Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe
Autor(a) principal: | |
---|---|
Data de Publicação: | 2020 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFS |
Texto Completo: | http://ri.ufs.br/jspui/handle/riufs/13137 |
Resumo: | In the process of producing clay based sintered solid wastes such as packaging glass can be incorporated. In the literature there are several works in which glass is used as a raw material in the production of sintered clay, but there are few reports of the influence of its granulometry on sintering. The present work aimed to investigate the influence of the particle size of glass embedded in a clay that is used in the ceramic industry of Sergipe. The glass was incorporated into the clay at 0, 10, 20, 30 and 40% by weight, with two different mean glass particle diameters (450 and 37,5 μm). The formulations were characterized by dilatometry and were subsequently produced sintered with clay and glass formulas burned at three different temperatures (1050, 1100 and 1150 ° C), which were characterized by their visual appearance, shrinkage, loss of fire mass. , density evolution, water absorption, mechanical strength, fracture surface, and their properties were correlated with the microstructural evolution through the SEM technique. Particle size was a key parameter to ensure the efficiency of glass incorporation in clay. |
id |
UFS-2_af0dc28b84647bb565b60a49686f2f63 |
---|---|
oai_identifier_str |
oai:ufs.br:riufs/13137 |
network_acronym_str |
UFS-2 |
network_name_str |
Repositório Institucional da UFS |
repository_id_str |
|
spelling |
Correia, João Victor Freitas BarrosMacedo, Zélia SoaresSantos, Cochiran Pereira dos2020-03-24T19:37:27Z2020-03-24T19:37:27Z2020-02CORREIA, João Victor Freitas Barros. Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe. 2020. 82 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, SE, 2020.http://ri.ufs.br/jspui/handle/riufs/13137In the process of producing clay based sintered solid wastes such as packaging glass can be incorporated. In the literature there are several works in which glass is used as a raw material in the production of sintered clay, but there are few reports of the influence of its granulometry on sintering. The present work aimed to investigate the influence of the particle size of glass embedded in a clay that is used in the ceramic industry of Sergipe. The glass was incorporated into the clay at 0, 10, 20, 30 and 40% by weight, with two different mean glass particle diameters (450 and 37,5 μm). The formulations were characterized by dilatometry and were subsequently produced sintered with clay and glass formulas burned at three different temperatures (1050, 1100 and 1150 ° C), which were characterized by their visual appearance, shrinkage, loss of fire mass. , density evolution, water absorption, mechanical strength, fracture surface, and their properties were correlated with the microstructural evolution through the SEM technique. Particle size was a key parameter to ensure the efficiency of glass incorporation in clay.No processo de produção de sinterizados à base de argila, resíduos sólidos como o vidro de embalagem podem ser incorporados. Na literatura existem vários trabalhos em que o vidro é utilizado como matéria-prima na produção de sinterizados de argila, mas existem poucos relatos da influência de sua granulometria na sinterização. O presente trabalho teve como objetivo investigar a influência do tamanho de partícula do vidro incorporado em uma argila que é utilizada na indústria cerâmica de Sergipe. O vidro foi incorporado na argila nos teores de 0, 10, 20, 30 e 40% em massa, com dois diferentes diâmetros médios de partículas de vidro (450 e 37,5 μm). As formulações foram caracterizadas por dilatometria e, posteriormente, foram produzidos sinterizados com as fórmulas de argila e vidro queimadas com três diferentes temperaturas (1050, 1100 e 1150 °C), que foram caracterizadas pelo seu aspecto visual, retração, perda de massa ao fogo, evolução da densidade, absorção de água, resistência mecânica, superfície da fratura, e tiveram suas propriedades correlacionadas com a evolução microestrutural através da técnica de MEV. O tamanho de partícula foi um parâmetro fundamental para assegurar a eficiência da incorporação do vidro na argila.Conselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPqCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESSão Cristóvão, SEporEngenharia de materiaisArgilaIndústriaSinterizaçãoResíduos industriaisResíduos de vidrosResíduos sólidosPartículas de vidroSintered claySolid wastesParticle of glassENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAInfluência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de SergipeInfluence of packaging glass granulometry on the properties of synterized products produced by a partner of clay used in the ceramic industry of Sergipe stateinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisPós-Graduação em Ciência e Engenharia de MateriaisUnivesidade Federal de Sergipereponame:Repositório Institucional da UFSinstname:Universidade Federal de Sergipe (UFS)instacron:UFSinfo:eu-repo/semantics/openAccessTEXTJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.txtJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.txtExtracted texttext/plain142024https://ri.ufs.br/jspui/bitstream/riufs/13137/3/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.txt723fe468af9dab59e04635d010cd2196MD53THUMBNAILJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.jpgJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.jpgGenerated Thumbnailimage/jpeg1356https://ri.ufs.br/jspui/bitstream/riufs/13137/4/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.jpg90564d80bd05a5a6ba59ba1c23189568MD54ORIGINALJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdfJOAO_VICTOR_FREITAS_BARROS_CORREIA.pdfapplication/pdf2581516https://ri.ufs.br/jspui/bitstream/riufs/13137/2/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf40e42eb59e6d693bb3c27dcf0292b09eMD52LICENSElicense.txtlicense.txttext/plain; charset=utf-81475https://ri.ufs.br/jspui/bitstream/riufs/13137/1/license.txt098cbbf65c2c15e1fb2e49c5d306a44cMD51riufs/131372020-03-24 16:37:27.712oai:ufs.br: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Repositório InstitucionalPUBhttps://ri.ufs.br/oai/requestrepositorio@academico.ufs.bropendoar:2020-03-24T19:37:27Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)false |
