Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Outros Autores: | , , , |
Tipo de documento: | Artigo de conferência |
Título da fonte: | Repositório Institucional do IPEN |
Texto Completo: | http://repositorio.ipen.br/handle/123456789/26435 |
Resumo: | Al alloys of the 6XXX series (Al-Mg-Si) are employed as structural materials in a variety of industrial applications due to a combination of high mechanical strength and good corrosion resistance. The final mechanical properties are achieved after specific precipitation hardening heat treatments. The aging time during precipitation hardening is known to affect these properties and can also influence the corrosion resistance of the alloy. The susceptibility of Al alloys to corrosion in alkaline media is well-known. In this work the effect of aging time on the corrosion behavior of 6061 Al alloy was evaluated in NaOH and NaCl solutions. The material was aged at 200 ??C for times ranging from 1 to 36 h. The corrosion behavior of the aged alloy was studied using potentiodynamic polarization and electrochemical impedance spectroscopy. The results showed that the corrosion resistance was progressively lower for increasing aging times up to 8 h in NaCl and up to 24 h in NaOH. Longer aging times led to a decrease of the corrosion current density. |
id |
IPEN_cf78721f62759fb12a39e611e0f11768 |
---|---|
oai_identifier_str |
oai:repositorio.ipen.br:123456789/26435 |
network_acronym_str |
IPEN |
network_name_str |
Repositório Institucional do IPEN |
repository_id_str |
4510 |
spelling |
2016-06-29T16:28:05Z2016-06-29T16:28:05Z19-23 de maio, 2014http://repositorio.ipen.br/handle/123456789/26435Al alloys of the 6XXX series (Al-Mg-Si) are employed as structural materials in a variety of industrial applications due to a combination of high mechanical strength and good corrosion resistance. The final mechanical properties are achieved after specific precipitation hardening heat treatments. The aging time during precipitation hardening is known to affect these properties and can also influence the corrosion resistance of the alloy. The susceptibility of Al alloys to corrosion in alkaline media is well-known. In this work the effect of aging time on the corrosion behavior of 6061 Al alloy was evaluated in NaOH and NaCl solutions. The material was aged at 200 ??C for times ranging from 1 to 36 h. The corrosion behavior of the aged alloy was studied using potentiodynamic polarization and electrochemical impedance spectroscopy. The results showed that the corrosion resistance was progressively lower for increasing aging times up to 8 h in NaCl and up to 24 h in NaOH. Longer aging times led to a decrease of the corrosion current density.Submitted by Claudinei Pracidelli (cpracide@ipen.br) on 2016-06-29T16:28:05Z No. of bitstreams: 1 22346.pdf: 348132 bytes, checksum: 91ce5e4080ea9f089085f56acb3d4799 (MD5)Made available in DSpace on 2016-06-29T16:28:05Z (GMT). No. of bitstreams: 1 22346.pdf: 348132 bytes, checksum: 91ce5e4080ea9f089085f56acb3d4799 (MD5)Associa????o Brasileira de Corros??o ??? ABRACOaluminium alloysprecipitation hardeningcorrosionaginghydroxidesevaluationpolarizationspectroscopyInfluence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solutioninfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObjectINTERCORRIRio de Janeiro, RJFortaleza, CECORREA, OLANDIR V.SOUZA, JOSE A.B. deOLIVEIRA, MARA C.L. deANTUNES, RENATO A.CONGRESSO BRASILEIRO DE CORROS??O, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSI??N Y PROTECCI??N, 10th.; CONCURSO DE FOTOGRAFIA DE CORROS??O E DEGRADA????O DE MATERIAIS, 19.; EXPOSI????O DE TECNOLOGIAS PARA PREVEN????O E CONTROLE DA CORROS??O, 34info:eu-repo/semantics/openAccessreponame:Repositório Institucional do IPENinstname:Instituto de Pesquisas Energéticas e Nucleares (IPEN)instacron:IPEN223462014CORREA, OLANDIR V.SOUZA, JOSE A.B. de16-06Anais488127422572685CORREA, OLANDIR V.:488:730:SSOUZA, JOSE A.B. DE:1274:410:NOLIVEIRA, MARA C.L. DE:2257:-1:NANTUNES, RENATO A.:2685:-1:NORIGINAL22346.pdf22346.pdfapplication/pdf348132http://repositorio.ipen.br/bitstream/123456789/26435/1/22346.pdf91ce5e4080ea9f089085f56acb3d4799MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81748http://repositorio.ipen.br/bitstream/123456789/26435/2/license.txt8a4605be74aa9ea9d79846c1fba20a33MD52123456789/264352022-04-08 12:55:16.923oai:repositorio.ipen.br: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Repositório InstitucionalPUBhttp://repositorio.ipen.br/oai/requestbibl@ipen.bropendoar:45102022-04-08T12:55:16Repositório Institucional do IPEN - Instituto de Pesquisas Energéticas e Nucleares (IPEN)false |
