Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/8119 |
Resumo: | Aims: to evaluate in vitro the fracture strength and failure pattern of endocrown restorations performed with Incoris TZI ceramics, Celta Duo and Empress CAD cemented on endodontically treated molars. Materials and methods: forty extracted sound molars were randomly distributed into 4 groups (n = 10). After being endodontically treated, they were restored with endocrowns carried out through the CEREC system with three different materials: Empress CAD (Ivoclar Vivadent), Celta Duo (Dentsply/Sirona) or Incoris TZI (Dentsply/Sirona). After, they were subjected to mechanical fatigue testing with vertical load application of 200N, totalling 500,000 cycles. Subsequently, the samples were submitted to the maximum fracture load under compressive force on the long axis of the tooth at cross-head speed of 1mm/min.. After the fracture strength testing the fracture patterns were evaluated being classified as repairable (cusps) or irreparable (pulp chamber floor rupture). Results: Sound: 4306Na ± 716.5; Incoris TZI: 3770NAb ± 846; Empress CAD: 1994Nc ± 498.5; Celta Duo: 3298Nb ± 1121. The Incoris TZI and Celta Duo presented the same proportion of irreparable fractures, 60%. The Empress Cad presented the same proportion for the repairable and irreparable fractures (50%). Conclusion: The Incoris TZI presented higher fracture strength, followed by Celta Duo, but did not differ statistically. In turn, the Empress CAD differed statistically from the others presenting lower fracture strength. The Incoris TZI and Celta Duo presented the same prognosis of failures with predominance of irreparable failures. |
id |
P_RS_14cdc9b8d46b78a13a72ed01ca8f97ea |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/8119 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Burnett Junior, Luiz Henriquehttp://lattes.cnpq.br/1252685026530007http://lattes.cnpq.br/4848668487808634Oliveira, Pâmella Tomazi Godoy de2018-06-11T16:31:30Z2018-01-25http://tede2.pucrs.br/tede2/handle/tede/8119Aims: to evaluate in vitro the fracture strength and failure pattern of endocrown restorations performed with Incoris TZI ceramics, Celta Duo and Empress CAD cemented on endodontically treated molars. Materials and methods: forty extracted sound molars were randomly distributed into 4 groups (n = 10). After being endodontically treated, they were restored with endocrowns carried out through the CEREC system with three different materials: Empress CAD (Ivoclar Vivadent), Celta Duo (Dentsply/Sirona) or Incoris TZI (Dentsply/Sirona). After, they were subjected to mechanical fatigue testing with vertical load application of 200N, totalling 500,000 cycles. Subsequently, the samples were submitted to the maximum fracture load under compressive force on the long axis of the tooth at cross-head speed of 1mm/min.. After the fracture strength testing the fracture patterns were evaluated being classified as repairable (cusps) or irreparable (pulp chamber floor rupture). Results: Sound: 4306Na ± 716.5; Incoris TZI: 3770NAb ± 846; Empress CAD: 1994Nc ± 498.5; Celta Duo: 3298Nb ± 1121. The Incoris TZI and Celta Duo presented the same proportion of irreparable fractures, 60%. The Empress Cad presented the same proportion for the repairable and irreparable fractures (50%). Conclusion: The Incoris TZI presented higher fracture strength, followed by Celta Duo, but did not differ statistically. In turn, the Empress CAD differed statistically from the others presenting lower fracture strength. The Incoris TZI and Celta Duo presented the same prognosis of failures with predominance of irreparable failures.Objetivos: avaliar in vitro a resistência à fratura e o padrão de falha de restaurações endocrown realizadas com as cerâmicas inCoris TZI, Celtra Duo e Empress CAD cimentadas sobre molares tratados endodonticamente. Materiais e métodos: quarenta dentes molares hígidos extraídos foram distribuídos aleatoriamente em 4 grupos (n=10). Após serem endodonticamente tratados, foram restaurados com endocrowns realizadas através do sistema CEREC/InLab (Sirona) com três diferentes materiais: Empress CAD (Ivoclar Vivadent), Celtra Duo (Dentsply/Sirona) ou inCoris TZI (Dentsply/Sirona). Após, foram submetidos à fadiga mecânica com aplicação de