Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2
Autor(a) principal: | |
---|---|
Data de Publicação: | 2021 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/10067 |
Resumo: | Class G Portland cement is the conventional material used for well construction, recovery, and abandonment operations. However, there are several studies indicating that this material is quite susceptible to acid environments degradation, as the ones observed in oil wells and CO2 injection wells, which can generate failures and leakages. Therefore, searches for alternative materials to cement has vital importance for the oil and gas industry to guarantee the integrity of wells, especially for well recovery and abandonment operations. In this context, the present work evaluates chemical and mechanical resistance of different commercial epoxy resin blends in conditions found in oil wells/CO2 geological storage reservoirs. The epoxy resin blends were formulated in different proportions and were exposed to degradation tests at 65 °C and 150 bar for 7 days in an aqueous medium saturated with CO2. Physicalchemical and mechanical characterization of the polymeric materials were performed through swelling test, X-ray microtomography (Micro-CT), compression test, scanning electron microscopy (MEV-FEG), atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR), thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC). Results indicated that the epoxy resin samples showed mechanical properties losses after the CO2 degradation test, due to macro-structural changes. There is no indication of chemical interaction between the epoxy resin blends and CO2. Despite the reduction of mechanical properties, resins can be a good option to repair and abandonment operations. From mathematical models, ideal blends for different well applications were identified. |
id |
P_RS_49ab2d0562733acca8668459249e3bbe |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/10067 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Dalla Vecchia, Felipehttp://lattes.cnpq.br/4065200380277145http://lattes.cnpq.br/8483911283548170Stepanha, Amanda Sofia de Guimarães e2022-01-31T20:01:19Z2021-08-26http://tede2.pucrs.br/tede2/handle/tede/10067Class G Portland cement is the conventional material used for well construction, recovery, and abandonment operations. However, there are several studies indicating that this material is quite susceptible to acid environments degradation, as the ones observed in oil wells and CO2 injection wells, which can generate failures and leakages. Therefore, searches for alternative materials to cement has vital importance for the oil and gas industry to guarantee the integrity of wells, especially for well recovery and abandonment operations. In this context, the present work evaluates chemical and mechanical resistance of different commercial epoxy resin blends in conditions found in oil wells/CO2 geological storage reservoirs. The epoxy resin blends were formulated in different proportions and were exposed to degradation tests at 65 °C and 150 bar for 7 days in an aqueous medium saturated with CO2. Physicalchemical and mechanical characterization of the polymeric materials were performed through swelling test, X-ray microtomography (Micro-CT), compression test, scanning electron microscopy (MEV-FEG), atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR), thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC). Results indicated that the epoxy resin samples showed mechanical properties losses after the CO2 degradation test, due to macro-structural changes. There is no indication of chemical interaction between the epoxy resin blends and CO2. Despite the reduction of mechanical properties, resins can be a good option to repair and abandonment operations. From mathematical models, ideal blends for different well applications were identified.O material convencionalmente utilizado para construção e/ou operações de reparo e abandono de poços é o cimento Portland classe G. No entanto, diversas pesquisas apontam que este material é bastante suscetível à degradação por meios ácidos encontrados em poços de petróleo e poços injetores de CO2, podendo gerar falhas e vazamentos. Portanto, a busca por materiais alternativos ao cimento é de fundamental importância para a indústria de óleo e gás para garantir a integridade dos poços. Neste contexto, no presente trabalho são avaliadas as resistências química e mecânica de diferentes blendas de resinas epóxi frente as condições encontradas em poços de petróleo/reservatórios de armazenamento geológico de CO2. Os materiais poliméricos, formulados a partir de blendas de resinas epóxi comerciais em diferentes proporções, foram submetidos a ensaios de degradação na temperatura de 65 °C e pressão de 150 bar por 7 dias em meio aquoso saturado com CO2. A caracterização físico-química e mecânica dos materiais poliméricos foi realizada por teste de inchamento (swelling test), microtomografia de raios-X (Micro-CT), ensaio de compressão, microscopia eletrônica de varredura (MEV-FEG), microscopia de força atômica (AFM), espectroscopia de infravermelho por transformada de Fourier (FTIR), análise termogravimétrica (TGA) e calorimetria exploratória diferencial (DSC). Os resultados obtidos indicaram que as amostra de resina epóxi sofreram uma redução nas suas propriedades mecânicas após o ensaio de degradação por CO2, devido a alterações macroestruturais. Não há indicações de que ocorre a interação química entre as blendas de resina epóxi e o CO2. Apesar da redução de propriedades mecânicas, as resinas apresentaram um bom desempenho para a aplicação em operações de reparo e abandono de poços. A partir de modelos matemáticos, foram identificadas as blendas ideais para diferentes aplicações em poços.Submitted by PPG Engenharia e Tecnologia de Materiais (engenharia.pg.materiais@pucrs.br) on 2022-01-31T17:39:33Z No. of bitstreams: 1 Dissertação Amanda Sofia de Guimarães e Stepanha (003).pdf: 5023165 bytes, checksum: 4fb7ab8888cd9a6feb5ed666a5000b94 (MD5)Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2022-01-31T19:51:56Z (GMT) No. of bitstreams: 1 Dissertação Amanda Sofia de Guimarães e Stepanha (003).pdf: 5023165 bytes, checksum: 4fb7ab8888cd9a6feb5ed666a5000b94 (MD5)Made available in DSpace on 2022-01-31T20:01:19Z (GMT). No. of bitstreams: 1 Dissertação Amanda Sofia de Guimarães e Stepanha (003).pdf: 5023165 bytes, checksum: 4fb7ab8888cd9a6feb5ed666a5000b94 (MD5) Previous issue date: 2021-08-26Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/183184/Disserta%c3%a7%c3%a3o%20Amanda%20Sofia%20de%20Guimar%c3%a3es%20e%20Stepanha%20%28003%29.