Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel
Autor(a) principal: | |
---|---|
Data de Publicação: | 2013 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Dental Journal |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402013000400330 |
Resumo: | This study evaluated in vitro the influence of thermocycling and water storage (WS) on the shear bond strength (SBS) of composite resin in cavities prepared in primary tooth enamel with conventional bur or Er:YAG laser. The test surfaces were obtained from 48 primary molars and randomly assigned to 2 groups (n=24), according to cavity preparation: A: bur-preparation and B: Er:YAG laser irradiation. The specimens were restored with an etch-and-rinse adhesive system and composite resin. Each group was divided into 4 subgroups (n=6) according to WS duration and number of thermal cycles (TCs): I: 24 h WS/no thermocycling; II: 7 days WS/500 TCs; III: 1 month WS/2,000 TCs; IV: 6 months WS/12,000 TCs. The specimens were tested to failure in shear strength at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by two-way ANOVA and Tukey's test. SBS means (S.D.) in MPa were: AI: 17.45 (2.03), AII:16.38 (1.49), AIII: 6.88 (0.66), AIV: 7.77 (1.53), BI: 12.32 (0.99), BII: 15.37 (2.24), BIII: 15.05 (2.01) and BIV-5.51 (1.01). WS duration and number of TCs influenced significantly the SBS values only for BIV (p<0.05). AI presented the highest SBS value, which was statistically similar to those of AII, BII and BIII. In conclusion, the adhesion of an etch-and-rinse adhesive to Er:YAG laser-irradiated primary tooth enamel was affected by the methods used to simulate degradation of the adhesive interface only when 6 months WS/12,000 TCs were employed. |
id |
FUNORP-1_c33b7b1b8c09df8e8caf54a330f5340c |
---|---|
oai_identifier_str |
oai:scielo:S0103-64402013000400330 |
network_acronym_str |
FUNORP-1 |
network_name_str |
Brazilian Dental Journal |
repository_id_str |
|
spelling |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth EnamelEr:YAG laserthermocyclingwater storageshear bond strengthprimary teethThis study evaluated in vitro the influence of thermocycling and water storage (WS) on the shear bond strength (SBS) of composite resin in cavities prepared in primary tooth enamel with conventional bur or Er:YAG laser. The test surfaces were obtained from 48 primary molars and randomly assigned to 2 groups (n=24), according to cavity preparation: A: bur-preparation and B: Er:YAG laser irradiation. The specimens were restored with an etch-and-rinse adhesive system and composite resin. Each group was divided into 4 subgroups (n=6) according to WS duration and number of thermal cycles (TCs): I: 24 h WS/no thermocycling; II: 7 days WS/500 TCs; III: 1 month WS/2,000 TCs; IV: 6 months WS/12,000 TCs. The specimens were tested to failure in shear strength at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by two-way ANOVA and Tukey's test. SBS means (S.D.) in MPa were: AI: 17.45 (2.03), AII:16.38 (1.49), AIII: 6.88 (0.66), AIV: 7.77 (1.53), BI: 12.32 (0.99), BII: 15.37 (2.24), BIII: 15.05 (2.01) and BIV-5.51 (1.01). WS duration and number of TCs influenced significantly the SBS values only for BIV (p<0.05). AI presented the highest SBS value, which was statistically similar to those of AII, BII and BIII. In conclusion, the adhesion of an etch-and-rinse adhesive to Er:YAG laser-irradiated primary tooth enamel was affected by the methods used to simulate degradation of the adhesive interface only when 6 months WS/12,000 TCs were employed.Fundação Odontológica de Ribeirão Preto2013-08-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402013000400330Brazilian Dental Journal v.24 n.4 2013reponame:Brazilian Dental Journalinstname:Fundação Odontológica de Ribeirão Preto (FUNORP)instacron:FUNORP10.1590/0103-6440201302217info:eu-repo/semantics/openAccessBorsatto,Maria CristinaMartinelli,Mayara GarciaContente,Marta Maria Martins GiamateiMellara,Talitha de SiqueiraPecora,Jesus DjalmaGalo,Rodrigoeng2013-10-16T00:00:00Zoai:scielo:S0103-64402013000400330Revistahttps://www.scielo.br/j/bdj/https://old.scielo.br/oai/scielo-oai.phpbdj@forp.usp.br||sergio@fosjc.unesp.br1806-47600103-6440opendoar:2013-10-16T00:00Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP)false |
dc.title.none.fl_str_mv |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
title |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
spellingShingle |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel Borsatto,Maria Cristina Er:YAG laser thermocycling water storage shear bond strength primary teeth |
title_short |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
title_full |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
title_fullStr |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
title_full_unstemmed |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
title_sort |
Bond Durability of Er:YAG Laser-Prepared Primary Tooth Enamel |
author |
Borsatto,Maria Cristina |
author_facet |
Borsatto,Maria Cristina Martinelli,Mayara Garcia Contente,Marta Maria Martins Giamatei Mellara,Talitha de Siqueira Pecora,Jesus Djalma Galo,Rodrigo |
author_role |
author |
author2 |
Martinelli,Mayara Garcia Contente,Marta Maria Martins Giamatei Mellara,Talitha de Siqueira Pecora,Jesus Djalma Galo,Rodrigo |
author2_role |
author author author author author |
dc.contributor.author.fl_str_mv |
Borsatto,Maria Cristina Martinelli,Mayara Garcia Contente,Marta Maria Martins Giamatei Mellara,Talitha de Siqueira Pecora,Jesus Djalma Galo,Rodrigo |
dc.subject.por.fl_str_mv |
Er:YAG laser thermocycling water storage shear bond strength primary teeth |
topic |
Er:YAG laser thermocycling water storage shear bond strength primary teeth |
description |
This study evaluated in vitro the influence of thermocycling and water storage (WS) on the shear bond strength (SBS) of composite resin in cavities prepared in primary tooth enamel with conventional bur or Er:YAG laser. The test surfaces were obtained from 48 primary molars and randomly assigned to 2 groups (n=24), according to cavity preparation: A: bur-preparation and B: Er:YAG laser irradiation. The specimens were restored with an etch-and-rinse adhesive system and composite resin. Each group was divided into 4 subgroups (n=6) according to WS duration and number of thermal cycles (TCs): I: 24 h WS/no thermocycling; II: 7 days WS/500 TCs; III: 1 month WS/2,000 TCs; IV: 6 months WS/12,000 TCs. The specimens were tested to failure in shear strength at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by two-way ANOVA and Tukey's test. SBS means (S.D.) in MPa were: AI: 17.45 (2.03), AII:16.38 (1.49), AIII: 6.88 (0.66), AIV: 7.77 (1.53), BI: 12.32 (0.99), BII: 15.37 (2.24), BIII: 15.05 (2.01) and BIV-5.51 (1.01). WS duration and number of TCs influenced significantly the SBS values only for BIV (p<0.05). AI presented the highest SBS value, which was statistically similar to those of AII, BII and BIII. In conclusion, the adhesion of an etch-and-rinse adhesive to Er:YAG laser-irradiated primary tooth enamel was affected by the methods used to simulate degradation of the adhesive interface only when 6 months WS/12,000 TCs were employed. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013-08-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402013000400330 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402013000400330 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/0103-6440201302217 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
dc.source.none.fl_str_mv |
Brazilian Dental Journal v.24 n.4 2013 reponame:Brazilian Dental Journal instname:Fundação Odontológica de Ribeirão Preto (FUNORP) instacron:FUNORP |
instname_str |
Fundação Odontológica de Ribeirão Preto (FUNORP) |
instacron_str |
FUNORP |
institution |
FUNORP |
reponame_str |
Brazilian Dental Journal |
collection |
Brazilian Dental Journal |
repository.name.fl_str_mv |
Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP) |
repository.mail.fl_str_mv |
bdj@forp.usp.br||sergio@fosjc.unesp.br |
_version_ |
1754204092669886464 |