dc.title.pt_BR.fl_str_mv |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
dc.title.alternative.eng.fl_str_mv |
Influence of packaging glass granulometry on the properties of synterized products produced by a partner of clay used in the ceramic industry of Sergipe state |
title |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
spellingShingle |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe Correia, João Victor Freitas Barros Engenharia de materiais Argila Indústria Sinterização Resíduos industriais Resíduos de vidros Resíduos sólidos Partículas de vidro Sintered clay Solid wastes Particle of glass ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
title_full |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
title_fullStr |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
title_full_unstemmed |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
title_sort |
Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe |
author |
Correia, João Victor Freitas Barros |
author_facet |
Correia, João Victor Freitas Barros |
author_role |
author |
dc.contributor.author.fl_str_mv |
Correia, João Victor Freitas Barros |
dc.contributor.advisor1.fl_str_mv |
Macedo, Zélia Soares |
dc.contributor.advisor-co1.fl_str_mv |
Santos, Cochiran Pereira dos |
contributor_str_mv |
Macedo, Zélia Soares Santos, Cochiran Pereira dos |
dc.subject.por.fl_str_mv |
Engenharia de materiais Argila Indústria Sinterização Resíduos industriais Resíduos de vidros Resíduos sólidos Partículas de vidro |
topic |
Engenharia de materiais Argila Indústria Sinterização Resíduos industriais Resíduos de vidros Resíduos sólidos Partículas de vidro Sintered clay Solid wastes Particle of glass ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Sintered clay Solid wastes Particle of glass |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
In the process of producing clay based sintered solid wastes such as packaging glass can be incorporated. In the literature there are several works in which glass is used as a raw material in the production of sintered clay, but there are few reports of the influence of its granulometry on sintering. The present work aimed to investigate the influence of the particle size of glass embedded in a clay that is used in the ceramic industry of Sergipe. The glass was incorporated into the clay at 0, 10, 20, 30 and 40% by weight, with two different mean glass particle diameters (450 and 37,5 μm). The formulations were characterized by dilatometry and were subsequently produced sintered with clay and glass formulas burned at three different temperatures (1050, 1100 and 1150 ° C), which were characterized by their visual appearance, shrinkage, loss of fire mass. , density evolution, water absorption, mechanical strength, fracture surface, and their properties were correlated with the microstructural evolution through the SEM technique. Particle size was a key parameter to ensure the efficiency of glass incorporation in clay. |
publishDate |
2020 |
dc.date.accessioned.fl_str_mv |
2020-03-24T19:37:27Z |
dc.date.available.fl_str_mv |
2020-03-24T19:37:27Z |
dc.date.issued.fl_str_mv |
2020-02 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
CORREIA, João Victor Freitas Barros. Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe. 2020. 82 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, SE, 2020. |
dc.identifier.uri.fl_str_mv |
http://ri.ufs.br/jspui/handle/riufs/13137 |
identifier_str_mv |
CORREIA, João Victor Freitas Barros. Influência da granulometria do vidro soda-cal de embalagem nas propriedades de sinterizados produzidos a partir de argila usada na indústria cerâmica do estado de Sergipe. 2020. 82 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, SE, 2020. |
url |
http://ri.ufs.br/jspui/handle/riufs/13137 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.program.fl_str_mv |
Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
Univesidade Federal de Sergipe |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFS instname:Universidade Federal de Sergipe (UFS) instacron:UFS |
instname_str |
Universidade Federal de Sergipe (UFS) |
instacron_str |
UFS |
institution |
UFS |
reponame_str |
Repositório Institucional da UFS |
collection |
Repositório Institucional da UFS |
bitstream.url.fl_str_mv |
https://ri.ufs.br/jspui/bitstream/riufs/13137/3/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.txt https://ri.ufs.br/jspui/bitstream/riufs/13137/4/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf.jpg https://ri.ufs.br/jspui/bitstream/riufs/13137/2/JOAO_VICTOR_FREITAS_BARROS_CORREIA.pdf https://ri.ufs.br/jspui/bitstream/riufs/13137/1/license.txt |
bitstream.checksum.fl_str_mv |
723fe468af9dab59e04635d010cd2196 90564d80bd05a5a6ba59ba1c23189568 40e42eb59e6d693bb3c27dcf0292b09e 098cbbf65c2c15e1fb2e49c5d306a44c |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS) |
repository.mail.fl_str_mv |
repositorio@academico.ufs.br |
_version_ |
1802110823358791680 |