Preparation of refractory calcium aluminate cement using the sonochemical process
Autor(a) principal: | |
---|---|
Data de Publicação: | 2013 |
Outros Autores: | , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Materials research (São Carlos. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392013000400006 |
Resumo: | Calcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis. |
id |
ABMABCABPOL-1_8ca64ef62d4bfd8be8b48cc85d8fe769 |
---|---|
oai_identifier_str |
oai:scielo:S1516-14392013000400006 |
network_acronym_str |
ABMABCABPOL-1 |
network_name_str |
Materials research (São Carlos. Online) |
repository_id_str |
|
spelling |
Preparation of refractory calcium aluminate cement using the sonochemical processsonochemistryheat treatmentsynthesiscalcium aluminate cementCalcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis.ABM, ABC, ABPol2013-08-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392013000400006Materials Research v.16 n.4 2013reponame:Materials research (São Carlos. Online)instname:Universidade Federal de São Carlos (UFSCAR)instacron:ABM ABC ABPOL10.1590/S1516-14392013005000041info:eu-repo/semantics/openAccessLourenço,Rafaela RobertaAngélica,Rômulo SimõesRodrigues,José de Anchietaeng2013-08-02T00:00:00Zoai:scielo:S1516-14392013000400006Revistahttp://www.scielo.br/mrPUBhttps://old.scielo.br/oai/scielo-oai.phpdedz@power.ufscar.br1980-53731516-1439opendoar:2013-08-02T00:00Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.none.fl_str_mv |
Preparation of refractory calcium aluminate cement using the sonochemical process |
title |
Preparation of refractory calcium aluminate cement using the sonochemical process |
spellingShingle |
Preparation of refractory calcium aluminate cement using the sonochemical process Lourenço,Rafaela Roberta sonochemistry heat treatment synthesis calcium aluminate cement |
title_short |
Preparation of refractory calcium aluminate cement using the sonochemical process |
title_full |
Preparation of refractory calcium aluminate cement using the sonochemical process |
title_fullStr |
Preparation of refractory calcium aluminate cement using the sonochemical process |
title_full_unstemmed |
Preparation of refractory calcium aluminate cement using the sonochemical process |
title_sort |
Preparation of refractory calcium aluminate cement using the sonochemical process |
author |
Lourenço,Rafaela Roberta |
author_facet |
Lourenço,Rafaela Roberta Angélica,Rômulo Simões Rodrigues,José de Anchieta |
author_role |
author |
author2 |
Angélica,Rômulo Simões Rodrigues,José de Anchieta |
author2_role |
author author |
dc.contributor.author.fl_str_mv |
Lourenço,Rafaela Roberta Angélica,Rômulo Simões Rodrigues,José de Anchieta |
dc.subject.por.fl_str_mv |
sonochemistry heat treatment synthesis calcium aluminate cement |
topic |
sonochemistry heat treatment synthesis calcium aluminate cement |
description |
Calcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013-08-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392013000400006 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392013000400006 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S1516-14392013005000041 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
ABM, ABC, ABPol |
publisher.none.fl_str_mv |
ABM, ABC, ABPol |
dc.source.none.fl_str_mv |
Materials Research v.16 n.4 2013 reponame:Materials research (São Carlos. Online) instname:Universidade Federal de São Carlos (UFSCAR) instacron:ABM ABC ABPOL |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
ABM ABC ABPOL |
institution |
ABM ABC ABPOL |
reponame_str |
Materials research (São Carlos. Online) |
collection |
Materials research (São Carlos. Online) |
repository.name.fl_str_mv |
Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
dedz@power.ufscar.br |
_version_ |
1754212662865035264 |