Stiffness plasticity degradation of masonry mortar under compression: preliminar results
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Revista IBRACON de Estruturas e Materiais |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1983-41952018000200279 |
Resumo: | Abstract The main goal of this research is to determine the mechanical properties of bedding mortar by assessing the mortar damage onset, the stiffness plasticity degradation and the apparent Poisson´s ratio under compression. Two mortar types, 1:0.5:4 and 1:1:6 (cement:lime:sand ratio), were used and tested at 28 days; specimens had diameter-to-height (d/h) ratios of 0.3 and 1.0. These diameter-to-height (d/h) ratios were chosen to evaluate the effect of confinement caused by the friction between the steel plates of the testing machine and the sample. Numerical models were developed, and their response compared with the experimental results. From the experimental results, it was concluded that there are meaningful differences in their responses with weak and strong mortar types and different d/h ratios. The d/h ratio influences the relationship between the stress and strength and the apparent Poisson´s ratio of the specimen, which is defined herein as the ratio of the horizontal to vertical strain, regardless of cracking of the specimen. The mortar damage onset and stiffness plasticity degradation for both mortar types and d/h ratio are different and depend on the stress/strength ratio level. All samples with a d/h ratio of 0.3 show a constant decrease in the volumetric strain until failure but with negligible expansion on the horizontal deformation. In contrast, samples with a d/h ratio of 1.0 present an increase of stiffness after development of the first crack, which causes the increase of the sample volume. Numerical simulation and experimental results for mortar 1:0.5:4 with a d/h ratio of 0.3 are similar until approximately 10 MPa, after which the numerical results diverge from the experimental results. For the d/h ratio of 1.0, the vertical strain results are also similar, but the horizontal strains results near failure are very different. The model can not represent the nonlinear increase of the horizontal strain near failure probably because the crack propagation and the stiffness plasticity degradation could not be controlled. For mortar 1:1:6, vertical strains from numerical and experimental results are similar, but again the model can not reproduce the nonlinear increase of horizontal strain near failure. |
id |
IBRACON-1_9b381aa0ff253e39cf609bf2718999b1 |
---|---|
oai_identifier_str |
oai:scielo:S1983-41952018000200279 |
network_acronym_str |
IBRACON-1 |
network_name_str |
Revista IBRACON de Estruturas e Materiais |
repository_id_str |
|
spelling |
Stiffness plasticity degradation of masonry mortar under compression: preliminar resultsbedding mortardamage onsetvertical strainhorizontal strainstrain differenceconfinement effectAbstract The main goal of this research is to determine the mechanical properties of bedding mortar by assessing the mortar damage onset, the stiffness plasticity degradation and the apparent Poisson´s ratio under compression. Two mortar types, 1:0.5:4 and 1:1:6 (cement:lime:sand ratio), were used and tested at 28 days; specimens had diameter-to-height (d/h) ratios of 0.3 and 1.0. These diameter-to-height (d/h) ratios were chosen to evaluate the effect of confinement caused by the friction between the steel plates of the testing machine and the sample. Numerical models were developed, and their response compared with the experimental results. From the experimental results, it was concluded that there are meaningful differences in their responses with weak and strong mortar types and different d/h ratios. The d/h ratio influences the relationship between the stress and strength and the apparent Poisson´s ratio of the specimen, which is defined herein as the ratio of the horizontal to vertical strain, regardless of cracking of the specimen. The mortar damage onset and stiffness plasticity degradation for both mortar types and d/h ratio are different and depend on the stress/strength ratio level. All samples with a d/h ratio of 0.3 show a constant decrease in the volumetric strain until failure but with negligible expansion on the horizontal deformation. In contrast, samples with a d/h ratio of 1.0 present an increase of stiffness after development of the first crack, which causes the increase of the sample volume. Numerical simulation and experimental results for mortar 1:0.5:4 with a d/h ratio of 0.3 are similar until approximately 10 MPa, after which the numerical results diverge from the experimental results. For the d/h ratio of 1.0, the vertical strain results are also similar, but the horizontal strains results near failure are very different. The model can not represent the nonlinear increase of the horizontal strain near failure probably because the crack propagation and the stiffness plasticity degradation could not be controlled. For mortar 1:1:6, vertical strains from numerical and experimental results are similar, but again the model can not reproduce the nonlinear increase of horizontal strain near failure.IBRACON - Instituto Brasileiro do Concreto2018-04-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1983-41952018000200279Revista IBRACON de Estruturas e Materiais v.11 n.2 2018reponame:Revista IBRACON de Estruturas e Materiaisinstname:Instituto Brasileiro do Concreto (IBRACON)instacron:IBRACON10.1590/s1983-4195201800020004info:eu-repo/semantics/openAccessMOHAMAD,G.FONSECA,F. S.VERMELTFOORT,A. T.LUBECK,A.eng2018-05-24T00:00:00Zoai:scielo:S1983-41952018000200279Revistahttp://www.revistas.ibracon.org.br/index.php/riemhttps://old.scielo.br/oai/scielo-oai.phpeditores.riem@gmail.com||arlene@ibracon.org.br1983-41951983-4195opendoar:2018-05-24T00:00Revista IBRACON de Estruturas e Materiais - Instituto Brasileiro do Concreto (IBRACON)false |
