Reproducibility of pop-ins in laboratory testing of welded joints
Autor(a) principal: | |
---|---|
Data de Publicação: | 2000 |
Outros Autores: | , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Materials research (São Carlos. Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392000000400008 |
Resumo: | The pop-in phenomenon, quite common in fracture mechanics tests of welded joints, corresponds to a brittle crack initiation grown from a local brittle zone (LBZ) that is arrested in reaching the higher toughness material that surrounds this LBZ. A methodology to obtain a high percentage of pop-in occurrence in laboratory testing is necessary to study the pop-in significance. Such a method is introduced in this work and includes the consumable combination and welding procedures for the SMAW welding process to generate artificial LBZ. In order to find out the influence of the loading state upon the pop-in phenomenon, laboratory CTOD tests were performed using two specimen configurations: some single edge-notched specimens were loaded on a three-point bending (SE(B)) fixture while others were tested in tensile load (SE(T)). A higher frequency of pop-in occurrence was observed in the SE(B) geometry. |
id |
ABMABCABPOL-1_c2b22bd0cadda886c3b980e82de4ea83 |
---|---|
oai_identifier_str |
oai:scielo:S1516-14392000000400008 |
network_acronym_str |
ABMABCABPOL-1 |
network_name_str |
Materials research (São Carlos. Online) |
repository_id_str |
|
spelling |
Reproducibility of pop-ins in laboratory testing of welded jointspop-inlocal brittle zonefracture toughnessThe pop-in phenomenon, quite common in fracture mechanics tests of welded joints, corresponds to a brittle crack initiation grown from a local brittle zone (LBZ) that is arrested in reaching the higher toughness material that surrounds this LBZ. A methodology to obtain a high percentage of pop-in occurrence in laboratory testing is necessary to study the pop-in significance. Such a method is introduced in this work and includes the consumable combination and welding procedures for the SMAW welding process to generate artificial LBZ. In order to find out the influence of the loading state upon the pop-in phenomenon, laboratory CTOD tests were performed using two specimen configurations: some single edge-notched specimens were loaded on a three-point bending (SE(B)) fixture while others were tested in tensile load (SE(T)). A higher frequency of pop-in occurrence was observed in the SE(B) geometry.ABM, ABC, ABPol2000-10-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392000000400008Materials Research v.3 n.4 2000reponame:Materials research (São Carlos. Online)instname:Universidade Federal de São Carlos (UFSCAR)instacron:ABM ABC ABPOL10.1590/S1516-14392000000400008info:eu-repo/semantics/openAccessBerejnoi,C.Perez Ipiña,J.E.Llorente,C.L.eng2001-04-04T00:00:00Zoai:scielo:S1516-14392000000400008Revistahttp://www.scielo.br/mrPUBhttps://old.scielo.br/oai/scielo-oai.phpdedz@power.ufscar.br1980-53731516-1439opendoar:2001-04-04T00:00Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.none.fl_str_mv |
Reproducibility of pop-ins in laboratory testing of welded joints |
title |
Reproducibility of pop-ins in laboratory testing of welded joints |
spellingShingle |
Reproducibility of pop-ins in laboratory testing of welded joints Berejnoi,C. pop-in local brittle zone fracture toughness |
title_short |
Reproducibility of pop-ins in laboratory testing of welded joints |
title_full |
Reproducibility of pop-ins in laboratory testing of welded joints |
title_fullStr |
Reproducibility of pop-ins in laboratory testing of welded joints |
title_full_unstemmed |
Reproducibility of pop-ins in laboratory testing of welded joints |
title_sort |
Reproducibility of pop-ins in laboratory testing of welded joints |
author |
Berejnoi,C. |
author_facet |
Berejnoi,C. Perez Ipiña,J.E. Llorente,C.L. |
author_role |
author |
author2 |
Perez Ipiña,J.E. Llorente,C.L. |
author2_role |
author author |
dc.contributor.author.fl_str_mv |
Berejnoi,C. Perez Ipiña,J.E. Llorente,C.L. |
dc.subject.por.fl_str_mv |
pop-in local brittle zone fracture toughness |
topic |
pop-in local brittle zone fracture toughness |
description |
The pop-in phenomenon, quite common in fracture mechanics tests of welded joints, corresponds to a brittle crack initiation grown from a local brittle zone (LBZ) that is arrested in reaching the higher toughness material that surrounds this LBZ. A methodology to obtain a high percentage of pop-in occurrence in laboratory testing is necessary to study the pop-in significance. Such a method is introduced in this work and includes the consumable combination and welding procedures for the SMAW welding process to generate artificial LBZ. In order to find out the influence of the loading state upon the pop-in phenomenon, laboratory CTOD tests were performed using two specimen configurations: some single edge-notched specimens were loaded on a three-point bending (SE(B)) fixture while others were tested in tensile load (SE(T)). A higher frequency of pop-in occurrence was observed in the SE(B) geometry. |
publishDate |
2000 |
dc.date.none.fl_str_mv |
2000-10-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392000000400008 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392000000400008 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S1516-14392000000400008 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
ABM, ABC, ABPol |
publisher.none.fl_str_mv |
ABM, ABC, ABPol |
dc.source.none.fl_str_mv |
Materials Research v.3 n.4 2000 reponame:Materials research (São Carlos. Online) instname:Universidade Federal de São Carlos (UFSCAR) instacron:ABM ABC ABPOL |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
ABM ABC ABPOL |
institution |
ABM ABC ABPOL |
reponame_str |
Materials research (São Carlos. Online) |
collection |
Materials research (São Carlos. Online) |
repository.name.fl_str_mv |
Materials research (São Carlos. Online) - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
dedz@power.ufscar.br |
_version_ |
1754212656605036544 |