Structural characterization of mullites synthesizedby thermal decomposition of topaz.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2007 |
Outros Autores: | , , , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFOP |
Texto Completo: | http://www.repositorio.ufop.br/handle/123456789/4450 http://dx.doi.org/10.1590/S1516-14392007000100016 |
Resumo: | The structure of mullite obtained by thermal decomposition of topaz at 1340 °C and after additional thermal treatment at 1600 °C was characterized by 29Si and 27Al MAS NMR spectroscopy and x ray diffraction. No amorphous phase was detected by these techniques. The 29Si MAS NMR spectra of the mullite samples showed four resonance peaks at -81, -86, -90 and -94 ppm. The peak at -81 ppm corresponded to silicon near oxygen vacancies in the mullite structure. The peak at 86 ppm was related to a sillimanite-type site and was the major contribution, ranging from 42 to 50%. The two other peaks, at -90.0 ppm and -94 ppm, were interpreted as resulting from rearrangements of the sillimanite-type site by the replacement of AlO4 by SiO4 tetrahedra16. The 27Al MAS NMR data of the two samples exhibited three different peaks, two of which were attributed to tetrahedral sites at 40 -45 and 63 -67 ppm, while the third was assigned to an octahedral site at about -6 ppm. The ratio of tetrahedral to octahedral aluminum sites was found to depend on the temperature applied during the preparation of the mullite and was higher at 1600 °C. |
id |
UFOP_8b85c697d0c69d8d46aed2b909e84d14 |
---|---|
oai_identifier_str |
oai:localhost:123456789/4450 |
network_acronym_str |
UFOP |
network_name_str |
Repositório Institucional da UFOP |
repository_id_str |
3233 |
spelling |
Soares, Robson de MirandaSabioni, Antônio Claret SoaresResck, Inês SabioniFalcomer, Viviane Aparecida SilvaDias, José AlvesSilva, Naira Machado daMenezes, Sônia Maria Cabral deCosta, Geraldo Magela da2015-02-20T15:08:02Z2015-02-20T15:08:02Z2007SOARES, R. M. de et al. Structural characterization of mullites synthesizedby thermal decomposition of topaz. Materials Research, São Carlos, v. 10, n. 1, p. 75-78, 2007. Disponível em: <http://www.scielo.br/pdf/mr/v10n1/15.pdf>. Acesso em: 13 fev. 2015.1516-1439http://www.repositorio.ufop.br/handle/123456789/4450http://dx.doi.org/10.1590/S1516-14392007000100016The structure of mullite obtained by thermal decomposition of topaz at 1340 °C and after additional thermal treatment at 1600 °C was characterized by 29Si and 27Al MAS NMR spectroscopy and x ray diffraction. No amorphous phase was detected by these techniques. The 29Si MAS NMR spectra of the mullite samples showed four resonance peaks at -81, -86, -90 and -94 ppm. The peak at -81 ppm corresponded to silicon near oxygen vacancies in the mullite structure. The peak at 86 ppm was related to a sillimanite-type site and was the major contribution, ranging from 42 to 50%. The two other peaks, at -90.0 ppm and -94 ppm, were interpreted as resulting from rearrangements of the sillimanite-type site by the replacement of AlO4 by SiO4 tetrahedra16. The 27Al MAS NMR data of the two samples exhibited three different peaks, two of which were attributed to tetrahedral sites at 40 -45 and 63 -67 ppm, while the third was assigned to an octahedral site at about -6 ppm. The ratio of tetrahedral to octahedral aluminum sites was found to depend on the temperature applied during the preparation of the mullite and was higher at 1600 °C.Mullite synthesisTopazCharacterizationStructural characterization of mullites synthesizedby thermal decomposition of topaz.