dc.title.none.fl_str_mv |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
title |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
spellingShingle |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results MOHAMAD,G. bedding mortar damage onset vertical strain horizontal strain strain difference confinement effect |
title_short |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
title_full |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
title_fullStr |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
title_full_unstemmed |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
title_sort |
Stiffness plasticity degradation of masonry mortar under compression: preliminar results |
author |
MOHAMAD,G. |
author_facet |
MOHAMAD,G. FONSECA,F. S. VERMELTFOORT,A. T. LUBECK,A. |
author_role |
author |
author2 |
FONSECA,F. S. VERMELTFOORT,A. T. LUBECK,A. |
author2_role |
author author author |
dc.contributor.author.fl_str_mv |
MOHAMAD,G. FONSECA,F. S. VERMELTFOORT,A. T. LUBECK,A. |
dc.subject.por.fl_str_mv |
bedding mortar damage onset vertical strain horizontal strain strain difference confinement effect |
topic |
bedding mortar damage onset vertical strain horizontal strain strain difference confinement effect |
description |
Abstract The main goal of this research is to determine the mechanical properties of bedding mortar by assessing the mortar damage onset, the stiffness plasticity degradation and the apparent Poisson´s ratio under compression. Two mortar types, 1:0.5:4 and 1:1:6 (cement:lime:sand ratio), were used and tested at 28 days; specimens had diameter-to-height (d/h) ratios of 0.3 and 1.0. These diameter-to-height (d/h) ratios were chosen to evaluate the effect of confinement caused by the friction between the steel plates of the testing machine and the sample. Numerical models were developed, and their response compared with the experimental results. From the experimental results, it was concluded that there are meaningful differences in their responses with weak and strong mortar types and different d/h ratios. The d/h ratio influences the relationship between the stress and strength and the apparent Poisson´s ratio of the specimen, which is defined herein as the ratio of the horizontal to vertical strain, regardless of cracking of the specimen. The mortar damage onset and stiffness plasticity degradation for both mortar types and d/h ratio are different and depend on the stress/strength ratio level. All samples with a d/h ratio of 0.3 show a constant decrease in the volumetric strain until failure but with negligible expansion on the horizontal deformation. In contrast, samples with a d/h ratio of 1.0 present an increase of stiffness after development of the first crack, which causes the increase of the sample volume. Numerical simulation and experimental results for mortar 1:0.5:4 with a d/h ratio of 0.3 are similar until approximately 10 MPa, after which the numerical results diverge from the experimental results. For the d/h ratio of 1.0, the vertical strain results are also similar, but the horizontal strains results near failure are very different. The model can not represent the nonlinear increase of the horizontal strain near failure probably because the crack propagation and the stiffness plasticity degradation could not be controlled. For mortar 1:1:6, vertical strains from numerical and experimental results are similar, but again the model can not reproduce the nonlinear increase of horizontal strain near failure. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-04-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1983-41952018000200279 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1983-41952018000200279 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/s1983-4195201800020004 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
IBRACON - Instituto Brasileiro do Concreto |
publisher.none.fl_str_mv |
IBRACON - Instituto Brasileiro do Concreto |
dc.source.none.fl_str_mv |
Revista IBRACON de Estruturas e Materiais v.11 n.2 2018 reponame:Revista IBRACON de Estruturas e Materiais instname:Instituto Brasileiro do Concreto (IBRACON) instacron:IBRACON |
instname_str |
Instituto Brasileiro do Concreto (IBRACON) |
instacron_str |
IBRACON |
institution |
IBRACON |
reponame_str |
Revista IBRACON de Estruturas e Materiais |
collection |
Revista IBRACON de Estruturas e Materiais |
repository.name.fl_str_mv |
Revista IBRACON de Estruturas e Materiais - Instituto Brasileiro do Concreto (IBRACON) |
repository.mail.fl_str_mv |
editores.riem@gmail.com||arlene@ibracon.org.br |
_version_ |
1754193605274107904 |