológicos destaca-se o tratamento térmico e a técnica de laminação. Esta última consiste em unir dois ou mais painéis de vidro por intermédio de uma película intercalar adesiva. A película de laminação mais recente e com melhor comportamento estrutural é o SentryGlas®. No entanto, dadas as propriedades viscoelásticas da referida película, o seu comportamento é significativamente afetado pela temperatura. A gama de temperaturas onde se verifica redução da sua capacidade resistente corresponde a valores facilmente atingíveis em zonas de clima temperado, numa posição não ventilada de uma fachada de um edifício corrente. Apesar da importância deste facto, até à data, ainda não existe formulação de dimensionamento ou disposições regulamentares para ter em conta este efeito explicitamente no cálculo de elementos de vidro estrutural. Por esta razão é necessário estudar não só a influência da temperatura no comportamento deste tipo de elementos, como também investigar métodos de reforço, que minimizem este efeito penalizador. Exemplo de tal é a introdução de sistemas de pré-esforço. A presente dissertação enquadra-se nesta problemática, pretendendo avaliar e caracterizar o comportamento de vigas de vidro estrutural, laminadas com SentryGlas®, quando sujeitas a ações térmicas. A caracterização é feita à custa de ensaios experimentais, à escala real, com e sem sistema de pré-esforço, em esquema de flexão em quatro pontos. As temperaturas estudadas foram 50ºC e 80ºC, para além da temperatura ambiente que serviu de referência. Deste modo foi possível avaliar não só o efeito da temperatura, como quais as vantagens da introdução de um sistema de pré-esforço neste tipo de elementos estruturais. As conclusões foram estabelecidas com base na comparação dos resultados obtidos experimentalmente, onde se comprovou a eficácia do sistema de pré-esforço e o dano devido à ação térmica, em particular na fase pós-rotura. O trabalho efetuado encontra-se no âmbito do projeto S-Glass: Desempenho Estrutural e Regras de Projeto de Vigas de Vidro Reforçadas Externamente; PTDC/ECM/116609/2010; relativamente às tarefas realizadas na Universidade de CoimbraIn recent years, there has been a significant increase in the use of glass in contemporary architecture. This is due not only to its extraordinary architectural and aesthetic advantages, its potential in terms of energy, as well as due to several technological developments that allowed the use of glass as a load bearing material. Among those technological advances stands out the heat treatment and the lamination technique. The latter consists of two or more glass panes that are bonded by means of an interlayer. One of the latest developed interlayer material that features a better mechanical behaviour is the SentryGlas®. Although since the interlayer is a viscoelastic material its characteristics are significantly affected by temperature. The referred downgrading due to temperature is noticeable at relatively low temperatures easily attainable due to light exposure, in temperate climate, and on an unventilated position of a façade on an ordinary building. In spite of that, the effect of temperature on the laminated compound is not yet fully characterized and there are no code guidelines concerning this aspect. For this reason further studies on the effect of temperature are needed as well as the investigation of reinforcement techniques for structural glass elements that may minimize the negative effects of the temperature on the interlayer. Example of such is pre stressed solution. The present study addresses those topics on an experimental approach, considering full-scale beams with SentryGlas®, with and without pre-stressed system, on an upright position, at a four point bending layout, and subjected to different temperatures. The temperatures considered were 50ºC, 80ºC and room temperature as reference. The thermal load was applied by mean of a thermal chamber especially built and optimized for this purpose. It was thus possible to evaluate not only temperature effects but also the advantages of a pre-stress system, in particular in the post-breakage regime. Conclusions are based on a comparison established between experimental results, which proved the effectiveness of the pre-stressed system and the damage due to thermal load, in particular in post-breakage regime. The research is within the framework of the research project S -Glass: Performance and Structural Beam Draft Rules of Glass Reinforced Externally; PTDC/ECM/116609/2010; concerning the tasks carried out at the University of Coimbra.2016-02info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/98903http://hdl.handle.net/10316/98903porLopes, Carla Filipa Nevesinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2022-02-28T21:59:21Zoai:estudogeral.uc.pt:10316/98903Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:16:36.786016Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
title Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
spellingShingle Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
Lopes, Carla Filipa Neves
Vidro laminado
SentryGlas®
Temperatura
Vigas
Sistema de pré-esforço
Ensaios experimentais
Flexão em quatro pontos
Ação termomecânica
Laminated glass
SentryGlas®
Temperature
Beams
Pre-stress system
Experimental tests
Four point bending
Thermomechanical action
title_short Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
title_full Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
title_fullStr Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
title_full_unstemmed Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
title_sort Caracterização do Comportamento de Vigas de Vidro Estrutural Sujeitas a Solicitação Térmica
author Lopes, Carla Filipa Neves
author_facet Lopes, Carla Filipa Neves
author_role author
dc.contributor.author.fl_str_mv Lopes, Carla Filipa Neves
dc.subject.por.fl_str_mv Vidro laminado
SentryGlas®
Temperatura
Vigas
Sistema de pré-esforço
Ensaios experimentais
Flexão em quatro pontos
Ação termomecânica
Laminated glass
SentryGlas®
Temperature
Beams
Pre-stress system
Experimental tests
Four point bending
Thermomechanical action
topic Vidro laminado
SentryGlas®
Temperatura
Vigas
Sistema de pré-esforço
Ensaios experimentais
Flexão em quatro pontos
Ação termomecânica
Laminated glass
SentryGlas®
Temperature
Beams
Pre-stress system
Experimental tests
Four point bending
Thermomechanical action
description Dissertação de Mestrado em Engenharia Civil, Mecânica Estrutural, apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
publishDate 2016
dc.date.none.fl_str_mv 2016-02
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/98903
http://hdl.handle.net/10316/98903
url http://hdl.handle.net/10316/98903
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134062290403328

Registros relacionados