Push-out bond strength of root-end filling materials
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UNESP |
Texto Completo: | http://dx.doi.org/10.1590/0103-6440201600340 http://hdl.handle.net/11449/172986 |
Resumo: | The aim of this study was to evaluate the bond strength of root-end filling materials. Forty 2-mm-thick slices were obtained from human single-rooted teeth. After root canal preparation using a 1.5 mm diameter cylindrical drill, the dentinal walls were prepared by diamond ultrasonic tip (CVD T0F-2). The specimens were divided according the material (n=10): MTA Angelus (MTAA), MTA Sealer (MTAS, experimental), Sealer 26 (S26) and zinc oxide and eugenol cement (ZOE). The push-out test was performed in a mechanical test machine (EMIC DL 2000) at 1 mm/min speed. The failure type was evaluated by stereomicroscopy. The results were subjected to ANOVA and Tukey test, at 5% significance level. MTAA (19.18 MPa), MTAS (19.13 MPa) and S26 (15.91 MPa) showed higher bond strength (p<0.05). ZOE (9.50 MPa) showed the least bond strength values (p<0.05). Adhesive failure was prevalent in all groups, except for ZOE, which showed mixed failures. It was concluded that root-end filling materials MTA Angelus, MTA Sealer and Sealer 26 showed higher bond strength to dentinal walls than zinc oxide and eugenol cement after retrograde preparation. |
id |
UNSP_96365733f98fb8ce5c3b80b5ed6d213c |
---|---|
oai_identifier_str |
oai:repositorio.unesp.br:11449/172986 |
network_acronym_str |
UNSP |
network_name_str |
Repositório Institucional da UNESP |
repository_id_str |
2946 |
spelling |
Push-out bond strength of root-end filling materialsBond strengthMineral trioxide aggregatePush-outRootend filling materialThe aim of this study was to evaluate the bond strength of root-end filling materials. Forty 2-mm-thick slices were obtained from human single-rooted teeth. After root canal preparation using a 1.5 mm diameter cylindrical drill, the dentinal walls were prepared by diamond ultrasonic tip (CVD T0F-2). The specimens were divided according the material (n=10): MTA Angelus (MTAA), MTA Sealer (MTAS, experimental), Sealer 26 (S26) and zinc oxide and eugenol cement (ZOE). The push-out test was performed in a mechanical test machine (EMIC DL 2000) at 1 mm/min speed. The failure type was evaluated by stereomicroscopy. The results were subjected to ANOVA and Tukey test, at 5% significance level. MTAA (19.18 MPa), MTAS (19.13 MPa) and S26 (15.91 MPa) showed higher bond strength (p<0.05). ZOE (9.50 MPa) showed the least bond strength values (p<0.05). Adhesive failure was prevalent in all groups, except for ZOE, which showed mixed failures. It was concluded that root-end filling materials MTA Angelus, MTA Sealer and Sealer 26 showed higher bond strength to dentinal walls than zinc oxide and eugenol cement after retrograde preparation.Department of Dentistry Bauru Dental School USP - Universidade de São PauloDepartment of Restorative Dentistry Araraquara Dental School UNESP – Universidade Estadual PaulistaDepartment of Restorative Dentistry Araraquara Dental School UNESP – Universidade Estadual PaulistaUniversidade de São Paulo (USP)Universidade Estadual Paulista (Unesp)Vivan, Rodrigo RicciGuerreiro-Tanomaru, Juliane Maria [UNESP]Bosso-Martelo, Roberta [UNESP]Costa, Bernardo Cesar [UNESP]Duarte, Marco Antonio HungaroTanomaru-Filho, Mário [UNESP]2018-12-11T17:03:00Z2018-12-11T17:03:00Z2016-05-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/article332-335application/pdfhttp://dx.doi.org/10.1590/0103-6440201600340Brazilian Dental Journal, v. 27, n. 3, p. 332-335, 2016.1806-47600103-6440http://hdl.handle.net/11449/17298610.1590/0103-6440201600340S0103-644020160003003322-s2.0-84969822936S0103-64402016000300332.pdfScopusreponame:Repositório Institucional da UNESPinstname:Universidade Estadual Paulista (UNESP)instacron:UNESPengBrazilian Dental Journal0,476info:eu-repo/semantics/openAccess2023-11-08T06:09:34Zoai:repositorio.unesp.br:11449/172986Repositório InstitucionalPUBhttp://repositorio.unesp.br/oai/requestopendoar:29462023-11-08T06:09:34Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP)false |
