Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses

Detalhes bibliográficos
Autor(a) principal: Figueiredo, António Manuel Aragão Aresta Valinho de
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: eng
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: http://hdl.handle.net/10316/94058
Resumo: Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia
id RCAP_0efa15aeae356221081e53a5ad36380b
oai_identifier_str oai:estudogeral.uc.pt:10316/94058
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Preparation of NFC-based films with incorporated minerals for packaging and printed electronics usesPreparação de filmes à base de NFC com incorporação de minerais para utilização em embalagens e eletrónica impressaCelulose NanofibriladaSepiolitePaligorsquiteCromatografia Gasosa InversaFilmes CompósitosNanofibrillar CelluloseSepiolitePalygorskiteInverse Gas ChromatographyComposite FilmsDissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e TecnologiaAo longo dos anos, alternativas mais ecológicas e sustentáveis têm vindo a ser procuradas com o objetivo de substituir plásticos e outros materiais que poderão ser fonte de poluição. Sendo a celulose um recurso renovável, esta apresenta-se como uma boa opção, especialmente quando exploradas as nanoceluloses, dadas as suas excelentes propriedades. O objetivo da presente dissertação é a identificação de alternativas adequadas ao uso dos plásticos, recorrendo a celuloses nanofibriladas (NFC), obtidas por diferentes tratamentos de pasta branqueada de eucalipto, e minerais (paligorsquite e sepiolite), para produzir filmes com melhores propriedades mecânicas e de barreira à passagem de gases, mantendo, ao mesmo atempo, a elevada transparência à luz associada às NFCs.Este trabalho foi dividido em duas etapas principais: i) estudos por cromatografia gasosa inversa (IGC) para avaliar as propriedades físico-químicas da superfície dos materiais (NFC e minerais), e ii) preparação de filmes à base de NFCs. Usaram-se NFCs obtidas por três tipos distintos de pré-tratamento (mecânico, enzimático ou químico (oxidação mediada pelo radical TEMPO)), e diferentes quantidades de minerais foram incorporadas nos filmes (0%, 10% e 50%). Para preparar os filmes, utilizaram-se técnicas de evaporação de solvente e de filtração a vácuo e, para a última, dois métodos de secagem. Realizaram-se também ensaios de tração, tendo-se ainda medido a espessura e a transmitância à luz dos filmes.A componente dispersiva da energia de superfície (γsd) seguiu uma tendência decrescente, com o aumento da temperatura, na gama de 35-50ºC, tendo-se obtido valores desde 32 a 49 mJ.m-2, sendo a NFC mecânica a que exibiu o maior valor de γsd (48.9 mJ.m-2, a 35ºC). Ao injetar provas polares, verificou-se a prevalência do carácter ácido de Lewis de todas as NFCs. As componentes específicas da entalpia e entropia de adsorção das provas polares não foram consideradas devido aos baixos coeficientes de correlação. A superfície dos minerais foi também avaliada, obtendo-se valores para γsd, a 240ºC, de 115.9 e 83.4 mJ.m-2 para a sepiolite e paligorsquite, respetivamente.Os filmes sem minerais incorporados evidenciaram-se transparentes, sendo possível ver através dos mesmos. Mesmo quando utilizado 10% de mineral, alguns filmes mantiveram-se bastante transparentes, especialmente aqueles obtidos a partir de NFC quimicamente pré tratada (NFCs oxidadas com TEMPO). Efetivamente, foram obtidos resultados promissores para a transmitância no visível (LT) com 10% de mineral para NFCs oxidadas com TEMPO: valores de LT de 19.6 e 30.2% para NFCs TEMPO 110 e 165. Filmes com 50% de mineral resultaram num aumento significativo da opacidade. A filtração a vácuo levou a filmes com maior espessura, o que se traduziu numa menor transparência observada nestes filmes. Relativamente às propriedades mecânicas, os filmes preparados através da filtração originaram os melhores resultados, resistindo a tensões até 83.9 MPa para filmes apenas com NFC, e até 77.4 MPa para a NFC enzimática com 10% de mineral. O presente trabalho proporcionou resultados promissores relativamente à preparação de filmes compósitos híbridos orgânico-inorgânico, podendo os mesmos ser melhorados através de técnicas como a filtração por membranas, ou alterando as condições de pH, para procurar obter filmes com melhores propriedades.Over the years, more ecological and sustainable alternatives are being pursued to replace plastics and other pollutant sources. Cellulose, being a renewable resource, becomes a good replacement option, especially when further exploited into nanocellulose since it attains excellent properties. The purpose of this dissertation is finding suitable alternatives for the use of plastics, using nanofibrillar celluloses (NFC), obtained from different pre-treatments of bleached eucalyptus pulp, and fibrous clays (sepiolite and palygorskite), to produce films with improved