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleO periódico Materials Research dá permissão ao RI/UFOP para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP. Contato via email em 25 out. 2013.info:eu-repo/semantics/openAccessengreponame:Repositório Institucional da UFOPinstname:Universidade Federal de Ouro Preto (UFOP)instacron:UFOPLICENSElicense.txtlicense.txttext/plain; charset=utf-82636http://www.repositorio.ufop.br/bitstream/123456789/4450/2/license.txtc2ffdd99e58acf69202dff00d361f23aMD52ORIGINALARTIGO_StructuralCharacterizationMullites.pdfARTIGO_StructuralCharacterizationMullites.pdfapplication/pdf803998http://www.repositorio.ufop.br/bitstream/123456789/4450/1/ARTIGO_StructuralCharacterizationMullites.pdfec1aad7dd66617d0a12e0c7e2186cd83MD51123456789/44502019-06-18 12:13:36.882oai:localhost:123456789/4450PGh0bWw+Cjxib2R5Pgo8ZGl2IGFsaWduPSJqdXN0aWZ5Ij48c3Ryb25nPkxpY2VuJmNjZWRpbDthIGRvIFJlcG9zaXQmb2FjdXRlO3JpbyBJbnN0aXR1Y2lvbmFsIGRhIFVuaXZlcnNpZGFkZSBGZWRlcmFsIGRlIE91cm8gUHJldG88L3N0cm9uZz4KICA8YnI+CiAgPGJyPgogIEFvIGNvbmNvcmRhciBjb20gZXN0YSBsaWNlbiZjY2VkaWw7YSwgdm9jJmVjaXJjOyhzKSBhdXRvcihlcykgb3UgdGl0dWxhcihlcykgZG9zIGRpcmVpdG9zIGF1dG9yYWlzIGRhIG9icmEgYXF1aSBkZXNjcml0YSBjb25jZWRlKG0pICZhZ3JhdmU7CiAgPGJyPgogIFVuaXZlcnNpZGFkZSBGZWRlcmFsIGRlIE91cm8gUHJldG8gKFVGT1ApIGdlc3RvcmEgZG8gUmVwb3NpdCZvYWN1dGU7cmlvIEluc3RpdHVjaW9uYWwgZGEgVW5pdmVyc2lkYWRlIEZlZGVyYWwgZGUgT3VybyBQcmV0bwogIDxicj4KICAoUkktVUZPUCksIG8gZGlyZWl0byBuJmF0aWxkZTtvLWV4Y2x1c2l2byBkZSByZXByb2R1emlyLCBjb252ZXJ0ZXIgKGNvbW8gZGVmaW5pZG8gYWJhaXhvKSBlL291IGRpc3RyaWJ1aXIgbyBkb2N1bWVudG8gZGVwb3NpdGFkbwogIDxicj4KICBlbSBmb3JtYXRvIGltcHJlc3NvLCBlbGV0ciZvY2lyYztuaWNvIG91IGVtIHF1YWxxdWVyIG91dHJvIG1laW8uCiAgPGJyPgogIDxicj4KICBWb2MmZWNpcmM7KHMpIGNvbmNvcmRhKG0pIHF1ZSBhIFVGT1AsIGdlc3RvcmEgZG8gUkktVUZPUCwgcG9kZSwgc2VtIGFsdGVyYXIgbyBjb250ZSZ1YWN1dGU7ZG8sIGNvbnZlcnRlciBvIGFycXVpdm8gZGVwb3NpdGFkbyBhCiAgPGJyPgogIHF1YWxxdWVyIG1laW8gb3UgZm9ybWF0byBjb20gZmlucyBkZSBwcmVzZXJ2YSZjY2VkaWw7JmF0aWxkZTtvLiBWb2MmZWNpcmM7KHMpIHRhbWImZWFjdXRlO20gY29uY29yZGEobSkgcXVlIGEgVUZPUCwgZ2VzdG9yYSBkbyBSSS1VRk9QLCBwb2RlCiAgPGJyPgogIG1hbnRlciBtYWlzIGRlIHVtYSBjJm9hY3V0ZTtwaWEgZGVzdGUgZGVwJm9hY3V0ZTtzaXRvIHBhcmEgZmlucyBkZSBzZWd1cmFuJmNjZWRpbDthLCA8ZW0+YmFjay11cDwvZW0+IGUvb3UgcHJlc2VydmEmY2NlZGlsOyZhdGlsZGU7by4KICA8YnI+CiAgPGJyPgogIFZvYyZlY2lyYzsocykgZGVjbGFyYShtKSBxdWUgYSBhcHJlc2VudGEmY2NlZGlsOyZhdGlsZGU7byBkbyBzZXUgdHJhYmFsaG8gJmVhY3V0ZTsgb3JpZ2luYWwgZSBxdWUgdm9jJmVjaXJjOyhzKSBwb2RlKG0pIGNvbmNlZGVyIG9zIGRpcmVpdG9zIGNvbnRpZG9zCiAgPGJyPgogIG5lc3RhIGxpY2VuJmNjZWRpbDthLiBWb2MmZWNpcmM7KHMpIHRhbWImZWFjdXRlO20gZGVjbGFyYShtKSBxdWUgbyBlbnZpbyAmZWFjdXRlOyBkZSBzZXUgY29uaGVjaW1lbnRvIGUgbiZhdGlsZGU7byBpbmZyaW5nZSBvcyBkaXJlaXRvcyBhdXRvcmFpcyBkZSBvdXRyYQogIDxicj4KICBwZXNzb2Egb3UgaW5zdGl0dWkmY2NlZGlsOyZhdGlsZGU7by4gQ2FzbyBvIGRvY3VtZW50byBhIHNlciBkZXBvc2l0YWRvIGNvbnRlbmhhIG1hdGVyaWFsIHBhcmEgbyBxdWFsIHZvYyZlY2lyYzsocykgbiZhdGlsZGU7byBkZXQmZWFjdXRlO20gYSB0aXR1bGFyaWRhZGUKICA8YnI+CiAgZG9zIGRpcmVpdG9zIGF1dG9yYWlzLCB2b2MmZWNpcmM7KHMpIGRlY2xhcmEobSkgcXVlIG9idGV2ZSBhIHBlcm1pc3MmYXRpbGRlO28gaXJyZXN0cml0YSBkbyB0aXR1bGFyIGRvcyBkaXJlaXRvcyBhdXRvcmFpcyBkZSBjb25jZWRlciAmYWdyYXZlOwogIDxicj4KICBVRk9QLCBnZXN0b3JhIGRvIFJJLVVGT1Agb3MgZGlyZWl0b3MgcmVxdWVyaWRvcyBwb3IgZXN0YSBsaWNlbiZjY2VkaWw7YSBlIHF1ZSBvcyBtYXRlcmlhaXMgZGUgcHJvcHJpZWRhZGUgZGUgdGVyY2Vpcm9zLCBlc3QmYXRpbGRlO28KICA8YnI+CiAgZGV2aWRhbWVudGUgaWRlbnRpZmljYWRvcyBlIHJlY29uaGVjaWRvcyBubyB0ZXh0byBvdSBjb250ZSZ1YWN1dGU7ZG8gZGEgYXByZXNlbnRhJmNjZWRpbDsmYXRpbGRlO28uCiAgPGJyPgogIDxicj4KICBDQVNPIE8gVFJBQkFMSE8gREVQT1NJVEFETyBURU5IQSBTSURPIEZJTkFOQ0lBRE8gT1UgQVBPSUFETyBQT1IgVU0gJk9hY3V0ZTtSRyZBdGlsZGU7TywgUVVFIE4mQXRpbGRlO08gQSBJTlNUSVRVSSZDY2VkaWw7JkF0aWxkZTtPIERFU1RFCiAgPGJyPgogIFJFU1BPU0lUJk9hY3V0ZTtSSU86IFZPQyZFY2lyYzsgREVDTEFSQSBURVIgQ1VNUFJJRE8gVE9ET1MgT1MgRElSRUlUT1MgREUgUkVWSVMmQXRpbGRlO08gRSBRVUFJU1FVRVIgT1VUUkFTIE9CUklHQSZDY2VkaWw7Jk90aWxkZTtFUwogIDxicj4KICBSRVFVRVJJREFTIFBFTE8gQ09OVFJBVE8gT1UgQUNPUkRPLiAKICA8YnI+CiAgPGJyPgogIE8gcmVwb3NpdCZvYWN1dGU7cmlvIGlkZW50aWZpY2FyJmFhY3V0ZTsgY2xhcmFtZW50ZSBvIHNldShzKSBub21lKHMpIGNvbW8gYXV0b3IoZXMpIG91IHRpdHVsYXIoZXMpIGRvIGRpcmVpdG8gZGUgYXV0b3IoZXMpIGRvIGRvY3VtZW50bwogIDxicj4KICBzdWJtZXRpZG8gZSBkZWNsYXJhIHF1ZSBuJmF0aWxkZTtvIGZhciZhYWN1dGU7IHF1YWxxdWVyIGFsdGVyYSZjY2VkaWw7JmF0aWxkZTtvIGFsJmVhY3V0ZTttIGRhcyBwZXJtaXRpZGFzIHBvciBlc3RhIGxpY2VuJmNjZWRpbDthLjwvcD4KPC9kaXY+CjwvYm9keT4KPC9odG1sPgo=Repositório InstitucionalPUBhttp://www.repositorio.ufop.br/oai/requestrepositorio@ufop.edu.bropendoar:32332019-06-18T16:13:36Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP)false |
dc.title.pt_BR.fl_str_mv |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
title |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
spellingShingle |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. Soares, Robson de Miranda Mullite synthesis Topaz Characterization |
title_short |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
title_full |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
title_fullStr |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
title_full_unstemmed |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
title_sort |
Structural characterization of mullites synthesizedby thermal decomposition of topaz. |
author |
Soares, Robson de Miranda |
author_facet |
Soares, Robson de Miranda Sabioni, Antônio Claret Soares Resck, Inês Sabioni Falcomer, Viviane Aparecida Silva Dias, José Alves Silva, Naira Machado da Menezes, Sônia Maria Cabral de Costa, Geraldo Magela da |
author_role |
author |
author2 |
Sabioni, Antônio Claret Soares Resck, Inês Sabioni Falcomer, Viviane Aparecida Silva Dias, José Alves Silva, Naira Machado da Menezes, Sônia Maria Cabral de Costa, Geraldo Magela da |
author2_role |
author author author author author author author |
dc.contributor.author.fl_str_mv |
Soares, Robson de Miranda Sabioni, Antônio Claret Soares Resck, Inês Sabioni Falcomer, Viviane Aparecida Silva Dias, José Alves Silva, Naira Machado da Menezes, Sônia Maria Cabral de Costa, Geraldo Magela da |
