Nanotubos de titanatos e sua aplicação em matrizes de poliuretano

Detalhes bibliográficos
Autor(a) principal: Monteiro, Wesley Formentin
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/6406
Resumo: The search for improvements in the properties of polymer matrices has been the subject of several studies. Among these, the use of inorganic fillers has shown results that demonstrate improvements in many properties of the polymers. In this context, this study aimed to preparation of titanates nanotubes (TNT) and its application in polyurethane nanocomposites (PU). In order to the TNT were synthesized from commercial TiO2 in anatase phase by hydrothermal method. After, these TNT were functionalized (TNTF) with hexamethylene diisocianato (HDI) and silanes compounds: aminopropyl trimethoxysilane (APTMS) and tetraethyl orthosilicate (TEOS) in order to study the interaction of the functionalizated charge with the polymer matrix. The titanates nanotubes (TNT) and titanates nanotubes functionalized (TNTF) were characterized regarding their morphological and structural properties. Nanocomposites of PU with TiO2, TNT and TNTF were synthesized, via in situ polymerization and characterized by FTIR, GPC, SEM, TEM (just NTT), AFM, TGA, DSC and DRX techniques. The results showed that the TNT synthesis by hydrothermal method was effective and was obtained nanotubes formed with a minimum of 3 staked sheets. The TNTF functionalized with APTMS and TEOS showed clustered structures whereas with HDI has a separation of nanotubes. The addition of TNT-HDI provided an increase of polymer molar weight. All nanocomposites showed higher thermal stability (between 330-340oC) than the pure PU (325oC). Nanocomposites PU/TNTF presented the highest values for crystallization temperature (≈ 6-10oC) when compared to pure PU (5oC), besides of its enthalpies, indicating that TNTF promote the increase of the polyurethane crystallinity.
id P_RS_bc9c1979efdba358ffee5b7f19dcc279
oai_identifier_str oai:tede2.pucrs.br:tede/6406
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Ligabue, Rosane Angélica501.822.770-20http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4784426H5020.837.130-36http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4470652A6Monteiro, Wesley Formentin2015-11-26T11:39:49Z2015-03-03http://tede2.pucrs.br/tede2/handle/tede/6406The search for improvements in the properties of polymer matrices has been the subject of several studies. Among these, the use of inorganic fillers has shown results that demonstrate improvements in many properties of the polymers. In this context, this study aimed to preparation of titanates nanotubes (TNT) and its application in polyurethane nanocomposites (PU). In order to the TNT were synthesized from commercial TiO2 in anatase phase by hydrothermal method. After, these TNT were functionalized (TNTF) with hexamethylene diisocianato (HDI) and silanes compounds: aminopropyl trimethoxysilane (APTMS) and tetraethyl orthosilicate (TEOS) in order to study the interaction of the functionalizated charge with the polymer matrix. The titanates nanotubes (TNT) and titanates nanotubes functionalized (TNTF) were characterized regarding their morphological and structural properties. Nanocomposites of PU with TiO2, TNT and TNTF were synthesized, via in situ polymerization and characterized by FTIR, GPC, SEM, TEM (just NTT), AFM, TGA, DSC and DRX techniques. The results showed that the TNT synthesis by hydrothermal method was effective and was obtained nanotubes formed with a minimum of 3 staked sheets. The TNTF functionalized with APTMS and TEOS showed clustered structures whereas with HDI has a separation of nanotubes. The addition of TNT-HDI provided an increase of polymer molar weight. All nanocomposites showed higher thermal stability (between 330-340oC) than the pure PU (325oC). Nanocomposites PU/TNTF presented the highest values for crystallization temperature (≈ 