Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução

Detalhes bibliográficos
Autor(a) principal: Cella, Rafael Ferraz
Data de Publicação: 2017
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/186283
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2017.
id UFSC_1654c3f3719d1bfae2cfc8c987621215
oai_identifier_str oai:repositorio.ufsc.br:123456789/186283
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissoluçãoEngenharia químicaReaproveitamento (Sobras, refugos, etc.)PoliestirenoTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2017.As espumas semirrígidas de poliestireno (PS) são materiais poliméricos de baixa massa específica e são conhecidas no Brasil pelo nome de uma marca comercial, Isopor®. A reciclagem das espumas semirrígidas de PS pós-consumo é desestimulada pelo grande volume ocupado pelo material, que encarece o transporte, além da presença de sujidades que dificultam o processo. A dissolução em solventes possibilita a filtração da solução polimérica para a retirada de impurezas, além de propiciar grande redução do volume das espumas semirrígidas de PS, viabilizando a logística reversa desse material. Entre os procedimentos adotados para a separação do polímero e do solvente, estão a evaporação do solvente e a precipitação do polímero. Neste trabalho foram realizados experimentos de reciclagem de PS por dissolução em dois solventes: limoneno e acetato de etila. Foram utilizadas amostras de PS extrusado (XPS) e PS cristal e avaliados três diferentes processos para separação do solvente e do polímero: precipitação, evaporação do solvente por contato direto com água aquecida em um evaporador tubular e evaporação do solvente durante o processo de extrusão do polímero. O método de dissolução-precipitação foi avaliado somente de forma qualitativa. As amostras recicladas por meio da evaporação do solvente foram caracterizadas em relação à massa molar média (Mw), à temperatura de transição vítrea (Tg), análise dinâmico-mecânica (DMA) e espectroscopia vibracional de absorção no infravermelho por transformada de Fourier (FTIR). Nas amostras recicladas por meio da dissolução seguida pela vaporização do solvente em evaporador tubular não foram observadas alterações significativas na Mw nem redução da Tg. No método de reciclagem que envolve a evaporação do solvente durante a extrusão foi notada redução na Mw e na Tg. Nas amostras de PS recicladas no evaporador tubular foi observado um aumento na Tg, que indica a remoção de aditivos plastificantes, comumente utilizados no PS cristal. A análise dos espectros FTIR indica degradação do polímero em ambos os processos, mas de forma mais acentuada nas amostras extrusadas. Na análise comparativa entre três processos de separação do polímero/solvente, foi considerado mais vantajoso o método de vaporização do solvente em evaporador tubular, devido a produção de um material reciclado de qualidade superior e a maior simplicidade do equipamento e segurança no processamento.Abstract : Semi-rigid polystyrene foams are internationally known as Styrofoam® (trademark of Dow Chemical Company), and as Isopor® (trademark of Isopor Knauf Ltd.) in Brazil, and are polymeric materials of low density that have good resistance to mechanical impact and insulation (thermal and acoustic). The recycling of post-consumer polystyrene (PS) foam is considered unattractive, mainly due to high transportation cost and high contamination of collected materials. The dissolution technique allows the filtration of the polymer solution to remove impurities, besides providing a great reduction of the volume of the PS foams, reducing transport costs. Among the procedures adopted for separation of the polymer and solvent are solvent evaporation and polymer precipitation. In this study was evaluated the technical feasibility of polystyrene foams recycling by dissolution in two solvents, limonene and ethyl acetate. Samples of extruded polystyrene (XPS) and crystal polystyrene (PS) were used, and three different processes for solvent/polymer separation were evaluated: precipitation, solvent evaporation by direct contact with hot water (85°C) in a tubular evaporator, and solvent evaporation during the polymer extrusion process. The samples were characterized by molecular weight (Mw), the glass transition temperature (Tg) and spectroscopy Fourier transform infrared (FTIR). In the samples recycled through dissolution followed by solvent vaporization in the tubular evaporator, no significant changes were observed in Mw, neither reduction in Tg. The samples produced by the solvent evaporation during the extrusion showed a reduction in Mw and Tg. The analysis of the infrared absorption spectra indicates degradation of the polymer in both processes, but more markedly in the extruded samples. The PS samples produced in the tubular evaporator showed an increase in Tg, that indicates the removal of plasticizing additives, commonly used in crystal PS. In the comparative analysis between three polymer/solvent separation processes, the method of the solvent vaporization in the tubular evaporator was considered more advantageous due to the production of a recycled material with a superior quality and the simplicity of equipment and safety in processing.Bolzan, AriovaldoOliveira, Patrícia Francisco deUniversidade Federal de Santa CatarinaCella, Rafael Ferraz2018-05-17T04:04:07Z2018-05-17T04:04:07Z2017info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis139 p.| il., gráfs., tabs.application/pdf350584https://repositorio.ufsc.br/handle/123456789/186283porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2018-05-17T04:04:07Zoai:repositorio.ufsc.br:123456789/186283Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732018-05-17T04:04:07Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
title Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
spellingShingle Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
Cella, Rafael Ferraz
Engenharia química
Reaproveitamento (Sobras, refugos, etc.)
Poliestireno
title_short Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
title_full Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
title_fullStr Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
title_full_unstemmed Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
title_sort Avaliação da viabilidade técnica de processos de reciclagem de espuma semirrígida de poliestireno por meio da dissolução
author Cella, Rafael Ferraz
author_facet Cella, Rafael Ferraz
author_role author
dc.contributor.none.fl_str_mv Bolzan, Ariovaldo
Oliveira, Patrícia Francisco de
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Cella, Rafael Ferraz
dc.subject.por.fl_str_mv Engenharia química
Reaproveitamento (Sobras, refugos, etc.)
Poliestireno
topic Engenharia química
Reaproveitamento (Sobras, refugos, etc.)
Poliestireno
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2017.
publishDate 2017
dc.date.none.fl_str_mv 2017
2018-05-17T04:04:07Z
2018-05-17T04:04:07Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 350584
https://repositorio.ufsc.br/handle/123456789/186283
identifier_str_mv 350584
url https://repositorio.ufsc.br/handle/123456789/186283
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 139 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652290531262464

Registros relacionados