Lithium disilicate glass-ceramic vs translucent zirconia polycrystals bonded to distinct substrates : fatigue failure load, number of cycles for failure, survival rates, and stress distribution
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Artigo |
Texto Completo: | https://hdl.handle.net/20.500.12733/1657247 |
id |
CAMP_c3b0812706b2609c05301e21ca4aebbe |
---|---|
oai_identifier_str |
oai:https://www.repositorio.unicamp.br/:1200758 |
network_name_str |
Repositório da Produção Científica e Intelectual da Unicamp |
title |
Lithium disilicate glass-ceramic vs translucent zirconia polycrystals bonded to distinct substrates : fatigue failure load, number of cycles for failure, survival rates, and stress distribution |
author |
Caldas, Ricardo Armini, 1989- |
topic |
Cerâmica odontológica Dental ceramics All-ceramics Monolithic restorations Fatigue failure Radial crack Artigo original |
publishDate |
2019 |
format |
article |
url |
https://hdl.handle.net/20.500.12733/1657247 |
instname_str |
Universidade Estadual de Campinas (UNICAMP) |
instacron_str |
UNICAMP |