6-10oC) when compared to pure PU (5oC), besides of its enthalpies, indicating that TNTF promote the increase of the polyurethane crystallinity.A busca por melhorias nas propriedades de matrizes poliméricas tem sido motivo de muitos estudos. Entre estes, a aplicação de cargas inorgânicas tem apresentado resultados que evidenciam melhorias nas diversas propriedades dos polímeros. Dentro deste contexto insere-se este trabalho, que teve como objetivo principal a preparação de nanotubos de titanatos (NTT) e sua aplicação em nanocompósitos de poliuretano (PU). Para tanto, os NTT foram sintetizados partindo de TiO2 comercial na fase anatásio por método hidrotérmico. Após, estes NTT foram funcionalizados (NTTF) com hexametilenodiisocianato (HDI) e os compostos: aminopropil trimetoxisilano (APTMS) e tetraetil ortosilicato (TEOS) a fim de estudar a influência destas funcionalizações na interação da carga com a matriz polimérica. Os nanotubo de titanatos (NTT) e os nanotubos de titanatos funcionalizados (NTTF) foram caracterizados em relação as suas propriedades morfológicas e estruturais. Nanocompósitos de PU com TiO2, NTT e NTTF foram sintetizados, via polimerização in situ, e caracterizados por técnicas de FTIR, GPC, MEV, MET (somente os NTT), AFM, TGA, DSC e DRX. Os resultados mostraram que a síntese dos NTT pelo método hidrotérmico foi eficiente e obteve-se nanotubos formados por no mínimo 3 folhas empilhadas. Os NTTF funcionalizados com APTMS e TEOS apresentaram estruturas aglomeradas enquanto que com HDI houve afastamento dos nanotubos. A adição de NTT-HDI proporcionou um aumento da massa molar do polímero e maior mobilidade para a cadeia. Todos os nanocompósitos apresentaram maior estabilidade térmica (entre 330-340oC) que o PU padrão (325oC). Os nanocompósitos PU/NTTF apresentaram os maiores valores para as temperaturas de cristalização (≈ 6-10oC) comparado ao PU padrão (Tc=5oC), além das respectivas entalpias indicando que os NTTF aumentam a cristalinidade do poliuretano.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2015-11-26T11:39:49Z No. of bitstreams: 1 476451 - Texto Completo.pdf: 8210475 bytes, checksum: d312c576e78b0f9de246885a55a53e56 (MD5)Made available in DSpace on 2015-11-26T11:39:49Z (GMT). No. of bitstreams: 1 476451 - Texto Completo.pdf: 8210475 bytes, checksum: d312c576e78b0f9de246885a55a53e56 (MD5) Previous issue date: 2015-03-03application/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/163717/476451%20-%20Texto%20Completo.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilFaculdade de EngenhariaENGENHARIA DE MATERIAISPOLÍMEROSPOLIURETANOSPOLIMERIZAÇÃONANOCOMPÓSITOSENGENHARIASNanotubos de titanatos e sua aplicação em matrizes de poliuretanoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-7432719344215120122600600600-6557705727614397854518971056484826825info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAIL476451 - Texto Completo.pdf.jpg476451 - Texto Completo.pdf.jpgimage/jpeg4021http://tede2.pucrs.br/tede2/bitstream/tede/6406/4/476451+-+Texto+Completo.pdf.jpg07dff070f50eedfe6190ac6116fce4c5MD54TEXT476451 - Texto Completo.pdf.txt476451 - Texto Completo.pdf.txttext/plain126630http://tede2.pucrs.br/tede2/bitstream/tede/6406/3/476451+-+Texto+Completo.pdf.txtede46ca296a338c1ce3471dfc516e061MD53ORIGINAL476451 - Texto Completo.pdf476451 - Texto Completo.pdfapplication/pdf8210475http://tede2.pucrs.br/tede2/bitstream/tede/6406/2/476451+-+Texto+Completo.pdfd312c576e78b0f9de246885a55a53e56MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6406/1/license.txt5a9d6006225b368ef605ba16b4f6d1beMD51tede/64062015-11-26 12:00:27.414oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2015-11-26T14:00:27Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
title Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
spellingShingle Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
Monteiro, Wesley Formentin
ENGENHARIA DE MATERIAIS
POLÍMEROS
POLIURETANOS
