Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/8602 |
Resumo: | Purpose: This in vitro study evaluated the tensile bond strength of a universal adhesive system to the surface of hybrid CAD/CAM materials treated with: Er:YAG laser, 10% fluoridric acid and Al2O3 sandblasting. Material and methods: One hundred and twenty samples were made with two restorative CAD/CAM materials (Lava Ultimate and Vita Enamic), resulting in 60 samples of each material, divided into 8 groups (n= 15) according to the surface treatments: Lava Ultimate: LU - Control, LAL - Sandblasting with Al2O3, LAC - 10% hydrofluoric acid, LER - Laser Er: YAG; Vita Enamic: EC - Control, EAL - Sandblasting with Al2O3, EAC - 10% hydrofluoric acid, EER - Laser Er: YAG. After the surface treatments the samples received silane (except control), and universal adhesive (Single Bond Universal) were applied and a resin cement RelyX Ultimate (3M ESPE) cone was built. The samples were submitted to tensile bond strength test until rupture between the materials and the failure patterns were analyzed. Results: The highest mean of bond strength in MPa were: EAL (65.94A ± 43.54), EAC (63.78A ± 40.1), LAC (56.40A ± 22.5) followed by LU (44.50AB ± 27.5), LAL (41.6AB ± 23.84) and LER (35.93AB ± 15.65). The lowest values were for EER (23,40B ± 13,8) and EC (20,10B ± 18,30) groups. The means followed by the same letter do not present statistical difference for ANOVA two-way and Tukey (p> 0.05). The failure analysis showed a predominance of adhesive failure for Lava Ultimate and adhesive and cohesive failures for Vita Enamic. Conclusion: There was no more effective treatment for Lava Ultimate in relation to its control. Both conditioning with 10% hydrofluoric acid and aluminum oxide sandblasting proved to be effective for Vita Enamic. |
id |
P_RS_ed25283b4b5b839e3fab6df4ec1c1fa0 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/8602 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Burnett Jr., Luiz Henriquehttp://lattes.cnpq.br/1252685026530007Bettiol, Heloisa Pressi2019-05-28T16:33:45Z2019-03-14http://tede2.pucrs.br/tede2/handle/tede/8602Purpose: This in vitro study evaluated the tensile bond strength of a universal adhesive system to the surface of hybrid CAD/CAM materials treated with: Er:YAG laser, 10% fluoridric acid and Al2O3 sandblasting. Material and methods: One hundred and twenty samples were made with two restorative CAD/CAM materials (Lava Ultimate and Vita Enamic), resulting in 60 samples of each material, divided into 8 groups (n= 15) according to the surface treatments: Lava Ultimate: LU - Control, LAL - Sandblasting with Al2O3, LAC - 10% hydrofluoric acid, LER - Laser Er: YAG; Vita Enamic: EC - Control, EAL - Sandblasting with Al2O3, EAC - 10% hydrofluoric acid, EER - Laser Er: YAG. After the surface treatments the samples received silane (except control), and universal adhesive (Single Bond Universal) were applied and a resin cement RelyX Ultimate (3M ESPE) cone was built. The samples were submitted to tensile bond strength test until rupture between the materials and the failure patterns were analyzed. Results: The highest mean of bond strength in MPa were: EAL (65.94A ± 43.54), EAC (63.78A ± 40.1), LAC (56.40A ± 22.5) followed by LU (44.50AB ± 27.5), LAL (41.6AB ± 23.84) and LER (35.93AB ± 15.65). The lowest values were for EER (23,40B ± 13,8) and EC (20,10B ± 18,30) groups. The means followed by the same letter do not present statistical difference for ANOVA two-way and Tukey (p> 0.05). The failure analysis showed a predominance of adhesive failure for Lava Ultimate and adhesive and cohesive failures for Vita Enamic. Conclusion: There was no more effective treatment for Lava Ultimate in relation to its control. Both conditioning with 10% hydrofluoric acid and aluminum oxide sandblasting proved to be effective for Vita Enamic.Objetivos: O presente estudo in vitro avaliou a resistência de união de um sistema adesivo universal à superfície de cimentação de materiais CAD/CAM híbridos submetidos a diferentes tratamentos: Laser Er:YAG, ácido fluorídrico 10% e jateamento com óxido de alumínio. Materiais e métodos: Cento e vinte amostras foram confeccionadas com dois materiais restauradores