Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242019000100287 |
Resumo: | Abstract: The aim of the present study was to evaluate the microtensile bond strength and the microleakage of a bulk-fill composite resin compared with a conventional incremental composite resin, in permanent molars and under cariogenic challenge using a Streptococcus mutans model. Permanent human third molars (n = 60) with an occlusal cavity of 5×3×2 mm were randomly allocated into four subgroups of restorative treatments: conventional composite resin with (n = 15) and without (n = 15) cariogenic challenge (Z350-E and Z350-C experimental and control groups, respectively), and bulk-fill composite resin with (n = 15) and without (n = 15) cariogenic challenge (Bulk Fill-E and Bulk Fill-C, respectively). Ten specimens from each subgroup were submitted to microtensile strength, and 5, to microleakage. The cariogenic challenge was conducted using the Streptococcus mutans strain (ATCC) for 7 days. The stickers obtained (1 × 1 × 2 mm) were submitted to a microtensile strength test, followed by classification of the fracture mode. Microleakage was performed using a scoring system. The data were analyzed by Kruskal-Wallis and Mann-Whitney tests (p < 0.05). Filtek Z350 XT resin presented higher microtensile bond strength than Bulk Fill resin without (19.02 ± 4.90 and 8.76 ± 3.94MPa, respectively; p < 0.001) and with cariogenic challenge (22.69 ± 7.86 and 13.31 ± 3.38MPa, respectively; p < 0.02). Z350-C and Bulk Fill-C resins presented a higher prevalence of mixed fractures (23 and 14%, respectively) in the specimens submitted to cariogenic challenge than those of the control groups, whereas microleakage was similar (p = 0.85). The conventional composite resin had higher microtensile bond strength than the bulk-fill resin, but both resin types had similar adhesion quality and microfiltration scores. |
id |
SBPQO-1_c1528a1cd0f55598044097281deb4692 |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242019000100287 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilmDental LeakageStreptococcus mutansDental CariesAbstract: The aim of the present study was to evaluate the microtensile bond strength and the microleakage of a bulk-fill composite resin compared with a conventional incremental composite resin, in permanent molars and under cariogenic challenge using a Streptococcus mutans model. Permanent human third molars (n = 60) with an occlusal cavity of 5×3×2 mm were randomly allocated into four subgroups of restorative treatments: conventional composite resin with (n = 15) and without (n = 15) cariogenic challenge (Z350-E and Z350-C experimental and control groups, respectively), and bulk-fill composite resin with (n = 15) and without (n = 15) cariogenic challenge (Bulk Fill-E and Bulk Fill-C, respectively). Ten specimens from each subgroup were submitted to microtensile strength, and 5, to microleakage. The cariogenic challenge was conducted using the Streptococcus mutans strain (ATCC) for 7 days. The stickers obtained (1 × 1 × 2 mm) were submitted to a microtensile strength test, followed by classification of the fracture mode. Microleakage was performed using a scoring system. The data were analyzed by Kruskal-Wallis and Mann-Whitney tests (p < 0.05). Filtek Z350 XT resin presented higher microtensile bond strength than Bulk Fill resin without (19.02 ± 4.90 and 8.76 ± 3.94MPa, respectively; p < 0.001) and with cariogenic challenge (22.69 ± 7.86 and 13.31 ± 3.38MPa, respectively; p < 0.02). Z350-C and Bulk Fill-C resins presented a higher prevalence of mixed fractures (23 and 14%, respectively) in the specimens submitted to cariogenic challenge than those of the control groups, whereas microleakage was similar (p = 0.85). The conventional composite resin had higher microtensile bond strength than the bulk-fill resin, but both resin types had similar adhesion quality and microfiltration scores.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2019-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242019000100287Brazilian Oral Research v.33 2019reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/1807-3107bor-2019.vol33.0111info:eu-repo/semantics/openAccessFidalgo,Tatiana Kelly da SilvaAmericano,GabrielaMedina,DeboraAthayde,GlauciaLetieri,Aline dos SantosMaia,Lucianne Copleeng2019-11-28T00:00:00Zoai:scielo:S1806-83242019000100287Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2019-11-28T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
title |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
spellingShingle |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm Fidalgo,Tatiana Kelly da Silva Dental Leakage Streptococcus mutans Dental Caries |
title_short |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
title_full |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
title_fullStr |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
title_full_unstemmed |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
title_sort |
Adhesiveness of bulk-fill composite resin in permanent molars submitted to Streptococcus mutans biofilm |
author |
Fidalgo,Tatiana Kelly da Silva |
author_facet |
Fidalgo,Tatiana Kelly da Silva Americano,Gabriela Medina,Debora Athayde,Glaucia Letieri,Aline dos Santos Maia,Lucianne Cople |
author_role |
author |
author2 |
Americano,Gabriela Medina,Debora Athayde,Glaucia Letieri,Aline dos Santos Maia,Lucianne Cople |
author2_role |
author author author author author |
dc.contributor.author.fl_str_mv |
Fidalgo,Tatiana Kelly da Silva Americano,Gabriela Medina,Debora Athayde,Glaucia Letieri,Aline dos Santos Maia,Lucianne Cople |
dc.subject.por.fl_str_mv |
Dental Leakage Streptococcus mutans Dental Caries |
topic |
Dental Leakage Streptococcus mutans Dental Caries |
description |
Abstract: The aim of the present study was to evaluate the microtensile bond strength and the microleakage of a bulk-fill composite resin compared with a conventional incremental composite resin, in permanent molars and under cariogenic challenge using a Streptococcus mutans model. Permanent human third molars (n = 60) with an occlusal cavity of 5×3×2 mm were randomly allocated into four subgroups of restorative treatments: conventional composite resin with (n = 15) and without (n = 15) cariogenic challenge (Z350-E and Z350-C experimental and control groups, respectively), and bulk-fill composite resin with (n = 15) and without (n = 15) cariogenic challenge (Bulk Fill-E and Bulk Fill-C, respectively). Ten specimens from each subgroup were submitted to microtensile strength, and 5, to microleakage. The cariogenic challenge was conducted using the Streptococcus mutans strain (ATCC) for 7 days. The stickers obtained (1 × 1 × 2 mm) were submitted to a microtensile strength test, followed by classification of the fracture mode. Microleakage was performed using a scoring system. The data were analyzed by Kruskal-Wallis and Mann-Whitney tests (p < 0.05). Filtek Z350 XT resin presented higher microtensile bond strength than Bulk Fill resin without (19.02 ± 4.90 and 8.76 ± 3.94MPa, respectively; p < 0.001) and with cariogenic challenge (22.69 ± 7.86 and 13.31 ± 3.38MPa, respectively; p < 0.02). Z350-C and Bulk Fill-C resins presented a higher prevalence of mixed fractures (23 and 14%, respectively) in the specimens submitted to cariogenic challenge than those of the control groups, whereas microleakage was similar (p = 0.85). The conventional composite resin had higher microtensile bond strength than the bulk-fill resin, but both resin types had similar adhesion quality and microfiltration scores. |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242019000100287 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242019000100287 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1807-3107bor-2019.vol33.0111 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.33 2019 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318326660202496 |