carga vertical de 200N, totalizando 500.000 ciclos. Posteriormente, foi testada a carga máxima de fratura com força compressiva no longo eixo do dente sob velocidade de 1mm/min.. Após o ensaio foram avaliados os padrões de fratura e classificados em reparáveis (cúspides) ou irreparáveis (assoalho da câmara pulpar). Resultados: Hígidos: 4306Na ± 716,5; inCoris TZI: 3770Nab ± 846; Empress CAD:1994Nc ± 498,5; Celtra Duo: 3298Nb ± 1121. O grupo inCoris TZI e Celtra Duo apresentaram a mesma proporção de fraturas irreparáveis, 60%. O grupo Empress Cad apresentou a mesma proporção para as fraturas reparáveis e irreparáveis (50%). Conclusão: O grupo inCoris TZI apresentou maior resistência à fratura, seguido do grupo Celtra Duo, mas não diferiram estatisticamente. Por sua vez, a cerâmica Empress CAD diferiu estatisticamente das demais apresentando menor valor de resistência à fratura. O grupo Incoris TZI e Celtra Duo apresentaram o mesmo prognóstico de falhas com predominância de falhas irreparáveis.Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2018-03-15T15:35:44Z No. of bitstreams: 1 PÂMELLA_TOMAZI_GODOY_DE_OLIVEIRA_DIS.pdf: 1304084 bytes, checksum: caf3b44234731105c91e07d645c0f956 (MD5)Rejected by Tatiana Lopes (tatiana.lopes@pucrs.br), reason: Devolvido porque o sumário do pdf está desconfigurado. on 2018-03-28T11:41:16Z (GMT)Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2018-05-25T13:25:14Z No. of bitstreams: 1 PÂMELLA_TOMAZI_GODOY_DE_OLIVEIRA_DIS.pdf: 1304084 bytes, checksum: caf3b44234731105c91e07d645c0f956 (MD5)Approved for entry into archive by Caroline Xavier (caroline.xavier@pucrs.br) on 2018-06-11T16:26:07Z (GMT) No. of bitstreams: 1 PÂMELLA_TOMAZI_GODOY_DE_OLIVEIRA_DIS.pdf: 1304084 bytes, checksum: caf3b44234731105c91e07d645c0f956 (MD5)Made available in DSpace on 2018-06-11T16:31:30Z (GMT). No. of bitstreams: 1 PÂMELLA_TOMAZI_GODOY_DE_OLIVEIRA_DIS.pdf: 1304084 bytes, checksum: caf3b44234731105c91e07d645c0f956 (MD5) Previous issue date: 2018-01-25Conselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPqapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/172424/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.jpghttps://tede2.pucrs.br/tede2/retrieve/187897/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilEscola de Ciências da SaúdeEndocrownResistência à FraturaCAD-CAMCerâmicaCIENCIAS DA SAUDE::ODONTOLOGIARestaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falhainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho será publicado como artigo ou livro60 meses11/06/2023-8096554818733665164500500600-2070498469879244349-2555911436985713659info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSORIGINALDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdfDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdfapplication/pdf939215https://tede2.pucrs.br/tede2/bitstream/tede/8119/7/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf1548ac847675714cc38a602579f03352MD57THUMBNAILDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.jpgDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.jpgimage/jpeg4085https://tede2.pucrs.br/tede2/bitstream/tede/8119/6/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.jpg7c7b7f1061e9501aea4ccb40ea9c0394MD56DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.jpgDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.jpgimage/jpeg5492https://tede2.pucrs.br/tede2/bitstream/tede/8119/9/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.jpg6ec07e655bb0ffd9c68ca95a049a3cdbMD59TEXTDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.txtDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.txttext/plain1554https://tede2.pucrs.br/tede2/bitstream/tede/8119/5/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.txtb475e63fb8cf38ad7b5bd03b4c072730MD55DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.txtDIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.txttext/plain75536https://tede2.pucrs.br/tede2/bitstream/tede/8119/8/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.txta693c5ac05e6837091e05893c0d62b42MD58LICENSElicense.txtlicense.txttext/plain; charset=utf-8610https://tede2.pucrs.br/tede2/bitstream/tede/8119/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53tede/81192023-06-14 20:00:07.801oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2023-06-14T23:00:07Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
