Efeito da nanossílica em matrizes cimentícias de ultra alta resistência

Detalhes bibliográficos
Autor(a) principal: Mendes, Thiago Melanda
Data de Publicação: 2016
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/176691
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.
id UFSC_b3f69bf6a0eb0ca05d0a8efb1d80c8c2
oai_identifier_str oai:repositorio.ufsc.br:123456789/176691
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Efeito da nanossílica em matrizes cimentícias de ultra alta resistência Engenharia civilConcreto de alta resistênciaMovimentoReologiaMicroestruturaTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.Os concretos de ultra alta resistência são materiais com elevada eficiência estrutural, os quais permitem a execução de estruturas mais leves. Pesquisas recentes têm demonstrado que o uso de nanossílica contribui para o ganho de desempenho destes materiais cimentícios. O objetivo desta Tese é avaliar o efeito da nanossílica em matrizes cimentícias de ultra alta resistência. Foram analisadas a resistência à compressão, a resistência à tração na flexão e o módulo de elasticidade dinâmico. A cinética de reação foi analisada por meio de calorimetria isotérmica de condução, e o comportamento reológico foi avaliado por meio dos ensaios de reometria rotacional e mini slump. A distribuição do tamanho dos poros das matrizes foi determinada por porosimetria de intrusão de mercúrio. Os produtos de hidratação foram identificados e quantificados por meio dos ensaios de difratometria de raios-X e termogravimetria. A microestrutura foi avaliada por meio de microscopia eletrônica de varredura. Os resultados demonstram que nanossílica reduz o tempo de indução, acelerando o processo de hidratação em função do teor de nanossílica. A fluidez das matrizes se reduz pela utilização da nanossílica, em decorrência do aumento da viscosidade e da tensão de escoamento das suspensões. Para teores de 0,2% de nanossílica em massa, foram obtidos ganhos na resistência à compressão. Todavia para teores em massa superiores a 0,8% de nanossílica, tem-se uma perda de desempenho das matrizes. Verificou-se o aumento na porosidade aberta das misturas. A utilização da nanossílica aumenta o consumo dos silicatos dicálcicos e tricálcicos do cimento, conforme atestaram os resultados de difratometria de raios-X. Pôde-se observar também um aumento na quantidade dos produtos de hidratação para as amostras formuladas com nanossílica: silicatos e aluminatos de cálcio hidratados, assim como do hidróxido de cálcio. A aglomeração das nanopartículas de sílica foi observada por meio de microscopia eletrônica de varredura. Pode-se concluir que, dependendo do teor utilizado, a nanossílica contribui para o ganho de resistência, sem comprometer o comportamento reológico e a cinética de reação das matrizes cimentícias. A nucleação e pozolanicidade são os principais efeitos da nanossílica na microestrutura das matrizes cimentíceas de ultra alta resistência.<br>Abstract : Ultra high performance concretes are estrutural composites, which exhibit a higher structural efficiency, allowing the implementation of lighter structures. Recent researchies have demonstrated that the use of nanossílica contributes to the gain on mechanical performance of these cementiteous materials. This thesis evaluated the effect of nanossílica in ultra high strength matrix, for which mechanical properties were measured, such as: compression strength, flexura strength and dynamic elastic modulus. The reaction kinetics was analyzed using adiabatic calorimetry and rheological behavior of suspensions was evaluated throught rotational rheometry and mini-slump tests. The pore size distribution was measured by mercury intrusion porosimetry. And the hydration products were identified and quantified by X-ray diffractometry and thermogravimetry. Scanning Electron Microscopy was employed in order to evaluate the microstrucuture of matrix and chemical analysis was obtained using backscattered electron probe. The results show that nano-silica changes the reaction kinetics of mixtures, reducing induction period and accelerating the hydration process according to the content of nano-silica. The rheological behavior of mixtures was also influencied by the use of nano-silica, reducing the paste spread due to the increased viscosity and yield stress of suspensions. For mixtures containing 0,2% of nano-silica, gains ranging from 12 to 16% were obtained on compression strength. However, for nano-silica content exceeding 0,8%, a reduction in mechanical performance was achivied. It was found that nano-silica increases the open porosity of the mixtures. Hydration of cimentiteous matrix also changes due the incorporation of nano-silica, increasing the consumption of di and tri-calcium silicates of Portland cement, measured through X-ray diffraction. As consequence, an increasing on aluminates and silicates calcium hydrates, and calcium hydroxide can be observed for mixtures formulated with nanoparticles of silica. It can be conclued that, depending on content used, nano-silica contributes to the resistance gain, without compromissing rheological behavior and reaction kinetics of cementitious matrix. Nuccleation and pozzolanic are the main effects of nano-silica on microstructure of ultra high strenght cementiteous matrix.Repette, Wellington LonguiniUniversidade Federal de Santa CatarinaMendes, Thiago Melanda2017-06-27T04:10:35Z2017-06-27T04:10:35Z2016info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis113 p.| il., gráfs., tabs.application/pdf346006https://repositorio.ufsc.br/xmlui/handle/123456789/176691porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2017-06-27T04:10:35Zoai:repositorio.ufsc.br:123456789/176691Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732017-06-27T04:10:35Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
title Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
spellingShingle Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
Mendes, Thiago Melanda
Engenharia civil
Concreto de alta resistência
Movimento
Reologia
Microestrutura
title_short Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
title_full Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
title_fullStr Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
title_full_unstemmed Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
title_sort Efeito da nanossílica em matrizes cimentícias de ultra alta resistência
author Mendes, Thiago Melanda
author_facet Mendes, Thiago Melanda
author_role author
dc.contributor.none.fl_str_mv Repette, Wellington Longuini
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Mendes, Thiago Melanda
dc.subject.por.fl_str_mv Engenharia civil
Concreto de alta resistência
Movimento
Reologia
Microestrutura
topic Engenharia civil
Concreto de alta resistência
Movimento
Reologia
Microestrutura
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.
publishDate 2016
dc.date.none.fl_str_mv 2016
2017-06-27T04:10:35Z
2017-06-27T04:10:35Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 346006
https://repositorio.ufsc.br/xmlui/handle/123456789/176691
identifier_str_mv 346006
url https://repositorio.ufsc.br/xmlui/handle/123456789/176691
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 113 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652021637578752

Registros relacionados