Correlation between the Mechanical Properties and Structural Characteristics of Different Fiber Posts Systems

• Autor(a) principal: Novais,Veridiana Resende
• Data de Publicação: 2016
• Outros Autores: Rodrigues,Renata Borges, Simamoto Júnior,Paulo Cezar, Lourenço,Correr-Sobrinho, Soares,Carlos José
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402016000100046
• topic: dental materials; carbon fiber; fiberglass; scanning electron microscopy.

Abstract The aim of this study was to evaluate the flexural strength and flexural modulus of different fiber-reinforcement composite (FRC) posts and determine the correlation between mechanical properties and structural characteristics. Eleven brands of fiber posts were analyzed (n=10): Exacto Cônico (Angelus), DT Light SL (VDW), RelyX Fiber Post (3M-Espe), Glassix Radiopaque (Nordim), Para Post Fiber White (Coltène), FRC Postec Plus (Ivoclar), Aestheti-Plus Post (Bisco), Superpost Cônico Estriado (Superdont), Superpost Ultrafine (Superdont), Reforpost (Angelus), and White Post DC (FGM). The posts were loaded in three-point bending test to calculate the flexural strength and flexural modulus using a mechanical testing machine (EMIC 2000 DL) at 0.5 mm/min. Data were submitted to one-way ANOVA and Scott-Knot test (p<0.05). The cross-sections of the posts were examined by scanning electron microscopy (SEM). Correlation between the mechanical properties and each of the structural variables was calculated by Pearson's correlation coefficients (p<0.05). The flexural strength values ranged from 493 to 835 MPa and were directly correlated with the fiber/matrix ratio (p=0.011). The flexural modulus ranged from 4500 to 8824 MPa and was inversely correlated with the number of fibers per mm2 of post (p<0.001). It was concluded that the structural characteristics significantly affected the properties of the FRC posts. The structural characteristic and mechanical properties of fiber glass posts are manufacture-dependent. A linear correlation between flexural strength and fiber/matrix ratio, as well as the flexural modulus and the amount of fiber was found.