para CAD/CAM (Lava Ultimate e Vita Enamic) resultando em 60 amostras de cada material divididos em oito grupos (n=15): Lava Ultimate: LU – Controle, LAL - Jateamento com Al2O3, LAC - Ácido fluorídrico 10%, LER – Laser Er:YAG; Vita Enamic: EC – Controle, EAL - Jateamento com Al2O3, EAC - Ácido fluorídrico 10%, EER – Laser Er:YAG. Após os tratamentos de superfície as amostras receberam silano (exceto controle), o adesivo Single Bond Universal e sobre ele um cone de cimento resinoso RelyX Ultimate foi confeccionado. As amostras foram submetidas a teste de resistência de união à tração até ruptura e os padrões de falha foram analisados. Resultados: As maiores médias de resistência de união em MPa foram: EAL (65,94A ±43,54), EAC (63,78A ±40,1), LAC (56,40A ±22,5) seguidas de LU (44,50AB ±27,5), LAL (41,6AB ±23,84) e LER (35,93AB ±15,65). Os menores valores ficaram para os grupos EER (23,40B ±13,8) e EC (20,10B ±18,30). As médias seguidas de mesma letra não apresentam diferença estatística para ANOVA two-way e Tukey (p>0,05). A análise de falhas mostrou uma predominância de falhas adesivas para Lava Ultimate e falhas adesivas e coesivas para Vita Enamic. Conclusões: Não houve um tratamento mais eficaz para o Lava Ultimate em relação ao seu controle. Tanto condicionamento com ácido fluorídrico 10% quanto jateamento com óxido de alumínio se mostraram eficazes para o Vita Enamic.Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2019-04-30T11:52:24Z No. of bitstreams: 1 HELOISA_PRESSI_BETTIOL_TES.pdf: 1603819 bytes, checksum: b33e4b8f9f7ef1de00f1fdeaaa7b6081 (MD5)Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2019-05-28T15:08:50Z (GMT) No. of bitstreams: 1 HELOISA_PRESSI_BETTIOL_TES.pdf: 1603819 bytes, checksum: b33e4b8f9f7ef1de00f1fdeaaa7b6081 (MD5)Made available in DSpace on 2019-05-28T16:33:45Z (GMT). No. of bitstreams: 1 HELOISA_PRESSI_BETTIOL_TES.pdf: 1603819 bytes, checksum: b33e4b8f9f7ef1de00f1fdeaaa7b6081 (MD5) Previous issue date: 2019-03-14Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/175172/TES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.jpghttp://tede2.pucrs.br:80/tede2/retrieve/181021/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilEscola de Ciências da SaúdeÁcido FluorídricoÓxido de AlumínioLaser Er:YAGResina Nano CerâmicaCerâmica HíbridaCIENCIAS DA SAUDE::ODONTOLOGIAResistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAMinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisTrabalho será publicado como artigo ou livro24 meses28/05/2021-7411869720500764667500500600-20704984698792443493590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSORIGINALTES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdfTES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdfapplication/pdf1603819http://tede2.pucrs.br/tede2/bitstream/tede/8602/5/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdfb33e4b8f9f7ef1de00f1fdeaaa7b6081MD55THUMBNAILTES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.jpgTES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.jpgimage/jpeg4082http://tede2.pucrs.br/tede2/bitstream/tede/8602/4/TES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.jpgb25fe4f60c99d41d9b96dd440a2e8599MD54TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.jpgTES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.jpgimage/jpeg5510http://tede2.pucrs.br/tede2/bitstream/tede/8602/7/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.jpgafd077198482954c9ef2eaa9c6d47cc0MD57TEXTTES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.txtTES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.txttext/plain1490http://tede2.pucrs.br/tede2/bitstream/tede/8602/3/TES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.txt2ab3c9e82ef127bf2627030c0df918daMD53TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.txtTES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.txttext/plain69179http://tede2.pucrs.br/tede2/bitstream/tede/8602/6/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.txte95dd08d27fb93e4c4a40ef150cceae1MD56LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/8602/1/license.txt220e11f2d3ba5354f917c7035aadef24MD51tede/86022021-06-01 12:00:26.969oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2021-06-01T15:00:26Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
