Sericin as compatibilizer in starch/ polyester blown films

• Autor(a) principal: Garcia,Patrícia Salomão
• Data de Publicação: 2018
• Outros Autores: Turbiani,Franciele Rezende Barbosa, Baron,Alessandra Machado, Brizola,Guilherme Luiz, Tavares,Mariane Alves, Yamashita,Fabio, Eiras,Daniel, Grossmann,Maria Victória Eiras
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Polímeros (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0104-14282018000500389
• topic: biodegradable packaging; compatibilization; extrusion; poly(butylene- adipate-co-terephthalate)

Abstract This study investigated the effects of low concentrations of sericin (≤ 1.5 wt%) in starch- poly(butylene-adipate-co-terephthalate) (PBAT) films. The films were produced by blown extrusion and mechanical, barrier and structural properties were determined. Films containing 1.0 and 1.5 wt% sericin showed higher tensile strength (6.41 and 6.59 MPa) and Young's modulus (90.88 and 132.71 MPa) compared with film without sericin (4.76 MPa and 18.64 MPa). When 0.5 wt% of sericin was used, the elongation was reduced by 62%. The addition of sericin in a concentration of 1.5% (w/w) decreased the water vapor permeability of films from 7.55 to 5.94 g (m s Pa)-1, likely due to the formation of a more homogeneous and compact matrix. Based on these results, a mechanism of action is proposed, whereby sericin acts at the interface of the polymers (starch and PBAT), reducing the interfacial tension and enhancing compatibility.