Effects of Contamination by Hemostatic Agents and Use of Cleaning Agent on Etch-and-Rinse Dentin Bond Strength

• Autor(a) principal: Pucci,César Rogério
• Data de Publicação: 2016
• Outros Autores: Araújo,Rodrigo Maximo de, Lacerda,Ana Julia Farias de, Souza,Mirella Anjos de, Huhtala,Maria Filomena Rocha Lima, Feitosa,Fernanda Alves
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402016000600688
• topic: bond strength; hemostatic agents; chlorhexidine.

Abstract The aim of this study was to evaluate the influence of contamination by hemostatic agents and rinsing with chlorhexidine on bond strength between dentin and resin composite. Ninety-six bovine teeth were sectioned to expose a flat dentin surface area. A standardized cavity with 2.0 mm in thickness, superficial diameter of 4.0 mm and bottom diameter of 3.0 mm was prepared with a diamond bur in each dentin specimen. The teeth were divided into four groups according to the hemostatic employed: G1: control; G2: use of ViscoStat, Ultradent; G3: Hemosthasegel, FGM; and G4: Hemostop, Dentsply. The groups were divided into two subgroups according to the cleaning protocol method (n=12): A: without any further cleaning; and B: cleaning with chlorhexidine at 0.2%. All cavities were filled using a dentin adhesive and a resin composite, following the manufacturer's instructions. After 24 h, the specimens were aged by thermal and mechanical cycling. The bond strength was determined by the push out bond test (MPa), Statistical analysis was performed using two-way ANOVA and Tukey test (p<0.05). Statistically significant differences were detected among all groups treated with hemostatic agents and the control group. The post-hoc test showed that cleaning the cavity with chlorhexidine significantly improves the bond strength between dentin and resin composite. Our results suggested that the use of chlorhexidine can reestablish the bond strength between dentin and resin composite when a hemostatic agent was applied.