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilEscola PolitécnicaArmazenamento Geológico de CO2Abandono e Reparo de PoçosResinas EpóxiDegradação de Resina Epóxi por CO2CO2 Geological StorageWell Repair and AbandonmentEpoxy ResinEpoxy Resin Degradation by CO2ENGENHARIASAvalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho não apresenta restrição para publicação495391460509391966550050060045189710564848268253590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDissertação Amanda Sofia de Guimarães e Stepanha (003).pdf.jpgDissertação Amanda Sofia de Guimarães e Stepanha (003).pdf.jpgimage/jpeg5236http://tede2.pucrs.br/tede2/bitstream/tede/10067/4/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf.jpgb5fa374c4a909b34d9a3338635b88d80MD54TEXTDissertação Amanda Sofia de Guimarães e Stepanha (003).pdf.txtDissertação Amanda Sofia de Guimarães e Stepanha (003).pdf.txttext/plain215315http://tede2.pucrs.br/tede2/bitstream/tede/10067/3/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf.txtd35012fe55df4d41025b60db1f509b05MD53ORIGINALDissertação Amanda Sofia de Guimarães e Stepanha (003).pdfDissertação Amanda Sofia de Guimarães e Stepanha (003).pdfapplication/pdf5023165http://tede2.pucrs.br/tede2/bitstream/tede/10067/2/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf4fb7ab8888cd9a6feb5ed666a5000b94MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/10067/1/license.txt220e11f2d3ba5354f917c7035aadef24MD51tede/100672022-01-31 20:00:27.95oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2022-01-31T22:00:27Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
title |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
spellingShingle |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 Stepanha, Amanda Sofia de Guimarães e Armazenamento Geológico de CO2 Abandono e Reparo de Poços Resinas Epóxi Degradação de Resina Epóxi por CO2 CO2 Geological Storage Well Repair and Abandonment Epoxy Resin Epoxy Resin Degradation by CO2 ENGENHARIAS |
title_short |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
title_full |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
title_fullStr |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
title_full_unstemmed |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
title_sort |
Avalianção da resistência química e mecânica de blendas de resina epóxi para aplicação em operações de reparo e abandono de poços de petróleo e de armazenamento geológico de CO2 |
author |
Stepanha, Amanda Sofia de Guimarães e |
author_facet |
Stepanha, Amanda Sofia de Guimarães e |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Dalla Vecchia, Felipe |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/4065200380277145 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/8483911283548170 |
dc.contributor.author.fl_str_mv |
Stepanha, Amanda Sofia de Guimarães e |
contributor_str_mv |
Dalla Vecchia, Felipe |
dc.subject.por.fl_str_mv |
Armazenamento Geológico de CO2 Abandono e Reparo de Poços Resinas Epóxi Degradação de Resina Epóxi por CO2 |
topic |
Armazenamento Geológico de CO2 Abandono e Reparo de Poços Resinas Epóxi Degradação de Resina Epóxi por CO2 CO2 Geological Storage Well Repair and Abandonment Epoxy Resin Epoxy Resin Degradation by CO2 ENGENHARIAS |
dc.subject.eng.fl_str_mv |
CO2 Geological Storage Well Repair and Abandonment Epoxy Resin Epoxy Resin Degradation by CO2 |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS |
description |
Class G Portland cement is the conventional material used for well construction, recovery, and abandonment operations. However, there are several studies indicating that this material is quite susceptible to acid environments degradation, as the ones observed in oil wells and CO2 injection wells, which can generate failures and leakages. Therefore, searches for alternative materials to cement has vital importance for the oil and gas industry to guarantee the integrity of wells, especially for well recovery and abandonment operations. In this context, the present work evaluates chemical and mechanical resistance of different commercial epoxy resin blends in conditions found in oil wells/CO2 geological storage reservoirs. The epoxy resin blends were formulated in different proportions and were exposed to degradation tests at 65 °C and 150 bar for 7 days in an aqueous medium saturated with CO2. Physicalchemical and mechanical characterization of the polymeric materials were performed through swelling test, X-ray microtomography (Micro-CT), compression test, scanning electron microscopy (MEV-FEG), atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR), thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC). Results indicated that the epoxy resin samples showed mechanical properties losses after the CO2 degradation test, due to macro-structural changes. There is no indication of chemical interaction between the epoxy resin blends and CO2. Despite the reduction of mechanical properties, resins can be a good option to repair and abandonment operations. From mathematical models, ideal blends for different well applications were identified. |
publishDate |
2021 |
dc.date.issued.fl_str_mv |
2021-08-26 |
dc.date.accessioned.fl_str_mv |
2022-01-31T20:01:19Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/10067 |
url |
http://tede2.pucrs.br/tede2/handle/tede/10067 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
4953914605093919665 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
4518971056484826825 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola Politécnica |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/10067/4/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/10067/3/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/10067/2/Disserta%C3%A7%C3%A3o+Amanda+Sofia+de+Guimar%C3%A3es+e+Stepanha+%28003%29.pdf http://tede2.pucrs.br/tede2/bitstream/tede/10067/1/license.txt |
bitstream.checksum.fl_str_mv |
b5fa374c4a909b34d9a3338635b88d80 d35012fe55df4d41025b60db1f509b05 4fb7ab8888cd9a6feb5ed666a5000b94 220e11f2d3ba5354f917c7035aadef24 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765353837887488 |