Effects of Heat Treatment and Yb 3+ Concentration on the Downconversion Emission of Er 3+ /Yb 3+ Co-Doped Transparent Silicate Glass-Ceramics

• Autor(a) principal: Dan,Ho Kim
• Data de Publicação: 2019
• Outros Autores: Tap,Tran Duy, Nguyen-Truong,Hieu, Ty,Nguyen Minh, Zhou,Dacheng, Qiu,Jianbei
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Materials research (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392019000500215
• topic: Downconversion; BaF2; heat treatment; glass-ceramics; Er3+/Yb3+.

The SiO2-Al2O3-BaF2-TiO2-CaF2 transparent silicate glass-ceramics containing BaF2 nanocrystals were successfully prepared by heat treatment process through conventional melting method. Effects of heat treatment processes and Yb3+ concentration on the downconversion (DC) emission of the co-doped Er3+/Yb3+ transparent silicate glass-ceramics were investigated. With the increase of temperatures and times of heat treatment process, the DC emission intensity of the co-doped Er3+/Yb3+ glass-ceramics was significantly enhanced. At the same time, with the increase of Yb3+ concentration, the value of DC intensity of Er3+/Yb3+ co-doped bands centered at 849, 883 and 1533 nm is maximized when the concentration of Yb3+ reaches 2.5 mol.%. When the concentration exceed 2.5 mol. %, the DC emission intensity of Er3+/Yb3+ co-doped bands centered at 849, 883 and 1533 nm was decreased, owing to the self-quenching effect. It’s interesting that the DC emission intensity of Er3+/Yb3+ co-doped band centered at 978 nm didn’t quench when the Yb3+ concentration exceed 2.5 mol. %. At the same time, the DC mechanism and ET processes between Yb3+ and Er3+ ions were discussed.