Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/8694 |
Resumo: | The use of nanomaterials in concrete has shown promise, as the use of several types of these materials in cementitious compounds have been found to guarantee greater physical-mechanical properties and improvement in concrete microstructure. The use of mineral admixtures like nanosilica and silica fume ensures the improvement of interfacial transition zone (ITZ) between aggregate and paste, which is a weaker part in high-performance concrete (HPC). In this way, the present work intends to evaluate the performance of nanosilica and silica fume in properties of HPC in macro and microstructural properties. Were evaluated the mechanical properties (compressive strength and elastic modulus) and microstructural properties through nanoindentation, scanning electron microscopy, X-ray microtomography and atomic force microscopy of concretes with 1.5 and 3% of nanosilica and 5% and 10% of silica fume. The results indicated that with the use of mineral admixtures the compressive strength and elastic modulus of concrete increase significantly. The microstructural investigations showed that the nanosilica and silica fume leads to a densification of ITZ, which was the main responsible for the improvement of HPC performance. |
id |
P_RS_c1d5fb64e22636adeb4963b11ad34302 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/8694 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Andrade, Jairo José de Oliveirahttp://lattes.cnpq.br/2835610496598824http://lattes.cnpq.br/2179298630407594Schiavon, Jéssica Zamboni2019-06-13T13:36:21Z2019-03-27http://tede2.pucrs.br/tede2/handle/tede/8694The use of nanomaterials in concrete has shown promise, as the use of several types of these materials in cementitious compounds have been found to guarantee greater physical-mechanical properties and improvement in concrete microstructure. The use of mineral admixtures like nanosilica and silica fume ensures the improvement of interfacial transition zone (ITZ) between aggregate and paste, which is a weaker part in high-performance concrete (HPC). In this way, the present work intends to evaluate the performance of nanosilica and silica fume in properties of HPC in macro and microstructural properties. Were evaluated the mechanical properties (compressive strength and elastic modulus) and microstructural properties through nanoindentation, scanning electron microscopy, X-ray microtomography and atomic force microscopy of concretes with 1.5 and 3% of nanosilica and 5% and 10% of silica fume. The results indicated that with the use of mineral admixtures the compressive strength and elastic modulus of concrete increase significantly. The microstructural investigations showed that the nanosilica and silica fume leads to a densification of ITZ, which was the main responsible for the improvement of HPC performance.O uso de nanomateriais no concreto tem se mostrado promissor, uma vez que se constatou que a utilização de diversos tipos desses materiais em compostos cimentícios proporciona melhorias nas propriedades físico-mecânicas e na microestrutura do concreto. O uso de adições minerais como a nanosílica e a sílica ativa garante a minoração da zona de transição entre agregado e pasta, que é a parte mais fraca no concreto de alto desempenho. Desta forma, o presente trabalho pretende avaliar a ação da nanosílica e sílica ativa nas propriedades macro e microestruturais do concreto de alto desempenho. Foram avaliadas as propriedades mecânicas (resistência à compressão e módulo de elasticidade) e propriedades microestruturais por nanoindentação, microscopia eletrônica de varredura, microtomografia de raios X e microscopia de força atômica de concretos com 1,5 e 3% de nanosílica e 5% e 10% de sílica ativa. Os resultados indicaram que, com o uso de aditivos minerais, a resistência à compressão e o módulo de elasticidade do concreto aumentam significativamente. As investigações microestruturais mostraram que a nanosílica e a sílica ativa proporcionaram uma densificação da zona de transição, que foi a principal responsável pelo aperfeiçoamento do concreto de alto desempenho.Submitted by PPG Engenharia e Tecnologia de Materiais (engenharia.pg.materiais@pucrs.br) on 2019-05-23T19:16:04Z No. of bitstreams: 1 Entrega final pdf Dissertação Jéssica Z Schiavon.pdf: 3893677 bytes, checksum: 7f12d33c16c4c5ca7d07bf753955057a (MD5)Approved for entry into archive by Caroline Xavier (caroline.xavier@pucrs.br) on 2019-06-13T13:32:56Z (GMT) No. of bitstreams: 1 Entrega final pdf Dissertação Jéssica Z Schiavon.pdf: 3893677 bytes, checksum: 7f12d33c16c4c5ca7d07bf753955057a (MD5)Made available in DSpace on 2019-06-13T13:36:21Z (GMT). No. of bitstreams: 1 Entrega final pdf Dissertação Jéssica Z Schiavon.pdf: 3893677 bytes, checksum: 7f12d33c16c4c5ca7d07bf753955057a (MD5) Previous issue date: 2019-03-27Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/175516/DIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.jpghttp://tede2.pucrs.br:80/tede2/retrieve/178239/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilEscola PolitécnicaConcreto de Alto DesempenhoZona de TransiçãoSílica AtivaNanosílicaPropriedades MicroestruturaisENGENHARIASAnálise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho será publicado como artigo ou livro12 