Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Materials research (São Carlos. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392019000200220 |
Resumo: | Abstract Stress corrosion cracking (SCC) of UNS S31603 austenitic stainless steel (ASS), UNS S32205 duplex stainless steel (DSS) and UNS S32750 super duplex stainless steel (SDSS) was investigated. SCC tests were carried out at 110 ºC for 500 h under drops of synthetic seawater (DET, drop evaporation test). Two loading conditions were investigated: 50 % and 100 % of the experimental yield strength of each steel. DSS and SDSS specimens showed no susceptibility to SCC under loading of 50 % of their yield strength, contrary to ASS, but all steels fractured at the highest load. SCC nucleated under the salt deposit formed on the surface of all specimens. SCC propagation was mainly transgranular, but SCC propagation of DSS also featured crack ramification in the austenite phase. In addition, SDSS also presented crack propagation along the ferrite/austenite interfaces. Transgranular cleavage fracture was also observed in all fractured specimens, but DSS also presented ferrite/austenite interfacial brittle fracture, while SDSS also featured intergranular brittle fracture. |
id |
ABMABCABPOL-1_2849a80e37dac3709fad295c236d020a |
---|---|
oai_identifier_str |
oai:scielo:S1516-14392019000200220 |
network_acronym_str |
ABMABCABPOL-1 |
network_name_str |
Materials research (São Carlos. Online) |
repository_id_str |
|
spelling |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic SeawaterStress Corrosion CrackingDrop Evaporation TestStainless SteelsAbstract Stress corrosion cracking (SCC) of UNS S31603 austenitic stainless steel (ASS), UNS S32205 duplex stainless steel (DSS) and UNS S32750 super duplex stainless steel (SDSS) was investigated. SCC tests were carried out at 110 ºC for 500 h under drops of synthetic seawater (DET, drop evaporation test). Two loading conditions were investigated: 50 % and 100 % of the experimental yield strength of each steel. DSS and SDSS specimens showed no susceptibility to SCC under loading of 50 % of their yield strength, contrary to ASS, but all steels fractured at the highest load. SCC nucleated under the salt deposit formed on the surface of all specimens. SCC propagation was mainly transgranular, but SCC propagation of DSS also featured crack ramification in the austenite phase. In addition, SDSS also presented crack propagation along the ferrite/austenite interfaces. Transgranular cleavage fracture was also observed in all fractured specimens, but DSS also presented ferrite/austenite interfacial brittle fracture, while SDSS also featured intergranular brittle fracture.ABM, ABC, ABPol2019-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392019000200220Materials Research v.22 n.2 2019reponame:Materials research (São Carlos. Online)instname:Universidade Federal de São Carlos (UFSCAR)instacron:ABM ABC ABPOL10.1590/1980-5373-mr-2018-0211info:eu-repo/semantics/openAccessPereira,Henrique BoschettiPanossian,ZehbourBaptista,Ilson PalmieriAzevedo,Cesar Roberto de Fariaseng2019-01-31T00:00:00Zoai:scielo:S1516-14392019000200220Revistahttp://www.scielo.br/mrPUBhttps://old.scielo.br/oai/scielo-oai.phpdedz@power.ufscar.br1980-53731516-1439opendoar:2019-01-31T00:00Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.none.fl_str_mv |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
title |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
spellingShingle |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater Pereira,Henrique Boschetti Stress Corrosion Cracking Drop Evaporation Test Stainless Steels |
title_short |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
title_full |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
title_fullStr |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
title_full_unstemmed |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
title_sort |
Investigation of Stress Corrosion Cracking of Austenitic, Duplex and Super Duplex Stainless Steels under Drop Evaporation Test using Synthetic Seawater |
author |
Pereira,Henrique Boschetti |
author_facet |
Pereira,Henrique Boschetti Panossian,Zehbour Baptista,Ilson Palmieri Azevedo,Cesar Roberto de Farias |
author_role |
author |
author2 |
Panossian,Zehbour Baptista,Ilson Palmieri Azevedo,Cesar Roberto de Farias |
author2_role |
author author author |
dc.contributor.author.fl_str_mv |
Pereira,Henrique Boschetti Panossian,Zehbour Baptista,Ilson Palmieri Azevedo,Cesar Roberto de Farias |
dc.subject.por.fl_str_mv |
Stress Corrosion Cracking Drop Evaporation Test Stainless Steels |
topic |
Stress Corrosion Cracking Drop Evaporation Test Stainless Steels |
description |
Abstract Stress corrosion cracking (SCC) of UNS S31603 austenitic stainless steel (ASS), UNS S32205 duplex stainless steel (DSS) and UNS S32750 super duplex stainless steel (SDSS) was investigated. SCC tests were carried out at 110 ºC for 500 h under drops of synthetic seawater (DET, drop evaporation test). Two loading conditions were investigated: 50 % and 100 % of the experimental yield strength of each steel. DSS and SDSS specimens showed no susceptibility to SCC under loading of 50 % of their yield strength, contrary to ASS, but all steels fractured at the highest load. SCC nucleated under the salt deposit formed on the surface of all specimens. SCC propagation was mainly transgranular, but SCC propagation of DSS also featured crack ramification in the austenite phase. In addition, SDSS also presented crack propagation along the ferrite/austenite interfaces. Transgranular cleavage fracture was also observed in all fractured specimens, but DSS also presented ferrite/austenite interfacial brittle fracture, while SDSS also featured intergranular brittle fracture. |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392019000200220 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392019000200220 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1980-5373-mr-2018-0211 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
ABM, ABC, ABPol |
publisher.none.fl_str_mv |
ABM, ABC, ABPol |
dc.source.none.fl_str_mv |
Materials Research v.22 n.2 2019 reponame:Materials research (São Carlos. Online) instname:Universidade Federal de São Carlos (UFSCAR) instacron:ABM ABC ABPOL |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
ABM ABC ABPOL |
institution |
ABM ABC ABPOL |
reponame_str |
Materials research (São Carlos. Online) |
collection |
Materials research (São Carlos. Online) |
repository.name.fl_str_mv |
Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
dedz@power.ufscar.br |
_version_ |
1754212674352185344 |