dc.subject.por.fl_str_mv |
Mullite synthesis Topaz Characterization |
topic |
Mullite synthesis Topaz Characterization |
description |
The structure of mullite obtained by thermal decomposition of topaz at 1340 °C and after additional thermal treatment at 1600 °C was characterized by 29Si and 27Al MAS NMR spectroscopy and x ray diffraction. No amorphous phase was detected by these techniques. The 29Si MAS NMR spectra of the mullite samples showed four resonance peaks at -81, -86, -90 and -94 ppm. The peak at -81 ppm corresponded to silicon near oxygen vacancies in the mullite structure. The peak at 86 ppm was related to a sillimanite-type site and was the major contribution, ranging from 42 to 50%. The two other peaks, at -90.0 ppm and -94 ppm, were interpreted as resulting from rearrangements of the sillimanite-type site by the replacement of AlO4 by SiO4 tetrahedra16. The 27Al MAS NMR data of the two samples exhibited three different peaks, two of which were attributed to tetrahedral sites at 40 -45 and 63 -67 ppm, while the third was assigned to an octahedral site at about -6 ppm. The ratio of tetrahedral to octahedral aluminum sites was found to depend on the temperature applied during the preparation of the mullite and was higher at 1600 °C. |
publishDate |
2007 |
dc.date.issued.fl_str_mv |
2007 |
dc.date.accessioned.fl_str_mv |
2015-02-20T15:08:02Z |
dc.date.available.fl_str_mv |
2015-02-20T15:08:02Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SOARES, R. M. de et al. Structural characterization of mullites synthesizedby thermal decomposition of topaz. Materials Research, São Carlos, v. 10, n. 1, p. 75-78, 2007. Disponível em: <http://www.scielo.br/pdf/mr/v10n1/15.pdf>. Acesso em: 13 fev. 2015. |
dc.identifier.uri.fl_str_mv |
http://www.repositorio.ufop.br/handle/123456789/4450 |
dc.identifier.issn.none.fl_str_mv |
1516-1439 |
dc.identifier.doi.none.fl_str_mv |
http://dx.doi.org/10.1590/S1516-14392007000100016 |
identifier_str_mv |
SOARES, R. M. de et al. Structural characterization of mullites synthesizedby thermal decomposition of topaz. Materials Research, São Carlos, v. 10, n. 1, p. 75-78, 2007. Disponível em: <http://www.scielo.br/pdf/mr/v10n1/15.pdf>. Acesso em: 13 fev. 2015. 1516-1439 |
url |
http://www.repositorio.ufop.br/handle/123456789/4450 http://dx.doi.org/10.1590/S1516-14392007000100016 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFOP instname:Universidade Federal de Ouro Preto (UFOP) instacron:UFOP |
instname_str |
Universidade Federal de Ouro Preto (UFOP) |
instacron_str |
UFOP |
institution |
UFOP |
reponame_str |
Repositório Institucional da UFOP |
collection |
Repositório Institucional da UFOP |
bitstream.url.fl_str_mv |
http://www.repositorio.ufop.br/bitstream/123456789/4450/2/license.txt http://www.repositorio.ufop.br/bitstream/123456789/4450/1/ARTIGO_StructuralCharacterizationMullites.pdf |
bitstream.checksum.fl_str_mv |
c2ffdd99e58acf69202dff00d361f23a ec1aad7dd66617d0a12e0c7e2186cd83 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP) |
repository.mail.fl_str_mv |
repositorio@ufop.edu.br |
_version_ |
1793531348970897408 |