dc.title.pt_BR.fl_str_mv |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
title |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
spellingShingle |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution CORREA, OLANDIR V. aluminium alloys precipitation hardening corrosion aging hydroxides evaluation polarization spectroscopy |
title_short |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
title_full |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
title_fullStr |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
title_full_unstemmed |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
title_sort |
Influence of aging time on the corrosion behavior of 6061 Al alloy in alkaline solution |
author |
CORREA, OLANDIR V. |
author_facet |
CORREA, OLANDIR V. SOUZA, JOSE A.B. de OLIVEIRA, MARA C.L. de ANTUNES, RENATO A. CONGRESSO BRASILEIRO DE CORROS??O, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSI??N Y PROTECCI??N, 10th.; CONCURSO DE FOTOGRAFIA DE CORROS??O E DEGRADA????O DE MATERIAIS, 19.; EXPOSI????O DE TECNOLOGIAS PARA PREVEN????O E CONTROLE DA CORROS??O, 34 |
author_role |
author |
author2 |
SOUZA, JOSE A.B. de OLIVEIRA, MARA C.L. de ANTUNES, RENATO A. CONGRESSO BRASILEIRO DE CORROS??O, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSI??N Y PROTECCI??N, 10th.; CONCURSO DE FOTOGRAFIA DE CORROS??O E DEGRADA????O DE MATERIAIS, 19.; EXPOSI????O DE TECNOLOGIAS PARA PREVEN????O E CONTROLE DA CORROS??O, 34 |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
CORREA, OLANDIR V. SOUZA, JOSE A.B. de OLIVEIRA, MARA C.L. de ANTUNES, RENATO A. CONGRESSO BRASILEIRO DE CORROS??O, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSI??N Y PROTECCI??N, 10th.; CONCURSO DE FOTOGRAFIA DE CORROS??O E DEGRADA????O DE MATERIAIS, 19.; EXPOSI????O DE TECNOLOGIAS PARA PREVEN????O E CONTROLE DA CORROS??O, 34 |
dc.subject.por.fl_str_mv |
aluminium alloys precipitation hardening corrosion aging hydroxides evaluation polarization spectroscopy |
topic |
aluminium alloys precipitation hardening corrosion aging hydroxides evaluation polarization spectroscopy |
description |
Al alloys of the 6XXX series (Al-Mg-Si) are employed as structural materials in a variety of industrial applications due to a combination of high mechanical strength and good corrosion resistance. The final mechanical properties are achieved after specific precipitation hardening heat treatments. The aging time during precipitation hardening is known to affect these properties and can also influence the corrosion resistance of the alloy. The susceptibility of Al alloys to corrosion in alkaline media is well-known. In this work the effect of aging time on the corrosion behavior of 6061 Al alloy was evaluated in NaOH and NaCl solutions. The material was aged at 200 ??C for times ranging from 1 to 36 h. The corrosion behavior of the aged alloy was studied using potentiodynamic polarization and electrochemical impedance spectroscopy. The results showed that the corrosion resistance was progressively lower for increasing aging times up to 8 h in NaCl and up to 24 h in NaOH. Longer aging times led to a decrease of the corrosion current density. |
publishDate |
2016 |
dc.date.evento.pt_BR.fl_str_mv |
19-23 de maio, 2014 |
dc.date.accessioned.fl_str_mv |
2016-06-29T16:28:05Z |
dc.date.available.fl_str_mv |
2016-06-29T16:28:05Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/conferenceObject |
format |
conferenceObject |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://repositorio.ipen.br/handle/123456789/26435 |
url |
http://repositorio.ipen.br/handle/123456789/26435 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.coverage.pt_BR.fl_str_mv |
I |
dc.publisher.none.fl_str_mv |
Associa????o Brasileira de Corros??o ??? ABRACO |
publisher.none.fl_str_mv |
Associa????o Brasileira de Corros??o ??? ABRACO |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional do IPEN instname:Instituto de Pesquisas Energéticas e Nucleares (IPEN) instacron:IPEN |
instname_str |
Instituto de Pesquisas Energéticas e Nucleares (IPEN) |
instacron_str |
IPEN |
institution |
IPEN |
reponame_str |
Repositório Institucional do IPEN |
collection |
Repositório Institucional do IPEN |
bitstream.url.fl_str_mv |
http://repositorio.ipen.br/bitstream/123456789/26435/1/22346.pdf http://repositorio.ipen.br/bitstream/123456789/26435/2/license.txt |
bitstream.checksum.fl_str_mv |
91ce5e4080ea9f089085f56acb3d4799 8a4605be74aa9ea9d79846c1fba20a33 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional do IPEN - Instituto de Pesquisas Energéticas e Nucleares (IPEN) |
repository.mail.fl_str_mv |
bibl@ipen.br |
_version_ |
1767254239169478656 |