Effect of Acacia Melanoxylon fibre morphology on papermaking potential

• Autor(a) principal: Anjos, O.
• Data de Publicação: 2011
• Outros Autores: Santos, António, Simões, Rogério
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
• Texto Completo: http://hdl.handle.net/10400.11/6478
• topic: Pulping; Wood chips; Fibers Analysis; Acacia melanoxylon; Wood pulp Testing

This paper reports on the relationship between the fibre morphology of six Acacia melanoxylon bleached kraft pulps, produced from wood chips with basic densities of 449, 489, 493, 505, 514 and 616 kg/m3, and their papermaking potential. Six wood samples were selected in order to provide pulps with markedly different fibre morphological properties. The pulps were beaten in a PFI mill at 500, 2500 and 4500 revolutions under a refining intensity of 1.7 N/mm and their papermaking potential evaluated. The mean values of fibre length, fibre width and coarseness ranged between 0.78 and 0.99 mm, 17.8 and 19.4 cm, and 4.8 and 6.2 mg/100 m, respectively. As expected, the fibres characteristics have very high impact on handsheet structure, including smoothness, and on mechanical and optical properties, for the unbeaten pulps. At a given beating input (same PFI revolutions), the differences between pulps remain very high. Moreover, for a given paper density, tensile and tear strength, and light scattering coefficient are very sensitive to mean pulp fibre characteristics.