Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2008 |
Outros Autores: | , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFOP |
Texto Completo: | http://www.repositorio.ufop.br/handle/123456789/4776 http://dx.doi.org/10.1590/S1516-14392008000200017 |
Resumo: | In this work we investigated the effect of visible radiation on the electrical properties of poly[(2-methoxy-5 hexyloxy)-p-phenylenevinylene]– MH-PPV films and light emitting diodes. Complex impedance measurements of (Au or ITO)/MH-PPV/(Au or Al) samples were carried out at room temperature and exposed to white light. Over the frequency range from 100 mHz to 2 MHz, the electrical results of Au/MH-PPV/Au was dominated by the Cole-Cole approach, where the electrode influence is negligible. However, some additional influence of the interface was observed to occur when Al was used as electrode. These effects were observed under both dark and visible-light illumination conditions. A simple model based on resistor-capacitor parallel circuits was developed to represent the complex impedance of the samples, thereby separating bulk and interface contributions. We observed that the polymer electrical resistivity decreased while the dielectric constant of the polymer and the thickness of the Al/MH-PPV layer were almost constant with increasing light intensity. The decrease of the polymer layer resistance comes from a better charge injection due to a light induced dissociation of positive charge carriers at the electrode. |
id |
UFOP_f9d4544f2660b9494e56695bca3c88dc |
---|---|
oai_identifier_str |
oai:localhost:123456789/4776 |
network_acronym_str |
UFOP |
network_name_str |
Repositório Institucional da UFOP |
repository_id_str |
3233 |
spelling |
Cury, Fábio RogérioCazati, ThiagoBianchi, Rodrigo Fernando2015-03-25T16:07:21Z2015-03-25T16:07:21Z2008CURY, F. R.; CAZATI, T.; BIANCHI, R. F. Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes.. Materials Research, v. 11, p. 213-215, 2008. Disponível em: <http://www.scielo.br/pdf/mr/v11n2/a17v11n2.pdf>. Acesso em: 23 fev. 2015.1516-1439http://www.repositorio.ufop.br/handle/123456789/4776http://dx.doi.org/10.1590/S1516-14392008000200017In this work we investigated the effect of visible radiation on the electrical properties of poly[(2-methoxy-5 hexyloxy)-p-phenylenevinylene]– MH-PPV films and light emitting diodes. Complex impedance measurements of (Au or ITO)/MH-PPV/(Au or Al) samples were carried out at room temperature and exposed to white light. Over the frequency range from 100 mHz to 2 MHz, the electrical results of Au/MH-PPV/Au was dominated by the Cole-Cole approach, where the electrode influence is negligible. However, some additional influence of the interface was observed to occur when Al was used as electrode. These effects were observed under both dark and visible-light illumination conditions. A simple model based on resistor-capacitor parallel circuits was developed to represent the complex impedance of the samples, thereby separating bulk and interface contributions. We observed that the polymer electrical resistivity decreased while the dielectric constant of the polymer and the thickness of the Al/MH-PPV layer were almost constant with increasing light intensity. The decrease of the polymer layer resistance comes from a better charge injection due to a light induced dissociation of positive charge carriers at the electrode.PolymerDevicePhotoconductivityInterfaceInfluence of intensive light exposure on the complex impedance of polymer light-emitting diodes.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleO periódico Materials Research dá permissão ao RI/UFOP para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP. Contato via email em 25 out. 2013.info:eu-repo/semantics/openAccessengreponame:Repositório Institucional da UFOPinstname:Universidade Federal de Ouro Preto (UFOP)instacron:UFOPLICENSElicense.txtlicense.txttext/plain; charset=utf-82636http://www.repositorio.ufop.br/bitstream/123456789/4776/2/license.txtc2ffdd99e58acf69202dff00d361f23aMD52ORIGINALARTIGO_InfluenceIntensiveLight.pdfARTIGO_InfluenceIntensiveLight.pdfapplication/pdf321740http://www.repositorio.ufop.br/bitstream/123456789/4776/1/ARTIGO_InfluenceIntensiveLight.pdfcf9827c908f69c1921c4e520505056d1MD51123456789/47762019-06-28 13:30:13.534oai:localhost: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Repositório InstitucionalPUBhttp://www.repositorio.ufop.br/oai/requestrepositorio@ufop.edu.bropendoar:32332019-06-28T17:30:13Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP)false |