title |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
spellingShingle |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha Oliveira, Pâmella Tomazi Godoy de Endocrown Resistência à Fratura CAD-CAM Cerâmica CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
title_full |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
title_fullStr |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
title_full_unstemmed |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
title_sort |
Restaurações endocrown produzidas em CAD/CAM : ensaio de carga máxima de fratura e análise do padrão de falha |
author |
Oliveira, Pâmella Tomazi Godoy de |
author_facet |
Oliveira, Pâmella Tomazi Godoy de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Burnett Junior, Luiz Henrique |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/1252685026530007 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/4848668487808634 |
dc.contributor.author.fl_str_mv |
Oliveira, Pâmella Tomazi Godoy de |
contributor_str_mv |
Burnett Junior, Luiz Henrique |
dc.subject.por.fl_str_mv |
Endocrown Resistência à Fratura CAD-CAM Cerâmica |
topic |
Endocrown Resistência à Fratura CAD-CAM Cerâmica CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Aims: to evaluate in vitro the fracture strength and failure pattern of endocrown restorations performed with Incoris TZI ceramics, Celta Duo and Empress CAD cemented on endodontically treated molars. Materials and methods: forty extracted sound molars were randomly distributed into 4 groups (n = 10). After being endodontically treated, they were restored with endocrowns carried out through the CEREC system with three different materials: Empress CAD (Ivoclar Vivadent), Celta Duo (Dentsply/Sirona) or Incoris TZI (Dentsply/Sirona). After, they were subjected to mechanical fatigue testing with vertical load application of 200N, totalling 500,000 cycles. Subsequently, the samples were submitted to the maximum fracture load under compressive force on the long axis of the tooth at cross-head speed of 1mm/min.. After the fracture strength testing the fracture patterns were evaluated being classified as repairable (cusps) or irreparable (pulp chamber floor rupture). Results: Sound: 4306Na ± 716.5; Incoris TZI: 3770NAb ± 846; Empress CAD: 1994Nc ± 498.5; Celta Duo: 3298Nb ± 1121. The Incoris TZI and Celta Duo presented the same proportion of irreparable fractures, 60%. The Empress Cad presented the same proportion for the repairable and irreparable fractures (50%). Conclusion: The Incoris TZI presented higher fracture strength, followed by Celta Duo, but did not differ statistically. In turn, the Empress CAD differed statistically from the others presenting lower fracture strength. The Incoris TZI and Celta Duo presented the same prognosis of failures with predominance of irreparable failures. |
publishDate |
2018 |
dc.date.accessioned.fl_str_mv |
2018-06-11T16:31:30Z |
dc.date.issued.fl_str_mv |
2018-01-25 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/8119 |
url |
http://tede2.pucrs.br/tede2/handle/tede/8119 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
-2555911436985713659 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola de Ciências da Saúde |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
https://tede2.pucrs.br/tede2/bitstream/tede/8119/7/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf https://tede2.pucrs.br/tede2/bitstream/tede/8119/6/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.jpg https://tede2.pucrs.br/tede2/bitstream/tede/8119/9/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.jpg https://tede2.pucrs.br/tede2/bitstream/tede/8119/5/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_CONFIDENCIAL.pdf.txt https://tede2.pucrs.br/tede2/bitstream/tede/8119/8/DIS_PAMELLA_TOMAZI_GODOY_DE_OLIVEIRA_COMPLETO.pdf.txt https://tede2.pucrs.br/tede2/bitstream/tede/8119/3/license.txt |
bitstream.checksum.fl_str_mv |
1548ac847675714cc38a602579f03352 7c7b7f1061e9501aea4ccb40ea9c0394 6ec07e655bb0ffd9c68ca95a049a3cdb b475e63fb8cf38ad7b5bd03b4c072730 a693c5ac05e6837091e05893c0d62b42 5a9d6006225b368ef605ba16b4f6d1be |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765331522093056 |