Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina
Autor(a) principal: | |
---|---|
Data de Publicação: | 2020 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/9981 |
Resumo: | The aim of the study was to evaluate, in vitro, the fracture resistance of occlusal veneers, made by CAD/CAM, with IPS e.max CAD material in thicknesses of 0.6 mm and 0.3 mm bonded to enamel and dentin. Fifty human molars were randomly divided into five groups (n=10): G1 – sound teeth (control); G2 – veneer thickness with 0,3 mm bonded to enamel; G3 – veneer thickness with 0,6 mm bonded to enamel; G4 – veneer thickness with 0,3 mm bonded to dentin; G5 – veneer thickness with 0,6 mm bonded to dentin. The venners were adhesively luted to enamel or dentin and stored in distilled water for 24 hours. After storage, the samples were submitted to mechanical cyclic loading (1 million cycles at 200 N load). After that, the fracture resistance test was performed in a universal testing machine with crosshead speed of 1 mm/minute. The fractures were classificate as reparable and irreparable. Accoding to two-way analysis of variance (ANOVA), only veneers thickness factor was significant (p=0,002). According to Tukey test, means followed by diferent letters represent significant diferences (p<0.05): G1 (3204 N)ab; G2 (3144 N)ab ; G3 (2489 N)b ; G4 (3591 N)a; G5 (2770 N)ab. In the control group the failures were irreparable and in the experimental groups there were reparable and irreparable failures. It was concluded that ultrathin occlusal veneers, luted to enamel or dentin, obtained fracture resistance comparable to that of the sound tooth. |
id |
P_RS_867e6c3c9de3f85ee31faffb77b0a5b5 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/9981 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Spohr, Ana Mariahttp://lattes.cnpq.br/9374309741859850http://lattes.cnpq.br/8616634625060319Valenzuela, Eneida Beatriz Sanfelice2021-11-30T17:27:34Z2020-02-26http://tede2.pucrs.br/tede2/handle/tede/9981The aim of the study was to evaluate, in vitro, the fracture resistance of occlusal veneers, made by CAD/CAM, with IPS e.max CAD material in thicknesses of 0.6 mm and 0.3 mm bonded to enamel and dentin. Fifty human molars were randomly divided into five groups (n=10): G1 – sound teeth (control); G2 – veneer thickness with 0,3 mm bonded to enamel; G3 – veneer thickness with 0,6 mm bonded to enamel; G4 – veneer thickness with 0,3 mm bonded to dentin; G5 – veneer thickness with 0,6 mm bonded to dentin. The venners were adhesively luted to enamel or dentin and stored in distilled water for 24 hours. After storage, the samples were submitted to mechanical cyclic loading (1 million cycles at 200 N load). After that, the fracture resistance test was performed in a universal testing machine with crosshead speed of 1 mm/minute. The fractures were classificate as reparable and irreparable. Accoding to two-way analysis of variance (ANOVA), only veneers thickness factor was significant (p=0,002). According to Tukey test, means followed by diferent letters represent significant diferences (p<0.05): G1 (3204 N)ab; G2 (3144 N)ab ; G3 (2489 N)b ; G4 (3591 N)a; G5 (2770 N)ab. In the control group the failures were irreparable and in the experimental groups there were reparable and irreparable failures. It was concluded that ultrathin occlusal veneers, luted to enamel or dentin, obtained fracture resistance comparable to that of the sound tooth.O objetivo do estudo, in vitro, foi avaliar a resistência à fratura de restaurações cerâmicas IPS e.max CAD confeccionadas pela técnica CAD/CAM (Computer-aided desing/Computer-aided manufacturing) em espessuras ultrafinas (0,3 mm 0,6 mm), cimentadas em substratos de esmalte ou dentina. Cinquenta molares humanos foram divididos randomicamente em cinco grupos (n=10): G1 – dentes hígidos (controle) ; G2 – espessura da restauração de 0,3 mm cimentada em esmalte; G3 – restauração com 0.6 mm cimentada em esmalte; G4 – restauração com 0,3 mm cimentada em dentina; G5 – restauração com 0,6 mm cimentada em dentina. A cimentação foi realizada em esmalte ou dentina pela técnica adesiva, sendo armazenadas em água destilada a 37ºC por 24 h. Após armazenagem, as amostras foram submetidas à ciclagem mecânica (1.000.000 de ciclos com carga de 200 N). Na sequência, foi realizado o teste de resistência à fratura em máquina de ensaio universal com velocidade de carregamento de 1 mm/minuto. As fraturas foram classificadas como reparáveis e irreparáveis. De acordo com a Análise de Variância de duas vias, apenas o efeito da espessura das restaurações foi significativo (p = 0,002). De acordo com o teste de Tukey, médias seguidas de letras distintas diferem estatisticamente entre si (p<0,05): G1 (3204 N)ab; G2 (3144 N)ab; G3 (2489 N)b; G4 (3591 N)a; G5 (2770 N)ab. As falhas foram irreparáveis no grupo controle, havendo falhas reparáveis e irreparáveis nos grupos experimentais. Concluiu-se que as restaurações ultrafinas, cimentadas em esmalte como em dentina, obtiveram resistência à fratura comparáveis ao do dente hígido.Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2021-11-29T19:14:41Z No. of bitstreams: 1 ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_DIS.pdf: 427498 bytes, checksum: b54e35b0a55a5cc8a3442f95775af5b5 (MD5)Approved for entry into archive by Caroline Xavier (caroline.xavier@pucrs.br) on 2021-11-30T17:20:28Z (GMT) No. of bitstreams: 1 ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_DIS.pdf: 427498 bytes, checksum: b54e35b0a55a5cc8a3442f95775af5b5 (MD5)Made available in DSpace on 2021-11-30T17:27:34Z (GMT). No. of bitstreams: 1 ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_DIS.pdf: 427498 bytes, checksum: b54e35b0a55a5cc8a3442f95775af5b5 (MD5) Previous issue date: 2020-02-26Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/182737/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilEscola de Ciências da Saúde e da VidaCerâmicaResistência à fraturaEsmalteDentinaCeramicFracture resistanceEnamelDentinCIENCIAS DA SAUDE:ODONTOLOGIAResistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentinainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho será publicado como artigo ou livro60 meses30/11/2026-74118697205007646675006003590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.jpgDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.jpgimage/jpeg4096http://tede2.pucrs.br/tede2/bitstream/tede/9981/4/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.jpg9b0d64ac488a54f0e6b1f05e65fd65e3MD54TEXTDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.txtDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.txttext/plain1375http://tede2.pucrs.br/tede2/bitstream/tede/9981/3/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.txt4e976abf2cdb0b0203b860919482b038MD53ORIGINALDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdfDIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdfapplication/pdf314954http://tede2.pucrs.br/tede2/bitstream/tede/9981/2/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdfa25f6471910fce9d3d149735a67c72b9MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/9981/1/license.txt220e11f2d3ba5354f917c7035aadef24MD51tede/99812021-11-30 20:00:25.899oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2021-11-30T22:00:25Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
title |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
spellingShingle |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina Valenzuela, Eneida Beatriz Sanfelice Cerâmica Resistência à fratura Esmalte Dentina Ceramic Fracture resistance Enamel Dentin CIENCIAS DA SAUDE:ODONTOLOGIA |
title_short |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
title_full |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
title_fullStr |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
title_full_unstemmed |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
title_sort |
Resistência à fratura de facetas oclusais ultrafinas confeccionadas em CAD/CAM e cimentadas em esmalte e dentina |
author |
Valenzuela, Eneida Beatriz Sanfelice |
author_facet |
Valenzuela, Eneida Beatriz Sanfelice |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Spohr, Ana Maria |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/9374309741859850 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/8616634625060319 |
dc.contributor.author.fl_str_mv |
Valenzuela, Eneida Beatriz Sanfelice |
contributor_str_mv |
Spohr, Ana Maria |
dc.subject.por.fl_str_mv |
Cerâmica Resistência à fratura Esmalte Dentina |
topic |
Cerâmica Resistência à fratura Esmalte Dentina Ceramic Fracture resistance Enamel Dentin CIENCIAS DA SAUDE:ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Ceramic Fracture resistance Enamel Dentin |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE:ODONTOLOGIA |
description |
The aim of the study was to evaluate, in vitro, the fracture resistance of occlusal veneers, made by CAD/CAM, with IPS e.max CAD material in thicknesses of 0.6 mm and 0.3 mm bonded to enamel and dentin. Fifty human molars were randomly divided into five groups (n=10): G1 – sound teeth (control); G2 – veneer thickness with 0,3 mm bonded to enamel; G3 – veneer thickness with 0,6 mm bonded to enamel; G4 – veneer thickness with 0,3 mm bonded to dentin; G5 – veneer thickness with 0,6 mm bonded to dentin. The venners were adhesively luted to enamel or dentin and stored in distilled water for 24 hours. After storage, the samples were submitted to mechanical cyclic loading (1 million cycles at 200 N load). After that, the fracture resistance test was performed in a universal testing machine with crosshead speed of 1 mm/minute. The fractures were classificate as reparable and irreparable. Accoding to two-way analysis of variance (ANOVA), only veneers thickness factor was significant (p=0,002). According to Tukey test, means followed by diferent letters represent significant diferences (p<0.05): G1 (3204 N)ab; G2 (3144 N)ab ; G3 (2489 N)b ; G4 (3591 N)a; G5 (2770 N)ab. In the control group the failures were irreparable and in the experimental groups there were reparable and irreparable failures. It was concluded that ultrathin occlusal veneers, luted to enamel or dentin, obtained fracture resistance comparable to that of the sound tooth. |
publishDate |
2020 |
dc.date.issued.fl_str_mv |
2020-02-26 |
dc.date.accessioned.fl_str_mv |
2021-11-30T17:27:34Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/9981 |
url |
http://tede2.pucrs.br/tede2/handle/tede/9981 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-7411869720500764667 |
dc.relation.confidence.fl_str_mv |
500 600 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola de Ciências da Saúde e da Vida |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/9981/4/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/9981/3/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/9981/2/DIS_ENEIDA_BEATRIZ_SANFELICE_VALENZUELA_CONFIDENCIAL.pdf http://tede2.pucrs.br/tede2/bitstream/tede/9981/1/license.txt |
bitstream.checksum.fl_str_mv |
9b0d64ac488a54f0e6b1f05e65fd65e3 4e976abf2cdb0b0203b860919482b038 a25f6471910fce9d3d149735a67c72b9 220e11f2d3ba5354f917c7035aadef24 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765352855371776 |