POLIMERIZAÇÃO
NANOCOMPÓSITOS
ENGENHARIAS
title_short Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
title_full Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
title_fullStr Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
title_full_unstemmed Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
title_sort Nanotubos de titanatos e sua aplicação em matrizes de poliuretano
author Monteiro, Wesley Formentin
author_facet Monteiro, Wesley Formentin
author_role author
dc.contributor.advisor1.fl_str_mv Ligabue, Rosane Angélica
dc.contributor.advisor1ID.fl_str_mv 501.822.770-20
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4784426H5
dc.contributor.authorID.fl_str_mv 020.837.130-36
dc.contributor.authorLattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4470652A6
dc.contributor.author.fl_str_mv Monteiro, Wesley Formentin
contributor_str_mv Ligabue, Rosane Angélica
dc.subject.por.fl_str_mv ENGENHARIA DE MATERIAIS
POLÍMEROS
POLIURETANOS
POLIMERIZAÇÃO
NANOCOMPÓSITOS
topic ENGENHARIA DE MATERIAIS
POLÍMEROS
POLIURETANOS
POLIMERIZAÇÃO
NANOCOMPÓSITOS
ENGENHARIAS
dc.subject.cnpq.fl_str_mv ENGENHARIAS
description The search for improvements in the properties of polymer matrices has been the subject of several studies. Among these, the use of inorganic fillers has shown results that demonstrate improvements in many properties of the polymers. In this context, this study aimed to preparation of titanates nanotubes (TNT) and its application in polyurethane nanocomposites (PU). In order to the TNT were synthesized from commercial TiO2 in anatase phase by hydrothermal method. After, these TNT were functionalized (TNTF) with hexamethylene diisocianato (HDI) and silanes compounds: aminopropyl trimethoxysilane (APTMS) and tetraethyl orthosilicate (TEOS) in order to study the interaction of the functionalizated charge with the polymer matrix. The titanates nanotubes (TNT) and titanates nanotubes functionalized (TNTF) were characterized regarding their morphological and structural properties. Nanocomposites of PU with TiO2, TNT and TNTF were synthesized, via in situ polymerization and characterized by FTIR, GPC, SEM, TEM (just NTT), AFM, TGA, DSC and DRX techniques. The results showed that the TNT synthesis by hydrothermal method was effective and was obtained nanotubes formed with a minimum of 3 staked sheets. The TNTF functionalized with APTMS and TEOS showed clustered structures whereas with HDI has a separation of nanotubes. The addition of TNT-HDI provided an increase of polymer molar weight. All nanocomposites showed higher thermal stability (between 330-340oC) than the pure PU (325oC). Nanocomposites PU/TNTF presented the highest values for crystallization temperature (≈ 6-10oC) when compared to pure PU (5oC), besides of its enthalpies, indicating that TNTF promote the increase of the polyurethane crystallinity.
publishDate 2015
dc.date.accessioned.fl_str_mv 2015-11-26T11:39:49Z
dc.date.issued.fl_str_mv 2015-03-03
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/6406
url http://tede2.pucrs.br/tede2/handle/tede/6406
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv -7432719344215120122
dc.relation.confidence.fl_str_mv 600
600
600
dc.relation.department.fl_str_mv -655770572761439785
dc.relation.cnpq.fl_str_mv 4518971056484826825
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Faculdade de Engenharia
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/6406/4/476451+-+Texto+Completo.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/6406/3/476451+-+Texto+Completo.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6406/2/476451+-+Texto+Completo.pdf
http://tede2.pucrs.br/tede2/bitstream/tede/6406/1/license.txt
bitstream.checksum.fl_str_mv 07dff070f50eedfe6190ac6116fce4c5
ede46ca296a338c1ce3471dfc516e061
d312c576e78b0f9de246885a55a53e56
5a9d6006225b368ef605ba16b4f6d1be
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1799765316133191680

Registros relacionados