Stability of crack propagation during bending tests on brittle materials
Autor(a) principal: | |
---|---|
Data de Publicação: | 2008 |
Outros Autores: | |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Cerâmica (São Paulo. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132008000300018 |
Resumo: | Applications of ceramic materials usually involve thermal stresses that can reduce their lifetime considerably. One of the most relevant mechanical properties for evaluating thermal shock damage resistance is the energy of fracture. In order to obtain this property, a stable crack growth regimen must be achieved throughout the test. In this paper, three-point bending tests are analyzed to determine how machine stiffness influences load point displacement rates. Understanding the differences between recorded and adjusted displacement rates is important in determining the stability of crack growth. This statement is corroborated by experimental data on sintered high-alumina, low-cement refractory castables. |
id |
USP-29_6a54d1a53a7f34c9690ec58488024a0b |
---|---|
oai_identifier_str |
oai:scielo:S0366-69132008000300018 |
network_acronym_str |
USP-29 |
network_name_str |
Cerâmica (São Paulo. Online) |
repository_id_str |
|
spelling |
Stability of crack propagation during bending tests on brittle materialsenergy of fracturestable crack growth3-point bending testrefractory castablestiffnessApplications of ceramic materials usually involve thermal stresses that can reduce their lifetime considerably. One of the most relevant mechanical properties for evaluating thermal shock damage resistance is the energy of fracture. In order to obtain this property, a stable crack growth regimen must be achieved throughout the test. In this paper, three-point bending tests are analyzed to determine how machine stiffness influences load point displacement rates. Understanding the differences between recorded and adjusted displacement rates is important in determining the stability of crack growth. This statement is corroborated by experimental data on sintered high-alumina, low-cement refractory castables.Associação Brasileira de Cerâmica2008-09-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132008000300018Cerâmica v.54 n.331 2008reponame:Cerâmica (São Paulo. Online)instname:Universidade de São Paulo (USP)instacron:USP10.1590/S0366-69132008000300018info:eu-repo/semantics/openAccessPeret,C. M.Rodrigues,J. A.eng2008-11-06T00:00:00Zoai:scielo:S0366-69132008000300018Revistahttps://www.scielo.br/j/ce/PUBhttps://old.scielo.br/oai/scielo-oai.phpceram.abc@gmail.com||ceram.abc@gmail.com1678-45530366-6913opendoar:2008-11-06T00:00Cerâmica (São Paulo. Online) - Universidade de São Paulo (USP)false |
dc.title.none.fl_str_mv |
Stability of crack propagation during bending tests on brittle materials |
title |
Stability of crack propagation during bending tests on brittle materials |
spellingShingle |
Stability of crack propagation during bending tests on brittle materials Peret,C. M. energy of fracture stable crack growth 3-point bending test refractory castable stiffness |
title_short |
Stability of crack propagation during bending tests on brittle materials |
title_full |
Stability of crack propagation during bending tests on brittle materials |
title_fullStr |
Stability of crack propagation during bending tests on brittle materials |
title_full_unstemmed |
Stability of crack propagation during bending tests on brittle materials |
title_sort |
Stability of crack propagation during bending tests on brittle materials |
author |
Peret,C. M. |
author_facet |
Peret,C. M. Rodrigues,J. A. |
author_role |
author |
author2 |
Rodrigues,J. A. |
author2_role |
author |
dc.contributor.author.fl_str_mv |
Peret,C. M. Rodrigues,J. A. |
dc.subject.por.fl_str_mv |
energy of fracture stable crack growth 3-point bending test refractory castable stiffness |
topic |
energy of fracture stable crack growth 3-point bending test refractory castable stiffness |
description |
Applications of ceramic materials usually involve thermal stresses that can reduce their lifetime considerably. One of the most relevant mechanical properties for evaluating thermal shock damage resistance is the energy of fracture. In order to obtain this property, a stable crack growth regimen must be achieved throughout the test. In this paper, three-point bending tests are analyzed to determine how machine stiffness influences load point displacement rates. Understanding the differences between recorded and adjusted displacement rates is important in determining the stability of crack growth. This statement is corroborated by experimental data on sintered high-alumina, low-cement refractory castables. |
publishDate |
2008 |
dc.date.none.fl_str_mv |
2008-09-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132008000300018 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132008000300018 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S0366-69132008000300018 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Associação Brasileira de Cerâmica |
publisher.none.fl_str_mv |
Associação Brasileira de Cerâmica |
dc.source.none.fl_str_mv |
Cerâmica v.54 n.331 2008 reponame:Cerâmica (São Paulo. Online) instname:Universidade de São Paulo (USP) instacron:USP |
instname_str |
Universidade de São Paulo (USP) |
instacron_str |
USP |
institution |
USP |
reponame_str |
Cerâmica (São Paulo. Online) |
collection |
Cerâmica (São Paulo. Online) |
repository.name.fl_str_mv |
Cerâmica (São Paulo. Online) - Universidade de São Paulo (USP) |
repository.mail.fl_str_mv |
ceram.abc@gmail.com||ceram.abc@gmail.com |
_version_ |
1748936781341917184 |