Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente
Autor(a) principal: | |
---|---|
Data de Publicação: | 2007 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFU |
Texto Completo: | https://repositorio.ufu.br/handle/123456789/17040 |
Resumo: | Studies concerning the effects of different post systems insertion depth on the strain and fracture resistance of endodontically treated teeth remain controversial. The purpose of this study was to investigate in vitro the effects of different post systems and depth of post insertion on the strain and fracture resistance of endodontically treated bovine incisors. One hundred thirty-five freshly extracted bovine incisors were sectioned 15 mm from their apices, endodontically treated and divided into 3 groups (n=45): GFP, glass fiber post; PSP, prefabricated steel post; CMC, cast metal core. Each group was divided into 3 subgroups (n=15) according to the post lenght: 5.0 mm; 7.5 mm; 10.0 mm. All teeth were restored with complete metal crowns. In the strain-gauge measurement were used two strain-gages for tooth bonded in one proximal and buccal surfaces of the tooth. Microstrain values (μS) were obtained and related of fracture resistance. The fracture resistance (N) was measured in a universal testing machine at 45 degrees to the long axis of the tooth until failure. The data were analyzed with 2-way analyses of variance, followed by the Tukey HSD test (α=.05). Fracture modes were recorded based on the degree of tooth structure and restoration damage. The results showed that microstrain was always higher in buccal surface than lingual surface in any post and length. In metallic posts with 5.0 mm length resulted in increased strain, mainly in proximal surface. The 2-way analyses showed that the post length was statistically significant for the metallic post. In length of 10.0 mm the CMC showed the highest fracture resistance. However, the GFP showed no statistically difference in fracture resistance in 3 post length. The root fractures were observed in CMC and PSP. In GFP was observed almost every fracture in the resin core and post. |
id |
UFU_454dc6be52002a33b556929db53b423b |
---|---|
oai_identifier_str |
oai:repositorio.ufu.br:123456789/17040 |
network_acronym_str |
UFU |
network_name_str |
Repositório Institucional da UFU |
repository_id_str |
|
spelling |
2016-06-22T18:47:41Z2007-08-102016-06-22T18:47:41Z2007-02-16SANTOS FILHO, Paulo César de Freitas. Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente. 2007. 113 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2007.https://repositorio.ufu.br/handle/123456789/17040Studies concerning the effects of different post systems insertion depth on the strain and fracture resistance of endodontically treated teeth remain controversial. The purpose of this study was to investigate in vitro the effects of different post systems and depth of post insertion on the strain and fracture resistance of endodontically treated bovine incisors. One hundred thirty-five freshly extracted bovine incisors were sectioned 15 mm from their apices, endodontically treated and divided into 3 groups (n=45): GFP, glass fiber post; PSP, prefabricated steel post; CMC, cast metal core. Each group was divided into 3 subgroups (n=15) according to the post lenght: 5.0 mm; 7.5 mm; 10.0 mm. All teeth were restored with complete metal crowns. In the strain-gauge measurement were used two strain-gages for tooth bonded in one proximal and buccal surfaces of the tooth. Microstrain values (μS) were obtained and related of fracture resistance. The fracture resistance (N) was measured in a universal testing machine at 45 degrees to the long axis of the tooth until failure. The data were analyzed with 2-way analyses of variance, followed by the Tukey HSD test (α=.05). Fracture modes were recorded based on the degree of tooth structure and restoration damage. The results showed that microstrain was always higher in buccal surface than lingual surface in any post and length. In metallic posts with 5.0 mm length resulted in increased strain, mainly in proximal surface. The 2-way analyses showed that the post length was statistically significant for the metallic post. In length of 10.0 mm the CMC showed the highest fracture resistance. However, the GFP showed no statistically difference in fracture resistance in 3 post length. The root fractures were observed in CMC and PSP. In GFP was observed almost every fracture in the resin core and post.Verifica-se grande controvérsia sobre os efeitos da extensão de diferentes retentores intra-radiculares na resistência de dentes tratados endodonticamente. O objetivo deste trabalho foi avaliar a influência de diferentes extensões e tipos de retentores intra-radiculares na deformação e resistência à fratura de dentes tratados endodonticamente. Cento e trinta e cinco raízes bovinas foram seccionadas com 15 mm, endodonticamente tratadas e aleatoriamente divididas em 3 grupos (n=45): PFV, pino de fibra de