Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Outros Autores: | |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Materials research (São Carlos. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000400201 |
Resumo: | Powder thixoforming (PTF) was a promising processing technology that can be used to fabricate high strength particle reinforced aluminum matrix composites, and a pioneer 6061 matrix alloy was fabricated utilizing PTF to investigate its solution treatment behaviors. A comparison study with traditional permanent mold cast (PMC) 6061 alloy disclosed that PTF alloy showed significantly reduced pore amount with only 0.16% (3.50% for PMC alloy). During solution treatment, PTF alloy displayed a much quicker solutionization progress than PMC alloy because of coarse eutectic phases and primary dendrites in latter alloy, its peak values of 14.5%, 241 MPa and 195 MPa in elongation, ultimate tensile strength and yield strength were achieved at 560ºC, an enhancement of 81.3%, 33.9% and 97.0%, respectively, compared with as-fabricated alloy. The dissolution of eutectic phases plays a dominative role in the growth of the primary α phases and secondarily primary α phases within 535ºC. However, the coarsening after 535ºC is subject to a mixture model involving atom diffusion along grain boundaries and through the crystal lattice. The superior tensile strengths of PTF alloy than PMC alloy resulted from decreased grain size, enhanced solid solution strengthening, reduced porosities and decreased harmful effect of insoluble phases in PTF alloy. |
id |
ABMABCABPOL-1_bae359792d10ab4bdc940f32322024d6 |
---|---|
oai_identifier_str |
oai:scielo:S1516-14392018000400201 |
network_acronym_str |
ABMABCABPOL-1 |
network_name_str |
Materials research (São Carlos. Online) |
repository_id_str |
|
spelling |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoformingsolution treatmentpowder thixoformingmicrostructuretensile propertiesPowder thixoforming (PTF) was a promising processing technology that can be used to fabricate high strength particle reinforced aluminum matrix composites, and a pioneer 6061 matrix alloy was fabricated utilizing PTF to investigate its solution treatment behaviors. A comparison study with traditional permanent mold cast (PMC) 6061 alloy disclosed that PTF alloy showed significantly reduced pore amount with only 0.16% (3.50% for PMC alloy). During solution treatment, PTF alloy displayed a much quicker solutionization progress than PMC alloy because of coarse eutectic phases and primary dendrites in latter alloy, its peak values of 14.5%, 241 MPa and 195 MPa in elongation, ultimate tensile strength and yield strength were achieved at 560ºC, an enhancement of 81.3%, 33.9% and 97.0%, respectively, compared with as-fabricated alloy. The dissolution of eutectic phases plays a dominative role in the growth of the primary α phases and secondarily primary α phases within 535ºC. However, the coarsening after 535ºC is subject to a mixture model involving atom diffusion along grain boundaries and through the crystal lattice. The superior tensile strengths of PTF alloy than PMC alloy resulted from decreased grain size, enhanced solid solution strengthening, reduced porosities and decreased harmful effect of insoluble phases in PTF alloy.ABM, ABC, ABPol2018-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000400201Materials Research v.21 n.4 2018reponame:Materials research (São Carlos. Online)instname:Universidade Federal de São Carlos (UFSCAR)instacron:ABM ABC ABPOL10.1590/1980-5373-mr-2018-0057info:eu-repo/semantics/openAccessZhang,XuezhengChen,Tijuneng2018-05-18T00:00:00Zoai:scielo:S1516-14392018000400201Revistahttp://www.scielo.br/mrPUBhttps://old.scielo.br/oai/scielo-oai.phpdedz@power.ufscar.br1980-53731516-1439opendoar:2018-05-18T00:00Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.none.fl_str_mv |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
title |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
spellingShingle |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming Zhang,Xuezheng solution treatment powder thixoforming microstructure tensile properties |
title_short |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
title_full |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
title_fullStr |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
title_full_unstemmed |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
title_sort |
Solution Treatment Behaviors of 6061 Aluminum Alloy Prepared by Powder Thixoforming |
author |
Zhang,Xuezheng |
author_facet |
Zhang,Xuezheng Chen,Tijun |
author_role |
author |
author2 |
Chen,Tijun |
author2_role |
author |
dc.contributor.author.fl_str_mv |
Zhang,Xuezheng Chen,Tijun |
dc.subject.por.fl_str_mv |
solution treatment powder thixoforming microstructure tensile properties |
topic |
solution treatment powder thixoforming microstructure tensile properties |
description |
Powder thixoforming (PTF) was a promising processing technology that can be used to fabricate high strength particle reinforced aluminum matrix composites, and a pioneer 6061 matrix alloy was fabricated utilizing PTF to investigate its solution treatment behaviors. A comparison study with traditional permanent mold cast (PMC) 6061 alloy disclosed that PTF alloy showed significantly reduced pore amount with only 0.16% (3.50% for PMC alloy). During solution treatment, PTF alloy displayed a much quicker solutionization progress than PMC alloy because of coarse eutectic phases and primary dendrites in latter alloy, its peak values of 14.5%, 241 MPa and 195 MPa in elongation, ultimate tensile strength and yield strength were achieved at 560ºC, an enhancement of 81.3%, 33.9% and 97.0%, respectively, compared with as-fabricated alloy. The dissolution of eutectic phases plays a dominative role in the growth of the primary α phases and secondarily primary α phases within 535ºC. However, the coarsening after 535ºC is subject to a mixture model involving atom diffusion along grain boundaries and through the crystal lattice. The superior tensile strengths of PTF alloy than PMC alloy resulted from decreased grain size, enhanced solid solution strengthening, reduced porosities and decreased harmful effect of insoluble phases in PTF alloy. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000400201 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392018000400201 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/1980-5373-mr-2018-0057 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
ABM, ABC, ABPol |
publisher.none.fl_str_mv |
ABM, ABC, ABPol |
dc.source.none.fl_str_mv |
Materials Research v.21 n.4 2018 reponame:Materials research (São Carlos. Online) instname:Universidade Federal de São Carlos (UFSCAR) instacron:ABM ABC ABPOL |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
ABM ABC ABPOL |
institution |
ABM ABC ABPOL |
reponame_str |
Materials research (São Carlos. Online) |
collection |
Materials research (São Carlos. Online) |
repository.name.fl_str_mv |
Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
dedz@power.ufscar.br |
_version_ |
1754212674239987712 |