Study of the nature of non-metallic inclusions in samples of aluminum and silicon killed low carbon steels, collected in the refining treatment and continuous casting stages

• Autor(a) principal: Pires,José Carlos Santos
• Data de Publicação: 2004
• Outros Autores: Garcia,Amauri
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Materials research (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392004000400002
• topic: non-metallic inclusions; steel treatment; low carbon steel; scanning electron microscope (SEM/EDS); continuous-casting process

The amount, distribution, size and chemical composition of non-metallic inclusions have a direct influence on steel properties. By controlling size and chemical composition of these inclusions, it is possible to get a product with good quality. The identification of the nature and the control of inclusion formation are very important for steel cleanness. The behavior of these inclusions is predictable, in some extent, by the determination of the chemical composition of non-metallic phases that form such inclusions. With the objective of studying the chemical composition, the size and the distribution of such inclusions, samples of aluminum and silicon killed low carbon steels were collected in a national steel industry in the secondary refining and continuous casting stages. These samples were analyzed in the scanning electron microscope (SEM) coupled to an energy dispersive analysis system (EDS). From the results, it was possible to evaluate the nature of inclusions and to analyze the effectiveness of the refining process in the reduction of the number and area fraction of the inclusions. It was also possible to verify that the inclusions that remained after treatment, are less damage both to the steel properties as to the continuous casting process (clogging of the submerged valve).