Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/7682 |
Resumo: | Solid Oxide Fuel Cells (SOFCs) are energy conversion devices, capable of generating clean and renewable energy with high efficiency, and regarded as one of the enabling key technologies for future hydrogen economy and stationary power generation. The state of the art consists of cells with Yttria-Stabilized Zirconia (YSZ) as electrolyte and a planar design. Planar electrolytes can be obtained employing several techniques, however, tape casting is a wellestablished, low cost ceramic forming process, and almost one of the few that can be applied to manufacture ceramic sheets of controlled thickness with large areas. Organic solvents have been widely used in tape casting, but due to health, safety, disposal, cost and environmental issues, researches are focusing on aqueous systems, seeking the benefits of using water as solvent, since it is widely available, non-toxic, non-flammable and cheap. In this study, the optimization of slurry formulation and the systematic analysis of processing variables allowed the successful use of aqueous tape casting for obtaining green tapes with good mechanical characteristics (tensile strength - 11.7-12.5 MPa, strain to failure - 64- 49%) and homogeneous green microstructure with no laminating step. In turn, the sintered tapes showed homogeneous microstructure and high density (≈ 97% of theoretical density), with good mechanical and electrical characteristics (fourpoint flexural strength - 266 MPa, electrical conductivity - 4.42x10-2 S.cm-1 at 800°C), which enables their use as electrolytes in Solid Oxide Fuel Cells. |
id |
SCAR_19174b0463d6b6413de4674bfcf3e3e0 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/7682 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Goulart, Celso AntonioSouza, Dulcina Maria Pinatti Ferreira dehttp://lattes.cnpq.br/4100119317525940http://lattes.cnpq.br/90630227080709030cc269d4-4cd1-4cf4-b12a-f1e2f9f1947e2016-10-04T18:56:32Z2016-10-04T18:56:32Z2016-03-10GOULART, Celso Antonio. Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7682.https://repositorio.ufscar.br/handle/ufscar/7682Solid Oxide Fuel Cells (SOFCs) are energy conversion devices, capable of generating clean and renewable energy with high efficiency, and regarded as one of the enabling key technologies for future hydrogen economy and stationary power generation. The state of the art consists of cells with Yttria-Stabilized Zirconia (YSZ) as electrolyte and a planar design. Planar electrolytes can be obtained employing several techniques, however, tape casting is a wellestablished, low cost ceramic forming process, and almost one of the few that can be applied to manufacture ceramic sheets of controlled thickness with large areas. Organic solvents have been widely used in tape casting, but due to health, safety, disposal, cost and environmental issues, researches are focusing on aqueous systems, seeking the benefits of using water as solvent, since it is widely available, non-toxic, non-flammable and cheap. In this study, the optimization of slurry formulation and the systematic analysis of processing variables allowed the successful use of aqueous tape casting for obtaining green tapes with good mechanical characteristics (tensile strength - 11.7-12.5 MPa, strain to failure - 64- 49%) and homogeneous green microstructure with no laminating step. In turn, the sintered tapes showed homogeneous microstructure and high density (≈ 97% of theoretical density), with good mechanical and electrical characteristics (fourpoint flexural strength - 266 MPa, electrical conductivity - 4.42x10-2 S.cm-1 at 800°C), which enables their use as electrolytes in Solid Oxide Fuel Cells.As Células a Combustível de Óxido Sólido (CaCOS) são dispositivos de conversão de energia, capazes de gerar energia limpa e renovável com alta eficiência, e consideradas como uma das tecnologias essenciais para uma futura economia baseada em hidrogênio e para a geração de energia estacionária. O estado da arte consiste de células com eletrólitos planos de Zircônia Estabilizada com Ítria. Eletrólitos planares podem ser obtidos através de diversas técnicas, no entanto, a colagem de fita é uma técnica de processamento cerâmico bem estabelecida e de baixo custo, e uma das poucas que pode ser aplicada para a fabricação de filmes cerâmicos de espessura controlada e com grandes áreas. Solventes orgânicos têm sido amplamente utilizados nesse processo, entretanto, devido a problemas de saúde, de segurança, de descarte, de custo e preocupações ambientais, as pesquisas estão se concentrando em sistemas aquosos, buscando os benefícios de usar água como solvente, uma vez que esta apresenta grande disponibilidade e baixo custo, além de não ser tóxica nem inflamável. Neste estudo, a otimização da formulação de suspensões e a análise sistemática das variáveis de processamento permitiram o uso bem-sucedido da colagem de fita aquosa na obtenção de fitas com ótimas características mecânicas (resistência à tração - 11,7-12,5 MPa, deformação - 64-49%) e microestruturas a verde homogêneas sem a necessidade de uma etapa de laminação. Por sua vez, as fitas sinterizadas apresentaram microestrutura homogénea e alta densidade (≈ 97% da densidade teórica), com boas características mecânicas e eléctricas (resistência à flexão de quatro pontos - 266 MPa, condutividade eléctrica - 4.42x10-2 S.cm-1 a 800°C), o que permite sua utilização como eletrólitos em CaCOS.Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)porUniversidade Federal de São CarlosCâmpus São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarCaCOSZircônia estabilizada com ítriaColagem de fita aquosaProcessamento cerâmicoENGENHARIAS::ENGENHARIA CIVILObtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítriaObtention of planar electrolytes of yttria stabilizedb zirconia by aqueous tape castinginfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisOnline60060070fa011e-1108-4239-97ab-fe5cd4b2d233info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINALDissCAG.pdfDissCAG.pdfapplication/pdf4802028https://repositorio.ufscar.br/bitstream/ufscar/7682/1/DissCAG.pdf4ae7b0204ed655d1b2e282ed03e96a1cMD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81957https://repositorio.ufscar.br/bitstream/ufscar/7682/2/license.txtae0398b6f8b235e40ad82cba6c50031dMD52TEXTDissCAG.pdf.txtDissCAG.pdf.txtExtracted texttext/plain131254https://repositorio.ufscar.br/bitstream/ufscar/7682/3/DissCAG.pdf.txtea8acb17c0b0104c1baf7af53a406ea0MD53THUMBNAILDissCAG.pdf.jpgDissCAG.pdf.jpgIM Thumbnailimage/jpeg6243https://repositorio.ufscar.br/bitstream/ufscar/7682/4/DissCAG.pdf.jpg5fbbfe7397fe89f6c363e28abe998760MD54ufscar/76822023-09-18 18:30:53.449oai:repositorio.ufscar.br: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Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:30:53Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
dc.title.alternative.eng.fl_str_mv |
Obtention of planar electrolytes of yttria stabilizedb zirconia by aqueous tape casting |
title |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
spellingShingle |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria Goulart, Celso Antonio CaCOS Zircônia estabilizada com ítria Colagem de fita aquosa Processamento cerâmico ENGENHARIAS::ENGENHARIA CIVIL |
title_short |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
title_full |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
title_fullStr |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
title_full_unstemmed |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
title_sort |
Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria |
author |
Goulart, Celso Antonio |
author_facet |
Goulart, Celso Antonio |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/9063022708070903 |
dc.contributor.author.fl_str_mv |
Goulart, Celso Antonio |
dc.contributor.advisor1.fl_str_mv |
Souza, Dulcina Maria Pinatti Ferreira de |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/4100119317525940 |
dc.contributor.authorID.fl_str_mv |
0cc269d4-4cd1-4cf4-b12a-f1e2f9f1947e |
contributor_str_mv |
Souza, Dulcina Maria Pinatti Ferreira de |
dc.subject.por.fl_str_mv |
CaCOS Zircônia estabilizada com ítria Colagem de fita aquosa Processamento cerâmico |
topic |
CaCOS Zircônia estabilizada com ítria Colagem de fita aquosa Processamento cerâmico ENGENHARIAS::ENGENHARIA CIVIL |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA CIVIL |
description |
Solid Oxide Fuel Cells (SOFCs) are energy conversion devices, capable of generating clean and renewable energy with high efficiency, and regarded as one of the enabling key technologies for future hydrogen economy and stationary power generation. The state of the art consists of cells with Yttria-Stabilized Zirconia (YSZ) as electrolyte and a planar design. Planar electrolytes can be obtained employing several techniques, however, tape casting is a wellestablished, low cost ceramic forming process, and almost one of the few that can be applied to manufacture ceramic sheets of controlled thickness with large areas. Organic solvents have been widely used in tape casting, but due to health, safety, disposal, cost and environmental issues, researches are focusing on aqueous systems, seeking the benefits of using water as solvent, since it is widely available, non-toxic, non-flammable and cheap. In this study, the optimization of slurry formulation and the systematic analysis of processing variables allowed the successful use of aqueous tape casting for obtaining green tapes with good mechanical characteristics (tensile strength - 11.7-12.5 MPa, strain to failure - 64- 49%) and homogeneous green microstructure with no laminating step. In turn, the sintered tapes showed homogeneous microstructure and high density (≈ 97% of theoretical density), with good mechanical and electrical characteristics (fourpoint flexural strength - 266 MPa, electrical conductivity - 4.42x10-2 S.cm-1 at 800°C), which enables their use as electrolytes in Solid Oxide Fuel Cells. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-10-04T18:56:32Z |
dc.date.available.fl_str_mv |
2016-10-04T18:56:32Z |
dc.date.issued.fl_str_mv |
2016-03-10 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
GOULART, Celso Antonio. Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7682. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/7682 |
identifier_str_mv |
GOULART, Celso Antonio. Obtenção por colagem de fita aquosa de eletrólitos planos de zircônia estabilizada com ítria. 2016. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Universidade Federal de São Carlos, São Carlos, 2016. Disponível em: https://repositorio.ufscar.br/handle/ufscar/7682. |
url |
https://repositorio.ufscar.br/handle/ufscar/7682 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
600 600 |
dc.relation.authority.fl_str_mv |
70fa011e-1108-4239-97ab-fe5cd4b2d233 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos Câmpus São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/7682/1/DissCAG.pdf https://repositorio.ufscar.br/bitstream/ufscar/7682/2/license.txt https://repositorio.ufscar.br/bitstream/ufscar/7682/3/DissCAG.pdf.txt https://repositorio.ufscar.br/bitstream/ufscar/7682/4/DissCAG.pdf.jpg |
bitstream.checksum.fl_str_mv |
4ae7b0204ed655d1b2e282ed03e96a1c ae0398b6f8b235e40ad82cba6c50031d ea8acb17c0b0104c1baf7af53a406ea0 5fbbfe7397fe89f6c363e28abe998760 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136309847818240 |