Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio

Detalhes bibliográficos
Autor(a) principal: Souza, Bruno Vaz de
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/6220
Resumo: This work presents the influence of the heat treatment parameters of austempering carried out in a zinc aluminum bath on the mechanical properties of a ductile cast iron (ADI). Samples were extracted from as-cast standard blocks for the austempering heat treatment. The material was heated to 900°C for 60 minutes for austenitization and cooled in a zinc-aluminum bath, to a temperature of 400°C, for 30 minutes, 60 minutes and 90 minutes. The samples were analyzed by optical microscopy, scanning electron microscopy, and mechanical tests (Brinell hardness, Micro Vickers hardness, Izod Impact Test and Tensile Test). The results, comparing the mechanical properties and microstructural characteristics in all cycles, present results compatible with the two stages of the material process window, confirming the effectiveness of the zinc-aluminum bath in getting the ADI.
id P_RS_8e9c5d5fef960c32efd4f42c264e571b
oai_identifier_str oai:tede2.pucrs.br:tede/6220
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Santos, Carlos Alexandre dos172.870.678-54http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4768539U0984.648.090-34http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4715960P9Souza, Bruno Vaz de2015-07-17T20:14:00Z2015-03-30http://tede2.pucrs.br/tede2/handle/tede/6220This work presents the influence of the heat treatment parameters of austempering carried out in a zinc aluminum bath on the mechanical properties of a ductile cast iron (ADI). Samples were extracted from as-cast standard blocks for the austempering heat treatment. The material was heated to 900°C for 60 minutes for austenitization and cooled in a zinc-aluminum bath, to a temperature of 400°C, for 30 minutes, 60 minutes and 90 minutes. The samples were analyzed by optical microscopy, scanning electron microscopy, and mechanical tests (Brinell hardness, Micro Vickers hardness, Izod Impact Test and Tensile Test). The results, comparing the mechanical properties and microstructural characteristics in all cycles, present results compatible with the two stages of the material process window, confirming the effectiveness of the zinc-aluminum bath in getting the ADI.O presente trabalho apresenta a influência da variação de parâmetros do tratamento térmico de austêmpera realizado usando um banho de zinco fundido, e os efeitos nas propriedades mecânicas do ferro fundido austemperado (ADI). Corpos de prova foram extraídos de blocos fundidos padronizados para aplicação dos tratamentos térmicos de austêmpera. O material foi aquecido a 900oC durante 60 minutos para austenitização, e então resfriado em um banho de zinco-alumínio fundido a 400oC por 30 minutos, 60 minutos e 90 minutos. Os corpos de prova foram analisados por microscopia óptica, microscopia eletrônica de varredura e ensaios mecânicos (dureza Brinnell, microdureza Vickers, testes de Impacto Charpy e Resistência à Tração). Os resultados, comparadas as propriedades mecânicas e características microestruturais em todos os ciclos, apresentam resultados compatíveis com os dois estágios previstos pela janela de processo do material, confirmando a efetividade do banho de Zinco-Alumínio na obtenção do ADI.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2015-07-17T20:14:00Z No. of bitstreams: 1 472389 - Texto Completo.pdf: 3567307 bytes, checksum: 701ea7ad45fd2a973390e2755f3d5161 (MD5)Made available in DSpace on 2015-07-17T20:14:00Z (GMT). No. of bitstreams: 1 472389 - Texto Completo.pdf: 3567307 bytes, checksum: 701ea7ad45fd2a973390e2755f3d5161 (MD5) Previous issue date: 2015-03-30application/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/163160/472389%20-%20Texto%20Completo.