Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos
Autor(a) principal: | |
---|---|
Data de Publicação: | 2010 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFU |
Texto Completo: | https://repositorio.ufu.br/handle/123456789/16903 |
Resumo: | Objectives: Innumerous modifications have been made in the microtensile methodology since its introduction. The aim of this study was to evaluate the effect of critical parameters such as specimen geometry, microtensile device, fixation mode and bonding interface contamination on bond strength, failure mode, and stress distribution of an adhesive system to human dentin. Materials and Methods: Twenty-one extracted human third molars were ground to expose occlusal dentin, and after surface treatment with a total-etch 2-step adhesive system (Adper Single Bond II), composite resin restorations were constructed over the dentin. Dumbbell and stick-shaped specimens were fabricated from same teeth and divided into three microtensile gripping devices: Di- dumbbell-specimens placed onto Dircks device; GeS- stick-specimens gripped onto a Geraldeli s device with SuperGlue; GeZ- stick-specimens gripped onto a Geraldeli s device with Zapit. Specimens were tested and microtensile bond strengths were determined (MPa). The failure mode was examined under stereomicroscopy and fracture initiation sites were verified by scanning electron microscopy and energy dispersive spectroscopy. Three-dimensional models of each device and specimen were created and finite element simulations were performed. Results: The effect of the gripping devices on the bond strength was not significantly, but the failure mode was directly influenced by the type of device. Dircks device is less critical to human error than Geraldeli s device. The bonding interface contamination and regluing process increased the bond strength. Dircks device produced a more uniform stress distribution at the dumbbell specimen adhesive layer than did the Geraldeli s device at the stick specimen layer. Conclusions: The type of device and specimen geometry did not influence the bond strength values; however, the failure mode and the stress distribution of the specimens were affected by these parameters. |
id |
UFU_ffbae03977ebe2a45caaeb5351af9882 |
---|---|
oai_identifier_str |
oai:repositorio.ufu.br:123456789/16903 |
network_acronym_str |
UFU |
network_name_str |
Repositório Institucional da UFU |
repository_id_str |
|
spelling |
2016-06-22T18:47:23Z2011-03-032016-06-22T18:47:23Z2010-02-26RAPOSO, Luís Henrique Araújo. Evaluation of the microtensile critical testing parameters: laboratory and finite elements analysis. 2010. 159 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2010.https://repositorio.ufu.br/handle/123456789/16903Objectives: Innumerous modifications have been made in the microtensile methodology since its introduction. The aim of this study was to evaluate the effect of critical parameters such as specimen geometry, microtensile device, fixation mode and bonding interface contamination on bond strength, failure mode, and stress distribution of an adhesive system to human dentin. Materials and Methods: Twenty-one extracted human third molars were ground to expose occlusal dentin, and after surface treatment with a total-etch 2-step adhesive system (Adper Single Bond II), composite resin restorations were constructed over the dentin. Dumbbell and stick-shaped specimens were fabricated from same teeth and divided into three microtensile gripping devices: Di- dumbbell-specimens placed onto Dircks device; GeS- stick-specimens gripped onto a Geraldeli s device with SuperGlue; GeZ- stick-specimens gripped onto a Geraldeli s device with Zapit. Specimens were tested and microtensile bond strengths were determined (MPa). The failure mode was examined under stereomicroscopy and fracture initiation sites were verified by scanning electron microscopy and energy dispersive spectroscopy. Three-dimensional models of each device and specimen were created and finite element simulations were performed. Results: The effect of the gripping devices on the bond strength was not significantly, but the failure mode was directly influenced by the type of device. Dircks device is less critical to human error than Geraldeli s device. The bonding interface contamination and regluing process increased the bond strength. Dircks device produced a more uniform stress distribution at the dumbbell specimen adhesive layer than did the Geraldeli s device at the stick specimen layer. Conclusions: The type of device and specimen geometry did not influence the bond strength values; however, the failure mode and the stress distribution of the specimens were affected by these parameters.Objetivos: Inúmeras modificações foram feitas na metodologia de microtração desde sua introdução. Este estudo objetivou avaliar o efeito de parâmetros críticos do ensaio de microtração na resistência de união, modo de falha e distribuição de tensões de um sistema adesivo à dentina humana. Materiais e Métodos: Vinte e um terceiros molares humanos extraídos tiveram o esmalte oclusal removido e sobre a dentina superficial foi aplicado adesivo