Europium incorporated into titanium oxide by the sol-gel method

• Autor(a) principal: Rocha,Lucas Alonso
• Data de Publicação: 2005
• Outros Autores: Avila,Lilian Rodrigues, Caetano,Bruno Leonardo, Molina,Eduardo Ferreira, Sacco,Hérica Cristina, Ciuffi,Katia Jorge, Calefi,Paulo Sergio, Nassar,Eduardo José
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Materials research (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392005000300024
• topic: europium (III); xerogels; luminescence; TEM

In this work titanium sol was prepared from tetraethylorthotitanate (TEOT) in ethanol, stabilized with beta-diketonate 2,4 pentanedione in molar ratio 1:1 homogenized by magnetic stirring, europium ion was add as structural probe. The xerogels were heat treated at 500, 750 and 1000 °C and the characterization was realized by x-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric analysis (TGA/DSC) and photoluminescence (PL). The excitation spectra of Eu (III) ion present maximum in 394 nm correspondent to 5L6 level and emission spectra present bands characteristic transitions arising from the 5 D0 -> 7F J (J = 0, 1, 2, 3, 4) manifolds to samples treat at 500 and 750 °C. The Eu (III) emission disappear, when heated at 1000 °C, probably due to phase transition anatase to rutile and migrations of ions to the external surface that was proved by x-ray diffraction, transmission electronic microscopy and the thermogravimetric analyses of xerogels.