A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UNESP |
Texto Completo: | http://dx.doi.org/10.1016/j.surfcoat.2017.11.033 http://hdl.handle.net/11449/175504 |
Resumo: | The present study aims to compare the corrosion and tribocorrosion behaviour of nitrocarburized, gas-nitrided, fluidized-bed nitrided, and plasma-nitrided Impax Supreme (equivalent to AISI P20) pre-hardened plastic mould steel. Corrosion behaviour was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization in 3.5 wt% NaCl solution. Tribocorrosion tests were performed in the same solution under open circuit potential during sliding against 10 mm alumina balls. Results showed that plasma-nitrided samples presented better corrosion behaviour in terms of tendency to corrosion, corrosion rate, and polarization resistance, as compared to the other studied surface treatments. Together with nitrocarburised samples, plasma-nitrided samples also exhibited lower tendency to corrosion under sliding. |
id |
UNSP_ca954a558442c3e827fde9804274cb6e |
---|---|
oai_identifier_str |
oai:repositorio.unesp.br:11449/175504 |
network_acronym_str |
UNSP |
network_name_str |
Repositório Institucional da UNESP |
repository_id_str |
2946 |
spelling |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steelCorrosionNitridingNitrocarburisingPlastic mould steelTribocorrosionThe present study aims to compare the corrosion and tribocorrosion behaviour of nitrocarburized, gas-nitrided, fluidized-bed nitrided, and plasma-nitrided Impax Supreme (equivalent to AISI P20) pre-hardened plastic mould steel. Corrosion behaviour was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization in 3.5 wt% NaCl solution. Tribocorrosion tests were performed in the same solution under open circuit potential during sliding against 10 mm alumina balls. Results showed that plasma-nitrided samples presented better corrosion behaviour in terms of tendency to corrosion, corrosion rate, and polarization resistance, as compared to the other studied surface treatments. Together with nitrocarburised samples, plasma-nitrided samples also exhibited lower tendency to corrosion under sliding.Calouste Gulbenkian FoundationFundació Catalana de TrasplantamentYildiz Technical University Department of Metallurgical and Materials Engineering Faculty of Chemistry & Metallurgy, Davutpasa Campus, 34210 EsenlerCMEMS-UMinho - Center for MicroElectroMechanical Systems Universidade do Minho, AzurémUniversidade do Minho SEMAT/UM, AzurémUNESP—Univ. Estadual Paulista Faculdade de Ciências de Bauru Dep. FísicaIBTN Br – Brazilan Branch of the Institute of Biomaterials Tribocorrosion and NanomedicineUniversidade do Minho Dept. Eng. Mecânica, AzurémUNESP—Univ. Estadual Paulista Faculdade de Ciências de Bauru Dep. FísicaFundació Catalana de Trasplantament: UID/EEA/04436/2013Faculty of Chemistry & MetallurgyUniversidade do MinhoSEMAT/UMUniversidade Estadual Paulista (Unesp)Tribocorrosion and NanomedicineDept. Eng. MecânicaBoztepe, E.Alves, A. C.Ariza, E.Rocha, L. A. [UNESP]Cansever, N.Toptan, F.2018-12-11T17:16:05Z2018-12-11T17:16:05Z2018-01-25info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/article116-123application/pdfhttp://dx.doi.org/10.1016/j.surfcoat.2017.11.033Surface and Coatings Technology, v. 334, p. 116-123.0257-8972http://hdl.handle.net/11449/17550410.1016/j.surfcoat.2017.11.0332-s2.0-850344142052-s2.0-85034414205.pdfScopusreponame:Repositório Institucional da UNESPinstname:Universidade Estadual Paulista (UNESP)instacron:UNESPengSurface and Coatings Technology0,928info:eu-repo/semantics/openAccess2024-04-25T17:39:59Zoai:repositorio.unesp.br:11449/175504Repositório InstitucionalPUBhttp://repositorio.unesp.br/oai/requestopendoar:29462024-04-25T17:39:59Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP)false |
dc.title.none.fl_str_mv |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
title |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
spellingShingle |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel Boztepe, E. Corrosion Nitriding Nitrocarburising Plastic mould steel Tribocorrosion |
title_short |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
title_full |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
title_fullStr |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
title_full_unstemmed |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
title_sort |
A comparative investigation of the corrosion and tribocorrosion behaviour of nitrocarburized, gas nitrided, fluidized-bed nitrided, and plasma nitrided plastic mould steel |
author |
Boztepe, E. |
author_facet |
Boztepe, E. Alves, A. C. Ariza, E. Rocha, L. A. [UNESP] Cansever, N. Toptan, F. |
author_role |
author |
author2 |
Alves, A. C. Ariza, E. Rocha, L. A. [UNESP] Cansever, N. Toptan, F. |
author2_role |
author author author author author |
dc.contributor.none.fl_str_mv |
Faculty of Chemistry & Metallurgy Universidade do Minho SEMAT/UM Universidade Estadual Paulista (Unesp) Tribocorrosion and Nanomedicine Dept. Eng. Mecânica |
dc.contributor.author.fl_str_mv |
Boztepe, E. Alves, A. C. Ariza, E. Rocha, L. A. [UNESP] Cansever, N. Toptan, F. |
dc.subject.por.fl_str_mv |
Corrosion Nitriding Nitrocarburising Plastic mould steel Tribocorrosion |
topic |
Corrosion Nitriding Nitrocarburising Plastic mould steel Tribocorrosion |
description |
The present study aims to compare the corrosion and tribocorrosion behaviour of nitrocarburized, gas-nitrided, fluidized-bed nitrided, and plasma-nitrided Impax Supreme (equivalent to AISI P20) pre-hardened plastic mould steel. Corrosion behaviour was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization in 3.5 wt% NaCl solution. Tribocorrosion tests were performed in the same solution under open circuit potential during sliding against 10 mm alumina balls. Results showed that plasma-nitrided samples presented better corrosion behaviour in terms of tendency to corrosion, corrosion rate, and polarization resistance, as compared to the other studied surface treatments. Together with nitrocarburised samples, plasma-nitrided samples also exhibited lower tendency to corrosion under sliding. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-12-11T17:16:05Z 2018-12-11T17:16:05Z 2018-01-25 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://dx.doi.org/10.1016/j.surfcoat.2017.11.033 Surface and Coatings Technology, v. 334, p. 116-123. 0257-8972 http://hdl.handle.net/11449/175504 10.1016/j.surfcoat.2017.11.033 2-s2.0-85034414205 2-s2.0-85034414205.pdf |
url |
http://dx.doi.org/10.1016/j.surfcoat.2017.11.033 http://hdl.handle.net/11449/175504 |
identifier_str_mv |
Surface and Coatings Technology, v. 334, p. 116-123. 0257-8972 10.1016/j.surfcoat.2017.11.033 2-s2.0-85034414205 2-s2.0-85034414205.pdf |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
Surface and Coatings Technology 0,928 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
116-123 application/pdf |
dc.source.none.fl_str_mv |
Scopus reponame:Repositório Institucional da UNESP instname:Universidade Estadual Paulista (UNESP) instacron:UNESP |
instname_str |
Universidade Estadual Paulista (UNESP) |
instacron_str |
UNESP |
institution |
UNESP |
reponame_str |
Repositório Institucional da UNESP |
collection |
Repositório Institucional da UNESP |
repository.name.fl_str_mv |
Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP) |
repository.mail.fl_str_mv |
|
_version_ |
1799965112087347200 |