vidro; PPM, pino pré-fabricado metálico; NMF, núcleo metálico fundido. Posteriormente, cada grupo foi dividido em 3 subgrupos (n=15), variando a extensão do pino: 5,0 mm; 7,5 mm; 10,0 mm. Todas as raízes foram restauradas com coroas totais metálicas. No ensaio de extensometria (n=5) foram colados dois extensômetros na dentina radicular, um na face proximal e outro na face vestibular de cada amostra para medir a microdeformação (μS) sob carregamento contínuo de 0-100N. A resistência à fratura (N) foi medida em máquina de ensaio mecânico com aplicação de carga tangencial em um ângulo de 135° com o longo eixo do dente. Os dados foram submetidos à análise de variância fatorial (3x3), seguido pelo teste de Tukey (α=,05). A distribuição do padrão de fratura foi analisada baseada no grau de envolvimento do dano na estrutura dental e no retentor intra-radicular. Os resultados mostraram que a deformação foi sempre maior na face vestibular independente do tipo e extensão do retentor intra-radicular. A diminuição da extensão do pino para 5,0mm nos grupos NMF e PPM resultou em aumento significativo da deformação, principalmente na face proximal. Os valores médios de resistência à fratura indicaram que a extensão do retentor intra-radicular foi fator significante para os grupos NMF e PPM, e não significante para o grupo PFV. As fraturas radiculares foram prevalentes nos grupos NMF e PPM. No grupo PFV houve a prevalência de fratura envolvendo retentor intra-radicular e núcleo de preenchimento. Na extensão de 10,0 mm o núcleo metálico fundido apresentou maior resistência à fratura que o pino de fibra de vidro, porém este demonstrou efetividade nas três extensões estudadas, sendo superior aos pinos metálicos na extensão de 5,0 mm. Os pinos metálicos apresentaram padrão de fratura desfavorável envolvendo fraturas radiculares, enquanto os pinos de fibra de vidro apresentaram fraturas envolvendo núcleo de preenchimento, com maior facilidade de reparo.Coordenação de Aperfeiçoamento de Pessoal de Nível SuperiorMestre em Odontologiaapplication/pdfporUniversidade Federal de UberlândiaPrograma de Pós-graduação em OdontologiaUFUBRCiências da SaúdeDentes tratados endodonticamentePinos intra-radicularesResistência à fraturaExtensometriaMateriais dentáriosEndodontic treated teethEndodontic postFracture resistanceStrain gauge measurementCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIAInfluência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamenteinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisGomide, Henner Albertohttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787635Z4Soares, Carlos Joséhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790296P8Fernandes Neto, Alfredo Júliohttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780690T1Martins, Luís Roberto Marcondeshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4786910H6http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4776504J7Santos Filho, Paulo César de Freitas81759928info:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFUinstname:Universidade Federal de Uberlândia (UFU)instacron:UFUTHUMBNAILPCFSFilhoDISPRT.pdf.jpgPCFSFilhoDISPRT.pdf.jpgGenerated Thumbnailimage/jpeg1255https://repositorio.ufu.br/bitstream/123456789/17040/3/PCFSFilhoDISPRT.pdf.jpg876473977d7b4a4de9eda6430e3a2ddeMD53ORIGINALPCFSFilhoDISPRT.pdfapplication/pdf2157042https://repositorio.ufu.br/bitstream/123456789/17040/1/PCFSFilhoDISPRT.pdff1753604c3f8d2c89db3efd0a280acfeMD51TEXTPCFSFilhoDISPRT.pdf.txtPCFSFilhoDISPRT.pdf.txtExtracted texttext/plain111581https://repositorio.ufu.br/bitstream/123456789/17040/2/PCFSFilhoDISPRT.pdf.txt8eea50fd99c941219c021c2846adac35MD52123456789/170402021-03-19 17:23:50.423oai:repositorio.ufu.br:123456789/17040Repositório InstitucionalONGhttp://repositorio.ufu.br/oai/requestdiinf@dirbi.ufu.bropendoar:2024-04-26T15:20:36.031723Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU)false |
dc.title.por.fl_str_mv |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
title |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
spellingShingle |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente Santos Filho, Paulo César de Freitas Dentes tratados endodonticamente Pinos intra-radiculares Resistência à fratura Extensometria Materiais dentários Endodontic treated teeth Endodontic post Fracture resistance Strain gauge measurement CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
title_full |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
title_fullStr |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
title_full_unstemmed |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
title_sort |
Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente |
author |
Santos Filho, Paulo César de Freitas |
author_facet |
Santos Filho, Paulo César de Freitas |
author_role |
author |
dc.contributor.advisor-co1.fl_str_mv |
Gomide, Henner Alberto |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787635Z4 |
dc.contributor.advisor1.fl_str_mv |
