In Vitro Enamel Remineralization by Low-Fluoride Toothpaste with Calcium Citrate and Sodium Trimetaphosphate

• Autor(a) principal: Hirata,Edo
• Data de Publicação: 2013
• Outros Autores: Danelon,Marcelle, Freire,Isabelle Rodrigues, Delbem,Alberto Carlos Botazzo
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402013000300253
• topic: dentifrices; fluoride; calcium; phosphate; dental caries prevention

The objective of this study was to evaluate in vitro the effect of a low fluoride toothpaste (450 µgF/g, NaF) combined with calcium citrate (Cacit) and sodium trimetaphosphate (TMP) on enamel remineralization. Bovine enamel blocks had the enamel surface polished sequentially to determine the surface hardness. After production of artificial carious lesions, the blocks selected by their surface hardness were submitted to remineralization pH cycling and daily treatment with dentifrice suspensions (diluted in deionized water or artificial saliva): placebo, 275, 450, 550 and 1,100 µgF/g and commercial dentifrice (positive control, 1,100 µgF/g). Finally, the surface and cross-section hardness was determined for calculating the change of surface hardness (%SH) and mineral content (%∆Z). Fluoride in enamel was also determined. The data from %SH, %∆Z and fluoride were subjected to two-way analysis of variance followed by Student-Newman-Keuls's test (p<0.05). The mineral gain (%SH and %∆Z) was higher for toothpastes diluted in saliva (p<0.05), except for the 450 µgF/g dentifrice with Cacit/TMP (p>0.05). The 450 Cacit/TMP toothpaste and the positive control showed similar results (p>0.05) when diluted in water. A dose-response was observed between fluoride concentration in toothpastes and fluoride present in enamel, regardless of dilution. It was concluded that it is possible to enhance the remineralization capacity of low F concentration toothpaste by of organic (Cacit) and inorganic (TMP) compounds with affinity to hydroxyapatite.