Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins

Detalhes bibliográficos
Autor(a) principal: Chaves,Carolina de Andrade Lima
Data de Publicação: 2009
Outros Autores: Regis,Rômulo Rocha, Machado,Ana Lucia, Souza,Raphael Freitas de
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Brazilian Dental Journal
Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402009000200007
Resumo: This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (µTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artificial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm² were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4ºC and 60ºC). µTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (α=0.05). There was no statisticaly significant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean µTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The µTBS of Biotone artificial teeth to the denture base acrylic resins was not influenced by the polymer type, surface treatment or thermocycling.
id FUNORP-1_af8142a0169f2e81e71c5a4f84a34a37
oai_identifier_str oai:scielo:S0103-64402009000200007
network_acronym_str FUNORP-1
network_name_str Brazilian Dental Journal
repository_id_str
spelling Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resinsacrylic resinsartificial toothsurface treatmentmicrotensile bond strengthThis study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (µTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artificial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm² were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4ºC and 60ºC). µTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (α=0.05). There was no statisticaly significant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean µTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The µTBS of Biotone artificial teeth to the denture base acrylic resins was not influenced by the polymer type, surface treatment or thermocycling.Fundação Odontológica de Ribeirão Preto2009-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402009000200007Brazilian Dental Journal v.20 n.2 2009reponame:Brazilian Dental Journalinstname:Fundação Odontológica de Ribeirão Preto (FUNORP)instacron:FUNORP10.1590/S0103-64402009000200007info:eu-repo/semantics/openAccessChaves,Carolina de Andrade LimaRegis,Rômulo RochaMachado,Ana LuciaSouza,Raphael Freitas deeng2009-09-01T00:00:00Zoai:scielo:S0103-64402009000200007Revistahttps://www.scielo.br/j/bdj/https://old.scielo.br/oai/scielo-oai.phpbdj@forp.usp.br||sergio@fosjc.unesp.br1806-47600103-6440opendoar:2009-09-01T00:00Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP)false
dc.title.none.fl_str_mv Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
title Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
spellingShingle Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
Chaves,Carolina de Andrade Lima
acrylic resins
artificial tooth
surface treatment
microtensile bond strength
title_short Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
title_full Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
title_fullStr Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
title_full_unstemmed Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
title_sort Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins
author Chaves,Carolina de Andrade Lima
author_facet Chaves,Carolina de Andrade Lima
Regis,Rômulo Rocha
Machado,Ana Lucia
Souza,Raphael Freitas de
author_role author
author2 Regis,Rômulo Rocha
Machado,Ana Lucia
Souza,Raphael Freitas de
author2_role author
author
author
dc.contributor.author.fl_str_mv Chaves,Carolina de Andrade Lima
Regis,Rômulo Rocha
Machado,Ana Lucia
Souza,Raphael Freitas de
dc.subject.por.fl_str_mv acrylic resins
artificial tooth
surface treatment
microtensile bond strength
topic acrylic resins
artificial tooth
surface treatment
microtensile bond strength
description This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (µTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artificial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm² were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4ºC and 60ºC). µTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (α=0.05). There was no statisticaly significant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean µTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The µTBS of Biotone artificial teeth to the denture base acrylic resins was not influenced by the polymer type, surface treatment or thermocycling.
publishDate 2009
dc.date.none.fl_str_mv 2009-01-01
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402009000200007
url http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402009000200007
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv 10.1590/S0103-64402009000200007
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv text/html
dc.publisher.none.fl_str_mv Fundação Odontológica de Ribeirão Preto
publisher.none.fl_str_mv Fundação Odontológica de Ribeirão Preto
dc.source.none.fl_str_mv Brazilian Dental Journal v.20 n.2 2009
reponame:Brazilian Dental Journal
instname:Fundação Odontológica de Ribeirão Preto (FUNORP)
instacron:FUNORP
instname_str Fundação Odontológica de Ribeirão Preto (FUNORP)
instacron_str FUNORP
institution FUNORP
reponame_str Brazilian Dental Journal
collection Brazilian Dental Journal
repository.name.fl_str_mv Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP)
repository.mail.fl_str_mv bdj@forp.usp.br||sergio@fosjc.unesp.br
_version_ 1754204090957561856