meses13/06/2020495391460509391966550050060045189710564848268253590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSORIGINALDIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdfDIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdfapplication/pdf3893677http://tede2.pucrs.br/tede2/bitstream/tede/8694/5/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf7f12d33c16c4c5ca7d07bf753955057aMD55THUMBNAILDIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.jpgDIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.jpgimage/jpeg4084http://tede2.pucrs.br/tede2/bitstream/tede/8694/4/DIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.jpgcfe97124be6dd755befffbd0bcdf8f36MD54DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.jpgDIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.jpgimage/jpeg5716http://tede2.pucrs.br/tede2/bitstream/tede/8694/7/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.jpg80fdface6d2f65d864fa69a2510173eaMD57TEXTDIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.txtDIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.txttext/plain1413http://tede2.pucrs.br/tede2/bitstream/tede/8694/3/DIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.txtb3f913924c96a27198cd414fdb87304fMD53DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.txtDIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.txttext/plain133457http://tede2.pucrs.br/tede2/bitstream/tede/8694/6/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.txt3aee826ec220406d02bc2713f359bce0MD56LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/8694/1/license.txt220e11f2d3ba5354f917c7035aadef24MD51tede/86942020-07-09 20:00:44.567oai:tede2.pucrs.br:tede/8694QXV0b3JpemE/P28gcGFyYSBQdWJsaWNhPz9vIEVsZXRyP25pY2E6IENvbSBiYXNlIG5vIGRpc3Bvc3RvIG5hIExlaSBGZWRlcmFsIG4/OS42MTAsIGRlIDE5IGRlIGZldmVyZWlybyBkZSAxOTk4LCBvIGF1dG9yIEFVVE9SSVpBIGEgcHVibGljYT8/byBlbGV0cj9uaWNhIGRhIHByZXNlbnRlIG9icmEgbm8gYWNlcnZvIGRhIEJpYmxpb3RlY2EgRGlnaXRhbCBkYSBQb250aWY/Y2lhIFVuaXZlcnNpZGFkZSBDYXQ/bGljYSBkbyBSaW8gR3JhbmRlIGRvIFN1bCwgc2VkaWFkYSBhIEF2LiBJcGlyYW5nYSA2NjgxLCBQb3J0byBBbGVncmUsIFJpbyBHcmFuZGUgZG8gU3VsLCBjb20gcmVnaXN0cm8gZGUgQ05QSiA4ODYzMDQxMzAwMDItODEgYmVtIGNvbW8gZW0gb3V0cmFzIGJpYmxpb3RlY2FzIGRpZ2l0YWlzLCBuYWNpb25haXMgZSBpbnRlcm5hY2lvbmFpcywgY29ucz9yY2lvcyBlIHJlZGVzID9zIHF1YWlzIGEgYmlibGlvdGVjYSBkYSBQVUNSUyBwb3NzYSBhIHZpciBwYXJ0aWNpcGFyLCBzZW0gP251cyBhbHVzaXZvIGFvcyBkaXJlaXRvcyBhdXRvcmFpcywgYSB0P3R1bG8gZGUgZGl2dWxnYT8/byBkYSBwcm9kdT8/byBjaWVudD9maWNhLgo=Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2020-07-09T23:00:44Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
title |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
spellingShingle |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa Schiavon, Jéssica Zamboni Concreto de Alto Desempenho Zona de Transição Sílica Ativa Nanosílica Propriedades Microestruturais ENGENHARIAS |
title_short |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
title_full |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
title_fullStr |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
title_full_unstemmed |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
title_sort |
Análise da microestrutura de concretos de alto desempenho contendo nanosílica e sílica ativa |
author |
Schiavon, Jéssica Zamboni |
author_facet |
Schiavon, Jéssica Zamboni |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Andrade, Jairo José de Oliveira |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/2835610496598824 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/2179298630407594 |
dc.contributor.author.fl_str_mv |
Schiavon, Jéssica Zamboni |
contributor_str_mv |
Andrade, Jairo José de Oliveira |
dc.subject.por.fl_str_mv |
Concreto de Alto Desempenho Zona de Transição Sílica Ativa Nanosílica Propriedades Microestruturais |
topic |
Concreto de Alto Desempenho Zona de Transição Sílica Ativa Nanosílica Propriedades Microestruturais ENGENHARIAS |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS |
description |
The use of nanomaterials in concrete has shown promise, as the use of several types of these materials in cementitious compounds have been found to guarantee greater physical-mechanical properties and improvement in concrete microstructure. The use of mineral admixtures like nanosilica and silica fume ensures the improvement of interfacial transition zone (ITZ) between aggregate and paste, which is a weaker part in high-performance concrete (HPC). In this way, the present work intends to evaluate the performance of nanosilica and silica fume in properties of HPC in macro and microstructural properties. Were evaluated the mechanical properties (compressive strength and elastic modulus) and microstructural properties through nanoindentation, scanning electron microscopy, X-ray microtomography and atomic force microscopy of concretes with 1.5 and 3% of nanosilica and 5% and 10% of silica fume. The results indicated that with the use of mineral admixtures the compressive strength and elastic modulus of concrete increase significantly. The microstructural investigations showed that the nanosilica and silica fume leads to a densification of ITZ, which was the main responsible for the improvement of HPC performance. |
publishDate |
2019 |
dc.date.accessioned.fl_str_mv |
2019-06-13T13:36:21Z |
dc.date.issued.fl_str_mv |
2019-03-27 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/8694 |
url |
http://tede2.pucrs.br/tede2/handle/tede/8694 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
4953914605093919665 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
4518971056484826825 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola Politécnica |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/8694/5/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf http://tede2.pucrs.br/tede2/bitstream/tede/8694/4/DIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/8694/7/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/8694/3/DIS_JESSICA_ZAMBONI_SCHIAVON_CONFIDENCIAL.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/8694/6/DIS_JESSICA_ZAMBONI_SCHIAVON_COMPLETO.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/8694/1/license.txt |
bitstream.checksum.fl_str_mv |
7f12d33c16c4c5ca7d07bf753955057a cfe97124be6dd755befffbd0bcdf8f36 80fdface6d2f65d864fa69a2510173ea b3f913924c96a27198cd414fdb87304f 3aee826ec220406d02bc2713f359bce0 220e11f2d3ba5354f917c7035aadef24 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765340174942208 |