Soares, Carlos José |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790296P8 |
dc.contributor.referee1.fl_str_mv |
Fernandes Neto, Alfredo Júlio |
dc.contributor.referee1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4780690T1 |
dc.contributor.referee2.fl_str_mv |
Martins, Luís Roberto Marcondes |
dc.contributor.referee2Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4786910H6 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4776504J7 |
dc.contributor.author.fl_str_mv |
Santos Filho, Paulo César de Freitas |
contributor_str_mv |
Gomide, Henner Alberto Soares, Carlos José Fernandes Neto, Alfredo Júlio Martins, Luís Roberto Marcondes |
dc.subject.por.fl_str_mv |
Dentes tratados endodonticamente Pinos intra-radiculares Resistência à fratura Extensometria Materiais dentários |
topic |
Dentes tratados endodonticamente Pinos intra-radiculares Resistência à fratura Extensometria Materiais dentários Endodontic treated teeth Endodontic post Fracture resistance Strain gauge measurement CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Endodontic treated teeth Endodontic post Fracture resistance Strain gauge measurement |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Studies concerning the effects of different post systems insertion depth on the strain and fracture resistance of endodontically treated teeth remain controversial. The purpose of this study was to investigate in vitro the effects of different post systems and depth of post insertion on the strain and fracture resistance of endodontically treated bovine incisors. One hundred thirty-five freshly extracted bovine incisors were sectioned 15 mm from their apices, endodontically treated and divided into 3 groups (n=45): GFP, glass fiber post; PSP, prefabricated steel post; CMC, cast metal core. Each group was divided into 3 subgroups (n=15) according to the post lenght: 5.0 mm; 7.5 mm; 10.0 mm. All teeth were restored with complete metal crowns. In the strain-gauge measurement were used two strain-gages for tooth bonded in one proximal and buccal surfaces of the tooth. Microstrain values (μS) were obtained and related of fracture resistance. The fracture resistance (N) was measured in a universal testing machine at 45 degrees to the long axis of the tooth until failure. The data were analyzed with 2-way analyses of variance, followed by the Tukey HSD test (α=.05). Fracture modes were recorded based on the degree of tooth structure and restoration damage. The results showed that microstrain was always higher in buccal surface than lingual surface in any post and length. In metallic posts with 5.0 mm length resulted in increased strain, mainly in proximal surface. The 2-way analyses showed that the post length was statistically significant for the metallic post. In length of 10.0 mm the CMC showed the highest fracture resistance. However, the GFP showed no statistically difference in fracture resistance in 3 post length. The root fractures were observed in CMC and PSP. In GFP was observed almost every fracture in the resin core and post. |
publishDate |
2007 |
dc.date.available.fl_str_mv |
2007-08-10 2016-06-22T18:47:41Z |
dc.date.issued.fl_str_mv |
2007-02-16 |
dc.date.accessioned.fl_str_mv |
2016-06-22T18:47:41Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANTOS FILHO, Paulo César de Freitas. Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente. 2007. 113 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2007. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufu.br/handle/123456789/17040 |
identifier_str_mv |
SANTOS FILHO, Paulo César de Freitas. Influência da extensão e tipo de retentor intra-radicular na deformacão e resistência à fratura de dentes tratados endodonticamente. 2007. 113 f. Dissertação (Mestrado em Ciências da Saúde) - Universidade Federal de Uberlândia, Uberlândia, 2007. |
url |
https://repositorio.ufu.br/handle/123456789/17040 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.publisher.program.fl_str_mv |
Programa de Pós-graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UFU |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Ciências da Saúde |
publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFU instname:Universidade Federal de Uberlândia (UFU) instacron:UFU |
instname_str |
Universidade Federal de Uberlândia (UFU) |
instacron_str |
UFU |
institution |
UFU |
reponame_str |
Repositório Institucional da UFU |
collection |
Repositório Institucional da UFU |
bitstream.url.fl_str_mv |
https://repositorio.ufu.br/bitstream/123456789/17040/3/PCFSFilhoDISPRT.pdf.jpg https://repositorio.ufu.br/bitstream/123456789/17040/1/PCFSFilhoDISPRT.pdf https://repositorio.ufu.br/bitstream/123456789/17040/2/PCFSFilhoDISPRT.pdf.txt |
bitstream.checksum.fl_str_mv |
876473977d7b4a4de9eda6430e3a2dde f1753604c3f8d2c89db3efd0a280acfe 8eea50fd99c941219c021c2846adac35 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU) |
repository.mail.fl_str_mv |
diinf@dirbi.ufu.br |
_version_ |
1797425668824236032 |