Boro-Austempering Treatment of Ductile Cast Irons
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Materials research (São Carlos. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000500204 |
Resumo: | Samples of ductile cast irons alloyed with Cu, Cu-Ni and Cu-Ni-Mo were austempered, borided and boro-austempered and characterized for hardness and micro-adhesive wear behavior. The kinetics of layer formation was also studied. The boriding method used was molten borax bath, in periods of 2 and 4 hours at temperatures of 850, 900 and 950 ºC. The direct austempering treatment was performed immediately following the boriding treatment (from 850, 900 and 950 ºC) using molten salt baths at temperatures of 240, 300 and 360 ºC for 4 hours (boro-austempering treatment). For comparative purposes, the conventional austempering treatment was also conducted. Optical microscopy, scanning electron microscopy, Brinell hardness measurements (on the substrate) and Vickers (on the layers) were performed, along with micro-adhesive wear tests. The boriding treatment resulted in the formation of high hardness layers, in the range of 1450 to 1750 HV, with high wear resistance. The wear resistance of borided and boro-austempered samples were increased by 40 times when compared to as cast or austempered samples, indicating the high efficiency of this type of treatment in increasing the wear resistance of this material. |
id |
ABMABCABPOL-1_84ca5af6e76a27c0e21f4076342aac28 |
---|---|
oai_identifier_str |
oai:scielo:S1516-14392018000500204 |
network_acronym_str |
ABMABCABPOL-1 |
network_name_str |
Materials research (São Carlos. Online) |
repository_id_str |
|
spelling |
Boro-Austempering Treatment of Ductile Cast Ironsductile cast ironADIboridingboro-austemperedkinectsmicro-adhesive wear testSamples of ductile cast irons alloyed with Cu, Cu-Ni and Cu-Ni-Mo were austempered, borided and boro-austempered and characterized for hardness and micro-adhesive wear behavior. The kinetics of layer formation was also studied. The boriding method used was molten borax bath, in periods of 2 and 4 hours at temperatures of 850, 900 and 950 ºC. The direct austempering treatment was performed immediately following the boriding treatment (from 850, 900 and 950 ºC) using molten salt baths at temperatures of 240, 300 and 360 ºC for 4 hours (boro-austempering treatment). For comparative purposes, the conventional austempering treatment was also conducted. Optical microscopy, scanning electron microscopy, Brinell hardness measurements (on the substrate) and Vickers (on the layers) were performed, along with micro-adhesive wear tests. The boriding treatment resulted in the formation of high hardness layers, in the range of 1450 to 1750 HV, with high wear resistance. The wear resistance of borided and boro-austempered samples were increased by 40 times when compared to as cast or austempered samples, indicating the high efficiency of this type of treatment in increasing the wear resistance of this material.ABM, ABC, ABPol2018-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000500204Materials Research v.21 n.5 2018reponame:Materials research (São Carlos. Online)instname:Universidade Federal de São Carlos (UFSCAR)instacron:ABM ABC ABPOL10.1590/1980-5373-mr-2017-0927info:eu-repo/semantics/openAccessMariani,Fábio EdsonSoares,CarolinaLombardi Neto,AmadeuTotten,George EdwardCasteletti,Luiz Carloseng2018-07-10T00:00:00Zoai:scielo:S1516-14392018000500204Revistahttp://www.scielo.br/mrPUBhttps://old.scielo.br/oai/scielo-oai.phpdedz@power.ufscar.br1980-53731516-1439opendoar:2018-07-10T00:00Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.none.fl_str_mv |
Boro-Austempering Treatment of Ductile Cast Irons |
title |
Boro-Austempering Treatment of Ductile Cast Irons |
spellingShingle |
Boro-Austempering Treatment of Ductile Cast Irons Mariani,Fábio Edson ductile cast iron ADI boriding boro-austempered kinects micro-adhesive wear test |
title_short |
Boro-Austempering Treatment of Ductile Cast Irons |
title_full |
Boro-Austempering Treatment of Ductile Cast Irons |
title_fullStr |
Boro-Austempering Treatment of Ductile Cast Irons |
title_full_unstemmed |
Boro-Austempering Treatment of Ductile Cast Irons |
title_sort |
Boro-Austempering Treatment of Ductile Cast Irons |
author |
Mariani,Fábio Edson |
author_facet |
Mariani,Fábio Edson Soares,Carolina Lombardi Neto,Amadeu Totten,George Edward Casteletti,Luiz Carlos |
author_role |
author |
author2 |
Soares,Carolina Lombardi Neto,Amadeu Totten,George Edward Casteletti,Luiz Carlos |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Mariani,Fábio Edson Soares,Carolina Lombardi Neto,Amadeu Totten,George Edward Casteletti,Luiz Carlos |
dc.subject.por.fl_str_mv |
ductile cast iron ADI boriding boro-austempered kinects micro-adhesive wear test |
topic |
ductile cast iron ADI boriding boro-austempered kinects micro-adhesive wear test |
description |
Samples of ductile cast irons alloyed with Cu, Cu-Ni and Cu-Ni-Mo were austempered, borided and boro-austempered and characterized for hardness and micro-adhesive wear behavior. The kinetics of layer formation was also studied. The boriding method used was molten borax bath, in periods of 2 and 4 hours at temperatures of 850, 900 and 950 ºC. The direct austempering treatment was performed immediately following the boriding treatment (from 850, 900 and 950 ºC) using molten salt baths at temperatures of 240, 300 and 360 ºC for 4 hours (boro-austempering treatment). For comparative purposes, the conventional austempering treatment was also conducted. Optical microscopy, scanning electron microscopy, Brinell hardness measurements (on the substrate) and Vickers (on the layers) were performed, along with micro-adhesive wear tests. The boriding treatment resulted in the formation of high hardness layers, in the range of 1450 to 1750 HV, with high wear resistance. The wear resistance of borided and boro-austempered samples were increased by 40 times when compared to as cast or austempered samples, indicating the high efficiency of this type of treatment in increasing the wear resistance of this material. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000500204 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000500204 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1980-5373-mr-2017-0927 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
ABM, ABC, ABPol |
publisher.none.fl_str_mv |
ABM, ABC, ABPol |
dc.source.none.fl_str_mv |
Materials Research v.21 n.5 2018 reponame:Materials research (São Carlos. Online) instname:Universidade Federal de São Carlos (UFSCAR) instacron:ABM ABC ABPOL |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
ABM ABC ABPOL |
institution |
ABM ABC ABPOL |
reponame_str |
Materials research (São Carlos. Online) |
collection |
Materials research (São Carlos. Online) |
repository.name.fl_str_mv |
Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
dedz@power.ufscar.br |
_version_ |
1754212673163100160 |