dc.title.pt_BR.fl_str_mv |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
title |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
spellingShingle |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. Cury, Fábio Rogério Polymer Device Photoconductivity Interface |
title_short |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
title_full |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
title_fullStr |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
title_full_unstemmed |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
title_sort |
Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes. |
author |
Cury, Fábio Rogério |
author_facet |
Cury, Fábio Rogério Cazati, Thiago Bianchi, Rodrigo Fernando |
author_role |
author |
author2 |
Cazati, Thiago Bianchi, Rodrigo Fernando |
author2_role |
author author |
dc.contributor.author.fl_str_mv |
Cury, Fábio Rogério Cazati, Thiago Bianchi, Rodrigo Fernando |
dc.subject.por.fl_str_mv |
Polymer Device Photoconductivity Interface |
topic |
Polymer Device Photoconductivity Interface |
description |
In this work we investigated the effect of visible radiation on the electrical properties of poly[(2-methoxy-5 hexyloxy)-p-phenylenevinylene]– MH-PPV films and light emitting diodes. Complex impedance measurements of (Au or ITO)/MH-PPV/(Au or Al) samples were carried out at room temperature and exposed to white light. Over the frequency range from 100 mHz to 2 MHz, the electrical results of Au/MH-PPV/Au was dominated by the Cole-Cole approach, where the electrode influence is negligible. However, some additional influence of the interface was observed to occur when Al was used as electrode. These effects were observed under both dark and visible-light illumination conditions. A simple model based on resistor-capacitor parallel circuits was developed to represent the complex impedance of the samples, thereby separating bulk and interface contributions. We observed that the polymer electrical resistivity decreased while the dielectric constant of the polymer and the thickness of the Al/MH-PPV layer were almost constant with increasing light intensity. The decrease of the polymer layer resistance comes from a better charge injection due to a light induced dissociation of positive charge carriers at the electrode. |
publishDate |
2008 |
dc.date.issued.fl_str_mv |
2008 |
dc.date.accessioned.fl_str_mv |
2015-03-25T16:07:21Z |
dc.date.available.fl_str_mv |
2015-03-25T16:07:21Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
CURY, F. R.; CAZATI, T.; BIANCHI, R. F. Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes.. Materials Research, v. 11, p. 213-215, 2008. Disponível em: <http://www.scielo.br/pdf/mr/v11n2/a17v11n2.pdf>. Acesso em: 23 fev. 2015. |
dc.identifier.uri.fl_str_mv |
http://www.repositorio.ufop.br/handle/123456789/4776 |
dc.identifier.issn.none.fl_str_mv |
1516-1439 |
dc.identifier.doi.none.fl_str_mv |
http://dx.doi.org/10.1590/S1516-14392008000200017 |
identifier_str_mv |
CURY, F. R.; CAZATI, T.; BIANCHI, R. F. Influence of intensive light exposure on the complex impedance of polymer light-emitting diodes.. Materials Research, v. 11, p. 213-215, 2008. Disponível em: <http://www.scielo.br/pdf/mr/v11n2/a17v11n2.pdf>. Acesso em: 23 fev. 2015. 1516-1439 |
url |
http://www.repositorio.ufop.br/handle/123456789/4776 http://dx.doi.org/10.1590/S1516-14392008000200017 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFOP instname:Universidade Federal de Ouro Preto (UFOP) instacron:UFOP |
instname_str |
Universidade Federal de Ouro Preto (UFOP) |
instacron_str |
UFOP |
institution |
UFOP |
reponame_str |
Repositório Institucional da UFOP |
collection |
Repositório Institucional da UFOP |
bitstream.url.fl_str_mv |
http://www.repositorio.ufop.br/bitstream/123456789/4776/2/license.txt http://www.repositorio.ufop.br/bitstream/123456789/4776/1/ARTIGO_InfluenceIntensiveLight.pdf |
bitstream.checksum.fl_str_mv |
c2ffdd99e58acf69202dff00d361f23a cf9827c908f69c1921c4e520505056d1 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP) |
repository.mail.fl_str_mv |
repositorio@ufop.edu.br |
_version_ |
1801685779981795328 |