Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic
Autor(a) principal: | |
---|---|
Data de Publicação: | 2004 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Journal of applied oral science (Online) |
Texto Completo: | https://www.revistas.usp.br/jaos/article/view/3221 |
Resumo: | INTRODUCTION: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik). MATERIAL AND METHOD: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer's recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion. The specimens were submitted to the shear bond test in an universal testing machine (EMIC), with the aid of a device developed for such intention, and constant speed of 0.5mm/min. RESULTS AND CONCLUSIONS: The mean resistance was 48.387MPa for Wirobond C alloy, with standard deviation of 17.718, and 55.956MPa for Remanium 2000, with standard deviation of 17.198. No statistically significant difference was observed between the shear strength of the two metal-ceramic alloys. |
id |
USP-17_3856ca686a3e7e89a7d970dedb6dc35a |
---|---|
oai_identifier_str |
oai:revistas.usp.br:article/3221 |
network_acronym_str |
USP-17 |
network_name_str |
Journal of applied oral science (Online) |
repository_id_str |
|
spelling |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic Avaliação da resistência ao cisalhamento da união entre duas ligas a base de CoCr e uma cerâmica CerâmicasTeste de cisalhamentoLigasCeramicsShear testAlloys INTRODUCTION: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik). MATERIAL AND METHOD: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer's recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion. The specimens were submitted to the shear bond test in an universal testing machine (EMIC), with the aid of a device developed for such intention, and constant speed of 0.5mm/min. RESULTS AND CONCLUSIONS: The mean resistance was 48.387MPa for Wirobond C alloy, with standard deviation of 17.718, and 55.956MPa for Remanium 2000, with standard deviation of 17.198. No statistically significant difference was observed between the shear strength of the two metal-ceramic alloys. INTRODUÇÃO: Baseados na importância da integridade da interface metal-cerâmica, este trabalho tem como objetivo avaliar a resistência ao cisalhamento da união metal-cerâmica de duas ligas de Co-Cr (Wirobond C, Bego; Remanium 2000, Dentaurum) combinadas com a cerâmica Omega 900 (Vita Zahnfabrik). MATERIAIS E MÉTODOS: Foram confeccionados 11 corpos-de-prova cilíndricos para cada liga utilizada, sendo que a porção metálica foi obtida por fundição pela técnica da cera perdida, através de enceramentos padronizados com 4mm de altura por 4mm de diâmetro. A aplicação da cerâmica foi realizada segundo recomendações do fabricante, com auxílio de uma matriz de teflon que permitia sua padronização com as mesmas dimensões da porção metálica. Os corpos-de-prova foram submetidos ao ensaio de resistência ao cisalhamento em máquina de ensaios universal (EMIC), com auxílio de dispositivo desenvolvido para tal propósito, sob velocidade constante de 0,5mm/min. RESULTADOS E CONCLUSÕES: As médias de resistência obtidas foram 48,387 MPa para a liga Wirobond C, com desvio padrão de 17,718, e 55,956 MPa para a Remanium 2000, com desvio padrão de 17,198. Após análise de variância foi possível observar que não há diferença estatisticamente significante entre os valores de resistência ao cisalhamento das duas ligas metalocerâmicas. Universidade de São Paulo. Faculdade de Odontologia de Bauru2004-12-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionapplication/pdfhttps://www.revistas.usp.br/jaos/article/view/322110.1590/S1678-77572004000400005Journal of Applied Oral Science; Vol. 12 No. 4 (2004); 280-284 Journal of Applied Oral Science; Vol. 12 Núm. 4 (2004); 280-284 Journal of Applied Oral Science; v. 12 n. 4 (2004); 280-284 1678-77651678-7757reponame:Journal of applied oral science (Online)instname:Universidade de São Paulo (USP)instacron:USPenghttps://www.revistas.usp.br/jaos/article/view/3221/3911Copyright (c) 2004 Journal of Applied Oral Scienceinfo:eu-repo/semantics/openAccessPretti, MarianaHilgert, EdsonBottino, Marco AntônioAvelar, Rander Pereira2012-04-27T11:48:35Zoai:revistas.usp.br:article/3221Revistahttp://www.scielo.br/jaosPUBhttps://www.revistas.usp.br/jaos/oai||jaos@usp.br1678-77651678-7757opendoar:2012-04-27T11:48:35Journal of applied oral science (Online) - Universidade de São Paulo (USP)false |
dc.title.none.fl_str_mv |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic Avaliação da resistência ao cisalhamento da união entre duas ligas a base de CoCr e uma cerâmica |
title |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
spellingShingle |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic Pretti, Mariana Cerâmicas Teste de cisalhamento Ligas Ceramics Shear test Alloys |
title_short |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
title_full |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
title_fullStr |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
title_full_unstemmed |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
title_sort |
Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic |
author |
Pretti, Mariana |
author_facet |
Pretti, Mariana Hilgert, Edson Bottino, Marco Antônio Avelar, Rander Pereira |
author_role |
author |
author2 |
Hilgert, Edson Bottino, Marco Antônio Avelar, Rander Pereira |
author2_role |
author author author |
dc.contributor.author.fl_str_mv |
Pretti, Mariana Hilgert, Edson Bottino, Marco Antônio Avelar, Rander Pereira |
dc.subject.por.fl_str_mv |
Cerâmicas Teste de cisalhamento Ligas Ceramics Shear test Alloys |
topic |
Cerâmicas Teste de cisalhamento Ligas Ceramics Shear test Alloys |
description |
INTRODUCTION: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik). MATERIAL AND METHOD: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer's recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion. The specimens were submitted to the shear bond test in an universal testing machine (EMIC), with the aid of a device developed for such intention, and constant speed of 0.5mm/min. RESULTS AND CONCLUSIONS: The mean resistance was 48.387MPa for Wirobond C alloy, with standard deviation of 17.718, and 55.956MPa for Remanium 2000, with standard deviation of 17.198. No statistically significant difference was observed between the shear strength of the two metal-ceramic alloys. |
publishDate |
2004 |
dc.date.none.fl_str_mv |
2004-12-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
https://www.revistas.usp.br/jaos/article/view/3221 10.1590/S1678-77572004000400005 |
url |
https://www.revistas.usp.br/jaos/article/view/3221 |
identifier_str_mv |
10.1590/S1678-77572004000400005 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
https://www.revistas.usp.br/jaos/article/view/3221/3911 |
dc.rights.driver.fl_str_mv |
Copyright (c) 2004 Journal of Applied Oral Science info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Copyright (c) 2004 Journal of Applied Oral Science |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade de São Paulo. Faculdade de Odontologia de Bauru |
publisher.none.fl_str_mv |
Universidade de São Paulo. Faculdade de Odontologia de Bauru |
dc.source.none.fl_str_mv |
Journal of Applied Oral Science; Vol. 12 No. 4 (2004); 280-284 Journal of Applied Oral Science; Vol. 12 Núm. 4 (2004); 280-284 Journal of Applied Oral Science; v. 12 n. 4 (2004); 280-284 1678-7765 1678-7757 reponame:Journal of applied oral science (Online) instname:Universidade de São Paulo (USP) instacron:USP |
instname_str |
Universidade de São Paulo (USP) |
instacron_str |
USP |
institution |
USP |
reponame_str |
Journal of applied oral science (Online) |
collection |
Journal of applied oral science (Online) |
repository.name.fl_str_mv |
Journal of applied oral science (Online) - Universidade de São Paulo (USP) |
repository.mail.fl_str_mv |
||jaos@usp.br |
_version_ |
1787713188791320576 |