Long-term fluoride release from resin-reinforced orthodontic cements following recharge with fluoride solution

• Autor(a) principal: Santos,Rogério Lacerda dos
• Data de Publicação: 2010
• Outros Autores: Pithon,Matheus Melo, Vaitsman,Delmo Santiago, Araújo,Mônica Tirre de Souza, Souza,Margareth Maria Gomes de, Nojima,Matilde Gonçalves da Cunha
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402010000200002
• topic: glass ionomer cement; fluoride release; Orthodontics

The aim of this study was to test the hypothesis that there is no difference in the fluoride release behavior of resin-reinforced glass ionomer cements before or after fluoride recharge. The materials were divided into 5 groups: 2 resin-reinforced glass ionomer cements used for attaching orthodontic bands, that is, group FOB (Fuji Ortho Band) and group MCB (Multi-Cure Glass Ionomer Orthodontic Band Cement); 2 resin-reinforced glass ionomer cements and a composite used for bonding orthodontic brackets, that is, group OGLC (Ortho Glass LC), group FOLC (Fuji Ortho LC), and group TXT (Transbond XT), respectively. Fluoride release was measured during a 60-day period by using selective ion electrodes connected to an ionic analyser. After 4 weeks, the samples were exposed to 0.221% sodium fluoride solution. The results showed that cements achieved a maximum fluoride release 24 h after initial setting. No statistically significant differences were observed between groups FOB and OGLC regarding the amount of released fluoride following fluoride recharge from day 31 to day 36 (p>0.05). In conclusion, FOB and OGLC cements showed a higher capacity of capturing and releasing fluoride compared to the other cements studied.