Determination of crystallization kinetics parameters of a Li1.5Al0.5Ge1.5(PO4)3 (LAGP) glass by differential scanning calorimetry

• Autor(a) principal: Rodrigues,A. M.
• Data de Publicação: 2013
• Outros Autores: Narváez-Semanate,J. L., Cabral,A. A., Rodrigues,A. C. M.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Materials research (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392013000400016
• topic: crystallization; nucleation; DSC; Ligero's method; Kissinger's method; activation energy; Avrami coefficient

Crystallization kinetics parameters of a stoichiometric glass with the composition Li1.5Al0.5Ge1.5(PO4)3 were investigated by subjecting parallelepipedonal samples (3 × 3 × 1.5 mm) to heat treatment in a differential scanning calorimeter at different heating rates (3, 5, 8 and 10 °C/min). The data were analyzed using Ligero's and Kissinger's methods to determine the activation energy (E) of crystallization, which yielded, respectively, E = 415 ± 37 kJ/mol and 378 ± 19 kJ/mol. Ligero's method was also employed to calculate the Avrami coefficient (n), which was found to be n = 3.0. A second set of samples were heat-treated in a tubular furnace at temperatures above the glass transition temperature, Tg, to induce crystallization. The X-ray diffraction analysis of these samples indicated the presence of LiGe2(PO4)3 which displays a NASICON-type structure. An analysis by optical microscopy revealed the presence of spheric crystals located primarily in the volume, in agreement with the crystallization mechanism predicted by the Avrami coefficient.