dc.title.none.fl_str_mv |
Push-out bond strength of root-end filling materials |
title |
Push-out bond strength of root-end filling materials |
spellingShingle |
Push-out bond strength of root-end filling materials Vivan, Rodrigo Ricci Bond strength Mineral trioxide aggregate Push-out Rootend filling material |
title_short |
Push-out bond strength of root-end filling materials |
title_full |
Push-out bond strength of root-end filling materials |
title_fullStr |
Push-out bond strength of root-end filling materials |
title_full_unstemmed |
Push-out bond strength of root-end filling materials |
title_sort |
Push-out bond strength of root-end filling materials |
author |
Vivan, Rodrigo Ricci |
author_facet |
Vivan, Rodrigo Ricci Guerreiro-Tanomaru, Juliane Maria [UNESP] Bosso-Martelo, Roberta [UNESP] Costa, Bernardo Cesar [UNESP] Duarte, Marco Antonio Hungaro Tanomaru-Filho, Mário [UNESP] |
author_role |
author |
author2 |
Guerreiro-Tanomaru, Juliane Maria [UNESP] Bosso-Martelo, Roberta [UNESP] Costa, Bernardo Cesar [UNESP] Duarte, Marco Antonio Hungaro Tanomaru-Filho, Mário [UNESP] |
author2_role |
author author author author author |
dc.contributor.none.fl_str_mv |
Universidade de São Paulo (USP) Universidade Estadual Paulista (Unesp) |
dc.contributor.author.fl_str_mv |
Vivan, Rodrigo Ricci Guerreiro-Tanomaru, Juliane Maria [UNESP] Bosso-Martelo, Roberta [UNESP] Costa, Bernardo Cesar [UNESP] Duarte, Marco Antonio Hungaro Tanomaru-Filho, Mário [UNESP] |
dc.subject.por.fl_str_mv |
Bond strength Mineral trioxide aggregate Push-out Rootend filling material |
topic |
Bond strength Mineral trioxide aggregate Push-out Rootend filling material |
description |
The aim of this study was to evaluate the bond strength of root-end filling materials. Forty 2-mm-thick slices were obtained from human single-rooted teeth. After root canal preparation using a 1.5 mm diameter cylindrical drill, the dentinal walls were prepared by diamond ultrasonic tip (CVD T0F-2). The specimens were divided according the material (n=10): MTA Angelus (MTAA), MTA Sealer (MTAS, experimental), Sealer 26 (S26) and zinc oxide and eugenol cement (ZOE). The push-out test was performed in a mechanical test machine (EMIC DL 2000) at 1 mm/min speed. The failure type was evaluated by stereomicroscopy. The results were subjected to ANOVA and Tukey test, at 5% significance level. MTAA (19.18 MPa), MTAS (19.13 MPa) and S26 (15.91 MPa) showed higher bond strength (p<0.05). ZOE (9.50 MPa) showed the least bond strength values (p<0.05). Adhesive failure was prevalent in all groups, except for ZOE, which showed mixed failures. It was concluded that root-end filling materials MTA Angelus, MTA Sealer and Sealer 26 showed higher bond strength to dentinal walls than zinc oxide and eugenol cement after retrograde preparation. |
publishDate |
2016 |
dc.date.none.fl_str_mv |
2016-05-01 2018-12-11T17:03:00Z 2018-12-11T17:03:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://dx.doi.org/10.1590/0103-6440201600340 Brazilian Dental Journal, v. 27, n. 3, p. 332-335, 2016. 1806-4760 0103-6440 http://hdl.handle.net/11449/172986 10.1590/0103-6440201600340 S0103-64402016000300332 2-s2.0-84969822936 S0103-64402016000300332.pdf |
url |
http://dx.doi.org/10.1590/0103-6440201600340 http://hdl.handle.net/11449/172986 |
identifier_str_mv |
Brazilian Dental Journal, v. 27, n. 3, p. 332-335, 2016. 1806-4760 0103-6440 10.1590/0103-6440201600340 S0103-64402016000300332 2-s2.0-84969822936 S0103-64402016000300332.pdf |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
Brazilian Dental Journal 0,476 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
332-335 application/pdf |
dc.source.none.fl_str_mv |
Scopus reponame:Repositório Institucional da UNESP instname:Universidade Estadual Paulista (UNESP) instacron:UNESP |
instname_str |
Universidade Estadual Paulista (UNESP) |
instacron_str |
UNESP |
institution |
UNESP |
reponame_str |
Repositório Institucional da UNESP |
collection |
Repositório Institucional da UNESP |
repository.name.fl_str_mv |
Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP) |
repository.mail.fl_str_mv |
|
_version_ |
1799964858579419136 |