title |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
spellingShingle |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM Bettiol, Heloisa Pressi Ácido Fluorídrico Óxido de Alumínio Laser Er:YAG Resina Nano Cerâmica Cerâmica Híbrida CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
title_full |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
title_fullStr |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
title_full_unstemmed |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
title_sort |
Resistência de união de um sistema adesivo universal à superfície de materiais híbridos para CAD/CAM |
author |
Bettiol, Heloisa Pressi |
author_facet |
Bettiol, Heloisa Pressi |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Burnett Jr., Luiz Henrique |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/1252685026530007 |
dc.contributor.author.fl_str_mv |
Bettiol, Heloisa Pressi |
contributor_str_mv |
Burnett Jr., Luiz Henrique |
dc.subject.por.fl_str_mv |
Ácido Fluorídrico Óxido de Alumínio Laser Er:YAG Resina Nano Cerâmica Cerâmica Híbrida |
topic |
Ácido Fluorídrico Óxido de Alumínio Laser Er:YAG Resina Nano Cerâmica Cerâmica Híbrida CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Purpose: This in vitro study evaluated the tensile bond strength of a universal adhesive system to the surface of hybrid CAD/CAM materials treated with: Er:YAG laser, 10% fluoridric acid and Al2O3 sandblasting. Material and methods: One hundred and twenty samples were made with two restorative CAD/CAM materials (Lava Ultimate and Vita Enamic), resulting in 60 samples of each material, divided into 8 groups (n= 15) according to the surface treatments: Lava Ultimate: LU - Control, LAL - Sandblasting with Al2O3, LAC - 10% hydrofluoric acid, LER - Laser Er: YAG; Vita Enamic: EC - Control, EAL - Sandblasting with Al2O3, EAC - 10% hydrofluoric acid, EER - Laser Er: YAG. After the surface treatments the samples received silane (except control), and universal adhesive (Single Bond Universal) were applied and a resin cement RelyX Ultimate (3M ESPE) cone was built. The samples were submitted to tensile bond strength test until rupture between the materials and the failure patterns were analyzed. Results: The highest mean of bond strength in MPa were: EAL (65.94A ± 43.54), EAC (63.78A ± 40.1), LAC (56.40A ± 22.5) followed by LU (44.50AB ± 27.5), LAL (41.6AB ± 23.84) and LER (35.93AB ± 15.65). The lowest values were for EER (23,40B ± 13,8) and EC (20,10B ± 18,30) groups. The means followed by the same letter do not present statistical difference for ANOVA two-way and Tukey (p> 0.05). The failure analysis showed a predominance of adhesive failure for Lava Ultimate and adhesive and cohesive failures for Vita Enamic. Conclusion: There was no more effective treatment for Lava Ultimate in relation to its control. Both conditioning with 10% hydrofluoric acid and aluminum oxide sandblasting proved to be effective for Vita Enamic. |
publishDate |
2019 |
dc.date.accessioned.fl_str_mv |
2019-05-28T16:33:45Z |
dc.date.issued.fl_str_mv |
2019-03-14 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/8602 |
url |
http://tede2.pucrs.br/tede2/handle/tede/8602 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-7411869720500764667 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola de Ciências da Saúde |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/8602/5/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf http://tede2.pucrs.br/tede2/bitstream/tede/8602/4/TES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/8602/7/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/8602/3/TES_HELOISA_PRESSI_BETTIOL_CONFIDENCIAL.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/8602/6/TES_HELOISA_PRESSI_BETTIOL_COMPLETO.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/8602/1/license.txt |
bitstream.checksum.fl_str_mv |
b33e4b8f9f7ef1de00f1fdeaaa7b6081 b25fe4f60c99d41d9b96dd440a2e8599 afd077198482954c9ef2eaa9c6d47cc0 2ab3c9e82ef127bf2627030c0df918da e95dd08d27fb93e4c4a40ef150cceae1 220e11f2d3ba5354f917c7035aadef24 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765339256389632 |