Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM

Detalhes bibliográficos
Autor(a) principal: Carvalho, Ligia Maria Nogarett Pibernat de
Data de Publicação: 2017
Tipo de documento: Tese
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/8155
Resumo: The aim of the present study was to asses the present of Bisphenol A in dental material used on CAD/CAM block.For this In Vitro study, blocks for CAD-CAM, Lava Ultimate, Enamic and Mark II in standardized fragments containeing Bisphenol A were evaluated. Ten fragments of each block were made: n = 30, immersed in deionized water on group 1 and artificial saliva Kin Hidrat on group 2 in a light protected bottle.Stored in a culture stove for 24 hours, all samples were put in 1,5ml bottles containing 1,0ml of artificial saliva (KIN HIDRAT, PharmaKIN, São Paulo, Brazil ) on group 1 and deionized water on group 2, and then freezed in -80ºC for 24 hours. After the 24 hour period, the samples were submitted to High Efficiency Chromatography on Toxicology and Pharmacology Institute of PUCRS as methodology described on this study.After cromatographic analysis of groups 1 and 2, the non-release of Bisphenol A was observed in all groups of samples tested. All groups and samples presented peak release of unidentified substance of different molecular weight and different breaking time than the Bisphenol A standard. Additional researches using other analysis methods are needed to examine the cumulative estrogenic effects of Bisphenol A dental materials for CAD CAM and composite resins.
id P_RS_65826fb31a3aa768edf6551a57d10280
oai_identifier_str oai:tede2.pucrs.br:tede/8155
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Mota, Eduardo Gonçalveshttp://lattes.cnpq.br/3500784167142389http://lattes.cnpq.br/3927794775424589Carvalho, Ligia Maria Nogarett Pibernat de2018-06-22T12:01:25Z2017-04-25http://tede2.pucrs.br/tede2/handle/tede/8155The aim of the present study was to asses the present of Bisphenol A in dental material used on CAD/CAM block.For this In Vitro study, blocks for CAD-CAM, Lava Ultimate, Enamic and Mark II in standardized fragments containeing Bisphenol A were evaluated. Ten fragments of each block were made: n = 30, immersed in deionized water on group 1 and artificial saliva Kin Hidrat on group 2 in a light protected bottle.Stored in a culture stove for 24 hours, all samples were put in 1,5ml bottles containing 1,0ml of artificial saliva (KIN HIDRAT, PharmaKIN, São Paulo, Brazil ) on group 1 and deionized water on group 2, and then freezed in -80ºC for 24 hours. After the 24 hour period, the samples were submitted to High Efficiency Chromatography on Toxicology and Pharmacology Institute of PUCRS as methodology described on this study.After cromatographic analysis of groups 1 and 2, the non-release of Bisphenol A was observed in all groups of samples tested. All groups and samples presented peak release of unidentified substance of different molecular weight and different breaking time than the Bisphenol A standard. Additional researches using other analysis methods are needed to examine the cumulative estrogenic effects of Bisphenol A dental materials for CAD CAM and composite resins.O objetivo geral deste estudo foi avaliar o componente Bisfenol A presente em blocos de materiais dentários utilizados no sistema CAD/CAM quanto a liberação ou não de Bisfenol A. Foram avaliados para a realização deste estudo in vitro, blocos para CAD/CAM, Lava Ultimate, Enamic e Mark II, em fragmentos padronizados, cuja matriz de resina composta continha Bisfenol A. Foram confeccionados 10 fragmentos de cada um dos blocos: n = 30, imerso em água deionizada no grupo 1 e saliva artificial KinHidrat no grupo 2 em frasco protegido da luz. Armazenadas em estufa por 24hs,todas as amostras, após o periodo de 24hs, foram armazenadas em recipientes de 1,5ml contendo 1,0 ml de saliva artificial (KIN HIDRAT,PharmaKIN, São Paulo, Brasil ) no grupo 1 e água deionizada no grupo 2 e após congeladas à - 80ºC por 24hs. Decorrido o período de 24h, as amostras foram submetidas a cromatografia de alta eficiência (HPLC) no Instituto de Toxicologia e Farmacologia da PUCRS com metodologia descrita no estudo.Após análise cromatográfica dos grupos 1 e 2 observou- se a não liberação de Bisfenol A em nenhum dos grupos de amostras testadas.Todos os grupos e amostras apresentaram pico de liberação de substância não identificada de diferente peso molecular e diferente tempo de quebra do padrão de Bisfenol A. Pesquisas adicionais, empregando outros métodos de análise são necessárias para examinar os efeitos estrogênicos cumulativos do Bisfenol A de materiais dentários para CAD/CAM e resinas compostas.Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2018-06-01T13:46:10Z No. of bitstreams: 1 LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf: 602746 bytes, checksum: 5e6dcc81b20622b739f9ab98624f9a66 (MD5)Rejected by Sheila Dias (sheila.dias@pucrs.br), reason: Devolvido devido à falta da capa institucional no arquivo em PDF. on 2018-06-11T12:41:58Z (GMT)Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2018-06-11T17:29:30Z No. of bitstreams: 1 LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf: 1308142 bytes, checksum: e3ba9abe3c75e3384b12c1a64fbba5dd (MD5)Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2018-06-22T11:52:39Z (GMT) No. of bitstreams: 1 LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf: 1308142 bytes, checksum: e3ba9abe3c75e3384b12c1a64fbba5dd (MD5)Made available in DSpace on 2018-06-22T12:01:25Z (GMT). No. of bitstreams: 1 LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf: 1308142 bytes, checksum: e3ba9abe3c75e3384b12c1a64fbba5dd (MD5) Previous issue date: 2017-04-25Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/172568/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilEscola de Ciências da SaúdeMateriais DentáriosCromatografia de Alta EficiênciaBisphenol ACAD/CAMCIENCIAS DA SAUDE::ODONTOLOGIAAvaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAMinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisTrabalho não apresenta restrição para publicação-8096554818733665164500500600-20704984698792443492075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.jpgLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.jpgimage/jpeg4720http://tede2.pucrs.br/tede2/bitstream/tede/8155/6/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.jpg44dc26caeef10853ca970750b5e92c17MD56TEXTLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.txtLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.txttext/plain42284http://tede2.pucrs.br/tede2/bitstream/tede/8155/5/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.txt6af03b9504476d4775d1f71b39d0d5dbMD55ORIGINALLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdfLIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdfapplication/pdf1308142http://tede2.pucrs.br/tede2/bitstream/tede/8155/4/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdfe3ba9abe3c75e3384b12c1a64fbba5ddMD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/8155/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53tede/81552018-06-22 12:00:54.681oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2018-06-22T15:00:54Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
title Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
spellingShingle Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
Carvalho, Ligia Maria Nogarett Pibernat de
Materiais Dentários
Cromatografia de Alta Eficiência
Bisphenol A
CAD/CAM
CIENCIAS DA SAUDE::ODONTOLOGIA
title_short Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
title_full Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
title_fullStr Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
title_full_unstemmed Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
title_sort Avaliação da liberação de bisfenol A em blocos de materiais dentários para CAD/CAM
author Carvalho, Ligia Maria Nogarett Pibernat de
author_facet Carvalho, Ligia Maria Nogarett Pibernat de
author_role author
dc.contributor.advisor1.fl_str_mv Mota, Eduardo Gonçalves
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/3500784167142389
dc.contributor.authorLattes.fl_str_mv http://lattes.cnpq.br/3927794775424589
dc.contributor.author.fl_str_mv Carvalho, Ligia Maria Nogarett Pibernat de
contributor_str_mv Mota, Eduardo Gonçalves
dc.subject.por.fl_str_mv Materiais Dentários
Cromatografia de Alta Eficiência
Bisphenol A
CAD/CAM
topic Materiais Dentários
Cromatografia de Alta Eficiência
Bisphenol A
CAD/CAM
CIENCIAS DA SAUDE::ODONTOLOGIA
dc.subject.cnpq.fl_str_mv CIENCIAS DA SAUDE::ODONTOLOGIA
description The aim of the present study was to asses the present of Bisphenol A in dental material used on CAD/CAM block.For this In Vitro study, blocks for CAD-CAM, Lava Ultimate, Enamic and Mark II in standardized fragments containeing Bisphenol A were evaluated. Ten fragments of each block were made: n = 30, immersed in deionized water on group 1 and artificial saliva Kin Hidrat on group 2 in a light protected bottle.Stored in a culture stove for 24 hours, all samples were put in 1,5ml bottles containing 1,0ml of artificial saliva (KIN HIDRAT, PharmaKIN, São Paulo, Brazil ) on group 1 and deionized water on group 2, and then freezed in -80ºC for 24 hours. After the 24 hour period, the samples were submitted to High Efficiency Chromatography on Toxicology and Pharmacology Institute of PUCRS as methodology described on this study.After cromatographic analysis of groups 1 and 2, the non-release of Bisphenol A was observed in all groups of samples tested. All groups and samples presented peak release of unidentified substance of different molecular weight and different breaking time than the Bisphenol A standard. Additional researches using other analysis methods are needed to examine the cumulative estrogenic effects of Bisphenol A dental materials for CAD CAM and composite resins.
publishDate 2017
dc.date.issued.fl_str_mv 2017-04-25
dc.date.accessioned.fl_str_mv 2018-06-22T12:01:25Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/8155
url http://tede2.pucrs.br/tede2/handle/tede/8155
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv -8096554818733665164
dc.relation.confidence.fl_str_mv 500
500
600
dc.relation.cnpq.fl_str_mv -2070498469879244349
dc.relation.sponsorship.fl_str_mv 2075167498588264571
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Odontologia
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Escola de Ciências da Saúde
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/8155/6/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/8155/5/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/8155/4/LIGIA_MARIA_NOGARETT_PIBERNAT_DE_CARVALHO_TES.pdf
http://tede2.pucrs.br/tede2/bitstream/tede/8155/3/license.txt
bitstream.checksum.fl_str_mv 44dc26caeef10853ca970750b5e92c17
6af03b9504476d4775d1f71b39d0d5db
e3ba9abe3c75e3384b12c1a64fbba5dd
5a9d6006225b368ef605ba16b4f6d1be
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1799765333822668800

Registros relacionados