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilFaculdade de EngenhariaENGENHARIA DE MATERIAISMETAIS - USINAGEMMETAIS - TRATAMENTO TÉRMICOUSINAGEMFERRO FUNDIDOENGENHARIASDesenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínioinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-7432719344215120122600600600-6557705727614397854518971056484826825info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAIL472389 - Texto Completo.pdf.jpg472389 - Texto Completo.pdf.jpgimage/jpeg3948http://tede2.pucrs.br/tede2/bitstream/tede/6220/4/472389+-+Texto+Completo.pdf.jpgbdd63bcea23176988233beabf671396fMD54TEXT472389 - Texto Completo.pdf.txt472389 - Texto Completo.pdf.txttext/plain73232http://tede2.pucrs.br/tede2/bitstream/tede/6220/3/472389+-+Texto+Completo.pdf.txt45a37480fc48cf6ffdec6d9201b0d5faMD53ORIGINAL472389 - Texto Completo.pdf472389 - Texto Completo.pdfapplication/pdf3567307http://tede2.pucrs.br/tede2/bitstream/tede/6220/2/472389+-+Texto+Completo.pdf701ea7ad45fd2a973390e2755f3d5161MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6220/1/license.txt5a9d6006225b368ef605ba16b4f6d1beMD51tede/62202015-09-29 08:29:29.435oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2015-09-29T11:29:29Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
title Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
spellingShingle Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
Souza, Bruno Vaz de
ENGENHARIA DE MATERIAIS
METAIS - USINAGEM
METAIS - TRATAMENTO TÉRMICO
USINAGEM
FERRO FUNDIDO
ENGENHARIAS
title_short Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
title_full Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
title_fullStr Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
title_full_unstemmed Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
title_sort Desenvolvimento de ferro fundido austemperado (ADI) em banho de zinco-alumínio
author Souza, Bruno Vaz de
author_facet Souza, Bruno Vaz de
author_role author
dc.contributor.advisor1.fl_str_mv Santos, Carlos Alexandre dos
dc.contributor.advisor1ID.fl_str_mv 172.870.678-54
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4768539U0
dc.contributor.authorID.fl_str_mv 984.648.090-34
dc.contributor.authorLattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4715960P9
dc.contributor.author.fl_str_mv Souza, Bruno Vaz de
contributor_str_mv Santos, Carlos Alexandre dos
dc.subject.por.fl_str_mv ENGENHARIA DE MATERIAIS
METAIS - USINAGEM
METAIS - TRATAMENTO TÉRMICO
USINAGEM
FERRO FUNDIDO
topic ENGENHARIA DE MATERIAIS
METAIS - USINAGEM
METAIS - TRATAMENTO TÉRMICO
USINAGEM
FERRO FUNDIDO
ENGENHARIAS
dc.subject.cnpq.fl_str_mv ENGENHARIAS
description This work presents the influence of the heat treatment parameters of austempering carried out in a zinc aluminum bath on the mechanical properties of a ductile cast iron (ADI). Samples were extracted from as-cast standard blocks for the austempering heat treatment. The material was heated to 900°C for 60 minutes for austenitization and cooled in a zinc-aluminum bath, to a temperature of 400°C, for 30 minutes, 60 minutes and 90 minutes. The samples were analyzed by optical microscopy, scanning electron microscopy, and mechanical tests (Brinell hardness, Micro Vickers hardness, Izod Impact Test and Tensile Test). The results, comparing the mechanical properties and microstructural characteristics in all cycles, present results compatible with the two stages of the material process window, confirming the effectiveness of the zinc-aluminum bath in getting the ADI.
publishDate 2015
dc.date.accessioned.fl_str_mv 2015-07-17T20:14:00Z
dc.date.issued.fl_str_mv 2015-03-30
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/6220
url http://tede2.pucrs.br/tede2/handle/tede/6220
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv -7432719344215120122
dc.relation.confidence.fl_str_mv 600
600
600
dc.relation.department.fl_str_mv -655770572761439785
dc.relation.cnpq.fl_str_mv 4518971056484826825
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Faculdade de Engenharia
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/6220/4/472389+-+Texto+Completo.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/6220/3/472389+-+Texto+Completo.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6220/2/472389+-+Texto+Completo.pdf
http://tede2.pucrs.br/tede2/bitstream/tede/6220/1/license.txt
bitstream.checksum.fl_str_mv bdd63bcea23176988233beabf671396f
45a37480fc48cf6ffdec6d9201b0d5fa
701ea7ad45fd2a973390e2755f3d5161
5a9d6006225b368ef605ba16b4f6d1be
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1821771188007862272

Registros relacionados