de condicionamento total simplificado (Adper Single Bond II). Restaurações de resina composta foram construídas incrementalmente. Os dentes foram seccionados e espécimes na forma de haltere e palito foram obtidos a partir do mesmo dente e então divididos entre três dispositivos: Di- espécimes na forma de haltere posicionados no dispositivo de Dircks; GeS- espécimes na forma de palito fixados no dispositivo de Geraldeli com cola SuperGlue; GeZ- palito fixados no dispositivo de Geraldeli com cola Zapit. Os espécimes foram submetidos a ensaio de microtração com velocidade de 1,0mm/minuto e a resistência de união determinada (MPa). O modo de falha foi examinado em lupa estereoscópica e o local de iniciação das falhas foi avaliado por meio de microscópio eletrônico de varredura e com espectroscopia por dispersão de energia. Modelos tridimensionais de cada dispositivo e espécimes foram criados e análises pelo método de elementos finitos foram feitas. Resultados: O efeito do tipo de dispositivo de microtração sobre a resistência de união dos espécimes não foi significante, porém o modo de falha foi influenciado significativamente. O dispositivo de Dircks mostrou-se menos crítico ao erro humano que o de Geraldeli. A contaminação da interface adesiva e o procedimento de re-colagem dos espécimes aumentaram os valores de união. Observou-se distribuição de tensões mais uniforme na camada adesiva do espécime testado no dispositivo de Dircks. Conclusões: O tipo de dispositivo de microtração e a geometria dos espécimes não influenciaram os valores de união, entretanto, o modo de falha e a distribuição de tensões foram influenciados por esses parâmetros.Fundação de Amparo a Pesquisa do Estado de Minas GeraisMestre em Odontologiaapplication/pdfporUniversidade Federal de UberlândiaPrograma de Pós-graduação em OdontologiaUFUBRCiências da SaúdeDispositivos de microtraçãoEspectroscopia por dispersão de energiaMétodo de elementos finitosMicroscopia eletrônica de varreduraMicrotraçãoModo de falhaResistência de uniãoMateriais dentáriosBond strengthEnergy dispersive spectroscopyFailure modeFinite Elements analysisMicrotensileMicrotensile devicesScanning electron microscopyCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIAAvaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos FinitosEvaluation of the microtensile critical testing parameters: laboratory and finite elements analysisinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisArmstrong, Steven R.Soares, Carlos Joséhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790296P8Fernandes Neto, Alfredo Júliohttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780690T1Noritomi, Pedro Yoshitohttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4767250Z7http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4267206U0Raposo, Luís Henrique Araújo81759583info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFUinstname:Universidade Federal de Uberlândia (UFU)instacron:UFUTHUMBNAILDiss Luis.pdf.jpgDiss Luis.pdf.jpgGenerated Thumbnailimage/jpeg1470https://repositorio.ufu.br/bitstream/123456789/16903/3/Diss%20Luis.pdf.jpgfdf4115f199a3c45f5ddcefd3a716220MD53ORIGINALDiss Luis.pdfapplication/pdf3395582https://repositorio.ufu.br/bitstream/123456789/16903/1/Diss%20Luis.pdf9b1cfcac7902ac843d4494c70f0d6e27MD51TEXTDiss Luis.pdf.txtDiss Luis.pdf.txtExtracted texttext/plain299653https://repositorio.ufu.br/bitstream/123456789/16903/2/Diss%20Luis.pdf.txtb76cfa0c8214f1247c5681c23742d714MD52123456789/169032021-03-19 17:23:53.172oai:repositorio.ufu.br:123456789/16903Repositório InstitucionalONGhttp://repositorio.ufu.br/oai/requestdiinf@dirbi.ufu.bropendoar:2021-03-19T20:23:53Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU)false |
dc.title.por.fl_str_mv |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
dc.title.alternative.eng.fl_str_mv |
Evaluation of the microtensile critical testing parameters: laboratory and finite elements analysis |
title |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
spellingShingle |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos Raposo, Luís Henrique Araújo Dispositivos de microtração Espectroscopia por dispersão de energia Método de elementos finitos Microscopia eletrônica de varredura Microtração Modo de falha Resistência de união Materiais dentários Bond strength Energy dispersive spectroscopy Failure mode Finite Elements analysis Microtensile Microtensile devices Scanning electron microscopy CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
title_full |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
title_fullStr |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
title_full_unstemmed |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
title_sort |
Avaliação dos parâmetros críticos do ensaio de microtração: análise laboratorial e por Elementos Finitos |
author |
Raposo, Luís Henrique Araújo |
author_facet |
Raposo, Luís Henrique Araújo |
author_role |
author |
dc.contributor.advisor-co1.fl_str_mv |
Armstrong, Steven R. |
dc.contributor.advisor1.fl_str_mv |
Soares, Carlos José |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790296P8 |
dc.contributor.referee1.fl_str_mv |