mechanical and gas barrier properties, while maintaining the high transparency to light associated with NFCs.This work was divided in two main stages: i) inverse gas chromatography (IGC) studies, to assess the physicochemical properties of the materials’ surfaces (NFC and minerals) and ii) preparation of NFC-based films. Three different NFCs obtained from different pre-treatments were used (mechanical, enzymatic or chemical (TEMPO-mediated oxidation)), and different quantities of minerals were incorporated in the films (0%, 10% and 50%). To prepare these films, solvent casting and vacuum filtration were the used techniques, and for the latter, two drying methods. Elongation at break tests were also performed, as well as the measurement of their thickness and light transmittance. The dispersive component of the surface energy (γsd) followed a decreasing tendency when increasing the temperature, in the range of 35 to 50ºC, obtaining γsd values from 32 to 49 mJ.m-2, with the mechanical pre-treated NFC exhibiting the highest value for γsd (48.9 mJ.m-2 at 35ºC). By injecting polar probes, the prevalent Lewis acidic character of the NFC samples was determined. The specific components of the enthalpy and entropy of adsorption of polar probes were not considered due to a poor correlation coefficient. Minerals’ surfaces were also evaluated, with γsd values of 115.9 and 83.4 mJ.m2, at 240ºC, for sepiolite and palygorskite, respectively.Films without incorporated minerals were transparent and could be see-through. Even with 10% mineral, some films were still very transparent, especially those from chemically pre-treated NFCs (TEMPO-oxidized NFCs). Promising results for light transmittance (LT) were attained with 10% mineral in TEMPO-oxidized NFCs, that achieved a value of 19.6 and 30.2% for NFC TEMPO 110 and 165. Increasing the mineral content to 50% lead to a massive increase in opacity. Filtrated films exhibited higher thicknesses, which led to a lower transparency observed in these films. Regarding mechanical properties, filtrated films yielded the best results, by resisting to a tensile strength up to 83.9 MPa for a pure NFC film, and up to 77.4 MPa was achieved for the enzymatic NFC with 10% mineral.This work produced promising results regarding the preparation of hybrid organic-inorganic composite films. The results of this dissertation could be further improved by using new approaches, such as membrane filtration or altering the pH conditions, to obtain films with better properties.2020-11-27info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://hdl.handle.net/10316/94058http://hdl.handle.net/10316/94058TID:202687414engFigueiredo, António Manuel Aragão Aresta Valinho deinfo:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2021-05-27T08:01:47Zoai:estudogeral.uc.pt:10316/94058Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T21:12:53.376727Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
Preparação de filmes à base de NFC com incorporação de minerais para utilização em embalagens e eletrónica impressa
title Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
spellingShingle Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
Figueiredo, António Manuel Aragão Aresta Valinho de
Celulose Nanofibrilada
Sepiolite
Paligorsquite
Cromatografia Gasosa Inversa
Filmes Compósitos
Nanofibrillar Cellulose
Sepiolite
Palygorskite
Inverse Gas Chromatography
Composite Films
title_short Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
title_full Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
title_fullStr Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
title_full_unstemmed Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
title_sort Preparation of NFC-based films with incorporated minerals for packaging and printed electronics uses
author Figueiredo, António Manuel Aragão Aresta Valinho de
author_facet Figueiredo, António Manuel Aragão Aresta Valinho de
author_role author
dc.contributor.author.fl_str_mv Figueiredo, António Manuel Aragão Aresta Valinho de
dc.subject.por.fl_str_mv Celulose Nanofibrilada
Sepiolite
Paligorsquite
Cromatografia Gasosa Inversa
Filmes Compósitos
Nanofibrillar Cellulose
Sepiolite
Palygorskite
Inverse Gas Chromatography
Composite Films
topic Celulose Nanofibrilada
Sepiolite
Paligorsquite
Cromatografia Gasosa Inversa
Filmes Compósitos
Nanofibrillar Cellulose
Sepiolite
Palygorskite
Inverse Gas Chromatography
Composite Films
description Dissertação de Mestrado Integrado em Engenharia Química apresentada à Faculdade de Ciências e Tecnologia
publishDate 2020
dc.date.none.fl_str_mv 2020-11-27
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/10316/94058
http://hdl.handle.net/10316/94058
TID:202687414
url http://hdl.handle.net/10316/94058
identifier_str_mv TID:202687414
dc.language.iso.fl_str_mv eng
language eng
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799134024973680640

Registros relacionados