Characterization of calcium oxide in root perforation sealer materials

• Autor(a) principal: Estrela,Carlos
• Data de Publicação: 2012
• Outros Autores: Sousa-Neto,Manoel Damião, Guedes,Orlando Aguirre, Alencar,Ana Helena Gonçalves, Duarte,Marco Antonio Hungaro, Pécora,Jesus Djalma
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402012000500012
• topic: MTA; Portland cement; calcium oxide; calcium hydroxide; root perforations

Root perforation represents an undesirable complication that may lead to an unfavorable prognosis. The aims of this study were to characterize and to compare the presence of calcium oxide (CaO) on the chemical composition of materials used for root perforation therapy: gray and white mineral trioxide aggregate (MTA) and Portland cement (PC), gray MTA+5%CaO and gray MTA+10%CaO. The last two materials were analyzed to evaluate the increase of CaO in the final sample. CaO alone was used as a standard. Eighteen polyethylene tubes with an internal diameter of 3 mm and 3 mm in length were prepared, filled and then transferred to a chamber with 95% relative humidity and a temperature of 37ºC. The chemical compounds (particularly CaO) and the main components were analyzed by energy-dispersive X-ray microanalysis (EDX). EDX revealed the following concentrations of CaO: gray MTA: 59.28%, white MTA: 63.09%; PC: 72.51%; gray MTA+5%CaO: 63.48% and gray MTA+10%CaO: 67.55%. The tested materials presented different concentrations of CaO. Even with an increase of 5 and 10% CaO in gray MTA, the CaO levels found in the MTA samples were lower than those found in PC.