Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/8828 |
Resumo: | Solution blow spinning is a technique to produce micro- and nano-scale fibers, forming films with high porosity and surface area. Chemical modifications or the incorporation of nanostructures in these fibers can improve the performance of these films for various applications, such as membranes, tissue engineering and sensors. Therefore, the aim of this work was to study poly(lactic acid) (PLA) films obtained by solution blow spinning reinforced with cellulose nanocrystals (CNC). First, different solvents were evaluated in order to determine the best processing conditions and the feasibility of using the solvent dimethyl carbonate (DMC) in the production of PLA films by solution blow spinning. Polymer concentration showed to be the most significant parameter affecting fiber diameter and DMC presented advantages over 1,1,1,3,3,3-hexafluoro-2-propanol (HFP) and chloroform due its less toxicity, and therefore, is an alternative solvent with an affordable price, using a more environmentally-friendly process. Subsequently, the CNCs were extracted from bleached eucalyptus kraft pulp by sulfuric acid hydrolysis, which were chemically modified with maleic anhydride (CNCMA). Then, composite films of PLA/CNC and PLA/CNCMA were obtained by solution blow spinning and the results indicated that the addition of nanocrystals did not significantly affected fiber diameters, although the fiber diameters tended to decrease with the increase of the nanocrystals concentration. The results also indicated that the nanocrystals may have increased the degree of PLA polymer chains orientation and that the composite films presented a more hydrophilic behavior when compared to the pure PLA film. It suggests that some of the nanocrystals may be on the surface of the fibers, indicating that these composite films are promising for filter and adsorbents membranes application. |
id |
SCAR_cb411fb000df4721679250a99ba12f5d |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/8828 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Parize, Delne Domingos da SilvaMattoso, Luiz Henrique Capparellihttp://lattes.cnpq.br/5839043594908917Marconcini, José Manoelhttp://lattes.cnpq.br/5373845785326215http://lattes.cnpq.br/10918972878593898876a795-c071-4bb4-af4d-d7838d45edad2017-06-05T17:07:15Z2017-06-05T17:07:15Z2016-07-15PARIZE, Delne Domingos da Silva. Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8828.https://repositorio.ufscar.br/handle/ufscar/8828Solution blow spinning is a technique to produce micro- and nano-scale fibers, forming films with high porosity and surface area. Chemical modifications or the incorporation of nanostructures in these fibers can improve the performance of these films for various applications, such as membranes, tissue engineering and sensors. Therefore, the aim of this work was to study poly(lactic acid) (PLA) films obtained by solution blow spinning reinforced with cellulose nanocrystals (CNC). First, different solvents were evaluated in order to determine the best processing conditions and the feasibility of using the solvent dimethyl carbonate (DMC) in the production of PLA films by solution blow spinning. Polymer concentration showed to be the most significant parameter affecting fiber diameter and DMC presented advantages over 1,1,1,3,3,3-hexafluoro-2-propanol (HFP) and chloroform due its less toxicity, and therefore, is an alternative solvent with an affordable price, using a more environmentally-friendly process. Subsequently, the CNCs were extracted from bleached eucalyptus kraft pulp by sulfuric acid hydrolysis, which were chemically modified with maleic anhydride (CNCMA). Then, composite films of PLA/CNC and PLA/CNCMA were obtained by solution blow spinning and the results indicated that the addition of nanocrystals did not significantly affected fiber diameters, although the fiber diameters tended to decrease with the increase of the nanocrystals concentration. The results also indicated that the nanocrystals may have increased the degree of PLA polymer chains orientation and that the composite films presented a more hydrophilic behavior when compared to the pure PLA film. It suggests that some of the nanocrystals may be on the surface of the fibers, indicating that these composite films are promising for filter and adsorbents membranes application.A técnica de fiação por sopro em solução produz fibras em escala micro e nanométrica, formando filmes com elevada porosidade e área superficial. Modificações químicas ou a incorporação de nanoestruturas nestas fibras podem melhorar o desempenho destes filmes para diversas aplicações, como por exemplo, membranas, engenharia de tecidos e sensores. Portanto, o objetivo deste trabalho foi estudar filmes de poli(ácido lático) (PLA) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose (CNC). Primeiramente, avaliou-se diferentes solventes a fim de determinar as melhores condições de processamento e a viabilidade de uso do solvente dimetilcarbonato (DMC) na obtenção de filmes de PLA por fiação por sopro em solução. A concentração de polímero mostrou ser o parâmetro mais significativo que afeta o diâmetro das fibras e que o DMC possui vantagens sobre o 1,1,1,3,3,3-hexafluoro-2-propanol (HFIP) e o clorofórmio por ser menos tóxico, sendo, portanto, um solvente alternativo com preço acessível, utilizando um processo ambientalmente mais correto. Em seguida, foram extraídos os CNC a partir da polpa branqueada de eucalipto via hidrólise com ácido sulfúrico, os quais foram modificados quimicamente com anidrido maleico (CNCMA). Então, foram obtidos filmes compósitos de PLA/CNC e PLA/CNCMA por fiação por sopro em solução e os resultados indicaram que a adição dos nanocristais não alterou significativamente o diâmetro das fibras, embora observou-se uma tendência de redução nos diâmetros com o aumento da concentração dos nanocristais. Os resultados também indicaram que os nanocristais podem ter aumentado o grau de orientação das cadeias poliméricas do PLA e que os filmes compósitos apresentaram caráter mais hidrofílico quando comparados ao filme de PLA puro. Isto sugere que parte dos nanocristais possam estar na superfície das fibras, indicando que estes filmes compósitos são promissores para aplicação em membranas filtrantes e adsorventes.Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)CNPQ: 202445/2014-3porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarFiação por sopro em soluçãoPoli(ácido lático)Nanocristais de celuloseSolution blow spinningPoly(lactic acid)Cellulose nanocrystalsENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEstudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celuloseStudy of poly(lactic acid) films obtained by solution blow spinning reinforced with cellulose nanocrystalsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisOnline600600cd4a0e5b-b40b-46f6-8c76-2c2bcc3239a9info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALTeseDDSP.pdfTeseDDSP.pdfapplication/pdf5654501https://repositorio.ufscar.br/bitstream/ufscar/8828/1/TeseDDSP.pdf314e8dafc9e9b26a7437132de9501321MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/8828/2/license.txtae0398b6f8b235e40ad82cba6c50031dMD52TEXTTeseDDSP.pdf.txtTeseDDSP.pdf.txtExtracted texttext/plain194891https://repositorio.ufscar.br/bitstream/ufscar/8828/3/TeseDDSP.pdf.txtcf770d85abc52e8adee64545a1b3c806MD53THUMBNAILTeseDDSP.pdf.jpgTeseDDSP.pdf.jpgIM Thumbnailimage/jpeg6328https://repositorio.ufscar.br/bitstream/ufscar/8828/4/TeseDDSP.pdf.jpgcc4c63d87141451bfdb16a595c9bc0f6MD54ufscar/88282023-09-18 18:31:24.509oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:31:24Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
dc.title.alternative.eng.fl_str_mv |
Study of poly(lactic acid) films obtained by solution blow spinning reinforced with cellulose nanocrystals |
title |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
spellingShingle |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose Parize, Delne Domingos da Silva Fiação por sopro em solução Poli(ácido lático) Nanocristais de celulose Solution blow spinning Poly(lactic acid) Cellulose nanocrystals ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
title_full |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
title_fullStr |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
title_full_unstemmed |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
title_sort |
Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose |
author |
Parize, Delne Domingos da Silva |
author_facet |
Parize, Delne Domingos da Silva |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/1091897287859389 |
dc.contributor.author.fl_str_mv |
Parize, Delne Domingos da Silva |
dc.contributor.advisor1.fl_str_mv |
Mattoso, Luiz Henrique Capparelli |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/5839043594908917 |
dc.contributor.advisor-co1.fl_str_mv |
Marconcini, José Manoel |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/5373845785326215 |
dc.contributor.authorID.fl_str_mv |
8876a795-c071-4bb4-af4d-d7838d45edad |
contributor_str_mv |
Mattoso, Luiz Henrique Capparelli Marconcini, José Manoel |
dc.subject.por.fl_str_mv |
Fiação por sopro em solução Poli(ácido lático) Nanocristais de celulose |
topic |
Fiação por sopro em solução Poli(ácido lático) Nanocristais de celulose Solution blow spinning Poly(lactic acid) Cellulose nanocrystals ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Solution blow spinning Poly(lactic acid) Cellulose nanocrystals |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
Solution blow spinning is a technique to produce micro- and nano-scale fibers, forming films with high porosity and surface area. Chemical modifications or the incorporation of nanostructures in these fibers can improve the performance of these films for various applications, such as membranes, tissue engineering and sensors. Therefore, the aim of this work was to study poly(lactic acid) (PLA) films obtained by solution blow spinning reinforced with cellulose nanocrystals (CNC). First, different solvents were evaluated in order to determine the best processing conditions and the feasibility of using the solvent dimethyl carbonate (DMC) in the production of PLA films by solution blow spinning. Polymer concentration showed to be the most significant parameter affecting fiber diameter and DMC presented advantages over 1,1,1,3,3,3-hexafluoro-2-propanol (HFP) and chloroform due its less toxicity, and therefore, is an alternative solvent with an affordable price, using a more environmentally-friendly process. Subsequently, the CNCs were extracted from bleached eucalyptus kraft pulp by sulfuric acid hydrolysis, which were chemically modified with maleic anhydride (CNCMA). Then, composite films of PLA/CNC and PLA/CNCMA were obtained by solution blow spinning and the results indicated that the addition of nanocrystals did not significantly affected fiber diameters, although the fiber diameters tended to decrease with the increase of the nanocrystals concentration. The results also indicated that the nanocrystals may have increased the degree of PLA polymer chains orientation and that the composite films presented a more hydrophilic behavior when compared to the pure PLA film. It suggests that some of the nanocrystals may be on the surface of the fibers, indicating that these composite films are promising for filter and adsorbents membranes application. |
publishDate |
2016 |
dc.date.issued.fl_str_mv |
2016-07-15 |
dc.date.accessioned.fl_str_mv |
2017-06-05T17:07:15Z |
dc.date.available.fl_str_mv |
2017-06-05T17:07:15Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
PARIZE, Delne Domingos da Silva. Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8828. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/8828 |
identifier_str_mv |
PARIZE, Delne Domingos da Silva. Estudo de filmes de poli(ácido lático) obtidos por fiação por sopro em solução reforçados com nanocristais de celulose. 2016. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/8828. |
url |
https://repositorio.ufscar.br/handle/ufscar/8828 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
cd4a0e5b-b40b-46f6-8c76-2c2bcc3239a9 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/8828/1/TeseDDSP.pdf https://repositorio.ufscar.br/bitstream/ufscar/8828/2/license.txt https://repositorio.ufscar.br/bitstream/ufscar/8828/3/TeseDDSP.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/8828/4/TeseDDSP.pdf.jpg |
bitstream.checksum.fl_str_mv |
314e8dafc9e9b26a7437132de9501321 ae0398b6f8b235e40ad82cba6c50031d cf770d85abc52e8adee64545a1b3c806 cc4c63d87141451bfdb16a595c9bc0f6 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136324338089984 |