A study of microstructure and wear behaviour of TiB2/Al metal matrix composites

• Autor(a) principal: Sreenivasan,A.
• Data de Publicação: 2011
• Outros Autores: Paul Vizhian,S., Shivakumar,N.D., Muniraju,M., Raguraman,M.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Latin American journal of solids and structures (Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1679-78252011000100001
• topic: MMC composites; wear; microstructure

The present paper deals with the study of microstructure and wear characteristics of TiB2 reinforced aluminium metal matrix composites (MMCs). Matrix alloys with 5, 10 and 15% of TiB2 were made using stir casting technique. Effect of sliding velocity on the wear behaviour and tribo-chemistry of the worn surfaces of both matrix and composites sliding against a EN24 steel disc has been investigated under dry conditions. A pin-on-disc wear testing machine was used to find the wear rate, in which EN24 steel disc was used as the counter face, loads of 10-60N in steps of 10N and speeds of 100, 200, 300, 400 and 500 rpm were employed. The results showed that the wear rate was increased with an increase in load and sliding speed for both the materials. However, a lower wear rate was obtained for MMCs when compared to the matrix alloys. The wear transition from slight to severe was presented at the critical applied loads. The transition loads for the MMCs were much higher than that of the matrix alloy. The transition loads were increased with increase in TiB2 and the same was decreased with the increase of sliding speeds. The SEM and EDS analyses were undertaken to demonstrate the effect of TiB2 particles on the wear mechanism for each conditions.