Fernandes Neto, Alfredo Júlio |
dc.contributor.referee1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780690T1 |
dc.contributor.referee2.fl_str_mv |
Noritomi, Pedro Yoshito |
dc.contributor.referee2Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4767250Z7 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4267206U0 |
dc.contributor.author.fl_str_mv |
Raposo, Luís Henrique Araújo |
contributor_str_mv |
Armstrong, Steven R. Soares, Carlos José Fernandes Neto, Alfredo Júlio Noritomi, Pedro Yoshito |
dc.subject.por.fl_str_mv |
Dispositivos de microtração Espectroscopia por dispersão de energia Método de elementos finitos Microscopia eletrônica de varredura Microtração Modo de falha Resistência de união Materiais dentários |
topic |
Dispositivos de microtração Espectroscopia por dispersão de energia Método de elementos finitos Microscopia eletrônica de varredura Microtração Modo de falha Resistência de união Materiais dentários Bond strength Energy dispersive spectroscopy Failure mode Finite Elements analysis Microtensile Microtensile devices Scanning electron microscopy CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Bond strength Energy dispersive spectroscopy Failure mode Finite Elements analysis Microtensile Microtensile devices Scanning electron microscopy |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Objectives: Innumerous modifications have been made in the microtensile methodology since its introduction. The aim of this study was to evaluate the effect of critical parameters such as specimen geometry, microtensile device, fixation mode and bonding interface contamination on bond strength, failure mode, and stress distribution of an adhesive system to human dentin. Materials and Methods: Twenty-one extracted human third molars were ground to expose occlusal dentin, and after surface treatment with a total-etch 2-step adhesive system (Adper Single Bond II), composite resin restorations were constructed over the dentin. Dumbbell and stick-shaped specimens were fabricated from same teeth and divided into three microtensile gripping devices: Di- dumbbell-specimens placed onto Dircks device; GeS- stick-specimens gripped onto a Geraldeli s device with SuperGlue; GeZ- stick-specimens gripped onto a Geraldeli s device with Zapit. Specimens were tested and microtensile bond strengths were determined (MPa). The failure mode was examined under stereomicroscopy and fracture initiation sites were verified by scanning electron microscopy and energy dispersive spectroscopy. Three-dimensional models of each device and specimen were created and finite element simulations were performed. Results: The effect of the gripping devices on the bond strength was not significantly, but the failure mode was directly influenced by the type of device. Dircks device is less critical to human error than Geraldeli s device. The bonding interface contamination and regluing process increased the bond strength. Dircks device produced a more uniform stress distribution at the dumbbell specimen adhesive layer than did the Geraldeli s device at the stick specimen layer. Conclusions: The type of device and specimen geometry did not influence the bond strength values; however, the failure mode and the stress distribution of the specimens were affected by these parameters. |
publishDate |
2010 |
dc.date.issued.fl_str_mv |
2010-02-26 |
dc.date.available.fl_str_mv |
2011-03-03 2016-06-22T18:47:23Z |
dc.date.accessioned.fl_str_mv |
2016-06-22T18:47:23Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
RAPOSO, Luís Henrique Araújo. Evaluation of the microtensile critical testing parameters: laboratory and finite elements analysis. 2010. 159 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2010. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufu.br/handle/123456789/16903 |
identifier_str_mv |
RAPOSO, Luís Henrique Araújo. Evaluation of the microtensile critical testing parameters: laboratory and finite elements analysis. 2010. 159 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2010. |
url |
https://repositorio.ufu.br/handle/123456789/16903 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.publisher.program.fl_str_mv |
Programa de Pós-graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UFU |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Ciências da Saúde |
publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFU instname:Universidade Federal de Uberlândia (UFU) instacron:UFU |
instname_str |
Universidade Federal de Uberlândia (UFU) |
instacron_str |
UFU |
institution |
UFU |
reponame_str |
Repositório Institucional da UFU |
collection |
Repositório Institucional da UFU |
bitstream.url.fl_str_mv |
https://repositorio.ufu.br/bitstream/123456789/16903/3/Diss%20Luis.pdf.jpg https://repositorio.ufu.br/bitstream/123456789/16903/1/Diss%20Luis.pdf https://repositorio.ufu.br/bitstream/123456789/16903/2/Diss%20Luis.pdf.txt |
bitstream.checksum.fl_str_mv |
fdf4115f199a3c45f5ddcefd3a716220 9b1cfcac7902ac843d4494c70f0d6e27 b76cfa0c8214f1247c5681c23742d714 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU) |
repository.mail.fl_str_mv |
diinf@dirbi.ufu.br |
_version_ |
1792331088019849216 |